Epoxy modified emulsion polymers

• US 4,522,962 A
• Filed: 09/08/1980
• Issued: 06/11/1985
• Est. Priority Date: 09/08/1980
• Status: Expired due to Term

• Current Assignee: Lilly Industries Limited
• Original Assignee: SCM Corporation (Heidelberg Materials AG)
• Inventors: Abbey, Kirk J., Erickson, James R.
• Primary Examiner(s): Lilling, Herbert J.
• Application Number:
  US06/185,253
• Time in Patent Office: 1,737 Days
• Field of Search: 260/29.6 NR, 260/29.6 PM, 260/29.2 EP, 525/529, 525/117, 525/530, 528/103, 523/410, 523/404
• US Class Current: 523/410
• CPC Class Codes: C08F 2/22 Emulsion polymerisation
• CPC Class Codes: C08F 283/10 on to polymers containing more than one epoxy radical per molecule C08F283/004 takes precedence
• CPC Class Codes: C09D 151/08 grafted on to macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds

Abstract

Emulsion polymers produced by polymerizing ethylenically unsaturated monomers in an aqueous medium can be substantially improved by incorporating into the monomer mixture a minor amount of blend of epoxy resin and glycidyl acrylate. The epoxy modified emulsion polymers are particularly useful as ambient or low temperature thermosetting latices for film-forming coatings.

Claims

1. In an emulsion polymerization process the improvement comprising the steps of:

providing a blend comprising on a weight basis, between 0.1% and 40% of an epoxy resin polymer, between 30% and 99.8% ethylenically unsaturated monomers, and between 0.1% and 30% oxirane containing ethylenically unsaturated monomers, and polymerizing said blend in an aqueous medium in the presence of polymerization catalysts to copolymerize said ethylenically unsaturated monomers with said oxirane containing ethylenically unsaturated monomers to form an oxirane polymer and provide an in situ emulsified blend of oxirane polymer and said epoxy resin polymer.

2. The composition in claim 1 wherein the oxirane monomer contains a pendant double bond and is a derivative of glycidol.

3. The composition in claim 1 wherein the oxirane monomer is selected from an acrylic, a methacrylic, or a vinyl derivative of glycidol.

4. The composition in claim 1 wherein the oxirane monomer is selected from glycidyl acrylate, glycidyl methacrylate, or allyl glycidyl ether.

5. The composition in claim 1 wherein the epoxy resin is a linear polymer.

6. The composition in claim 1 wherein the composition contains a multi-functional amino or mercapto cross-linker adapted to cross-link said polymer.

7. A coating composition containing the polymer composition in claim 1 wherein the coating is curable to provide a protective surface coating.

8. A coating composition in claim 1 wherein the composition contains an amine or mercaptan cross-linker for cross-linking the coating upon curing.