Polyvinylbutyral films which contain plasticizer and have a reduced adhesive power on glass
First Claim
1. A method of reducing adhesion to glass of a thermoplastic polyvinylbutyral molding composition, which contains plasticizer and in which the polyvinylbutyral component contains 21-28% by weight of vinyl alcohol units (based on the polyvinylbutyral), by mixing constituents of the molding composition with an anti-adhesive agent combination of(a) potassium hydroxide, potassium formate or potassium acetate in an amount corresponding to an alkali titer of between 10 and 200 (based on the polyvinylbutyral) and(b) 0.005 to 0.5% by weight (based on the polyvinylbutyral) of a compound having a betaine structure.
1 Assignment
0 Petitions
Accused Products
Abstract
The reduction of the adhesion to glass of thermoplastic polyvinylbutyral molding compositions, in particular films, which contain plasticizer and in which the polyvinylbutyral component has an increased content of vinyl alcohol units, by addition of a combination of potassium hydroxide, potassium formate or potassium acetate and a compound having a betaine structure, as the anti-adhesive agent. Use of the films with reduced adhesion to glass as the bonding layer for the production of glass laminates.
29 Citations
14 Claims
-
1. A method of reducing adhesion to glass of a thermoplastic polyvinylbutyral molding composition, which contains plasticizer and in which the polyvinylbutyral component contains 21-28% by weight of vinyl alcohol units (based on the polyvinylbutyral), by mixing constituents of the molding composition with an anti-adhesive agent combination of
(a) potassium hydroxide, potassium formate or potassium acetate in an amount corresponding to an alkali titer of between 10 and 200 (based on the polyvinylbutyral) and (b) 0.005 to 0.5% by weight (based on the polyvinylbutyral) of a compound having a betaine structure.
-
7. A plasticizer-containing thermoplastic polyvinylbutyral molding composition having reduced adhesion to glass, having a polyvinylbutyral component with from 21 to 28 percent by weight of vinyl alcohol units (based on the polyvinylbutyral) and wherein constituents of the molding composition are in admixture with an anti-adhesive agent combination of:
-
(a) a member selected from the group consisting of potassium hydroxide, potassium formate and potassium acetate in an amount corresponding to an alkali titer of between 10 and 200 (based on the polyvinylbutyral) and (b) from 0.005 to 0.5 percent by weight (based on the polyvinylbutyral) of a compound having a betaine structure. - View Dependent Claims (8, 9, 10, 11, 12, 13, 14)
-