Crosslinkable difunctionalized polyarylene polyethers

• US 4,562,243 A
• Filed: 03/06/1984
• Issued: 12/31/1985
• Est. Priority Date: 03/06/1984
• Status: Expired due to Fees

• Current Assignee: Goodrich Corporation (Raytheon Technologies Corporation d/b/a RTX)
• Original Assignee: Goodrich Corporation (Raytheon Technologies Corporation d/b/a RTX)
• Inventors: Percec, Virgil
• Primary Examiner(s): Lee, Lester L.
• Application Number:
  US06/586,678
• Time in Patent Office: 665 Days
• Field of Search: 528/174, 528/219, 528/373, 528/374, 528/375, 528/376, 528/212, 525/534
• US Class Current: 528/174
• CPC Class Codes: C08G 65/48 Polymers modified by chemical after-treatment
• CPC Class Codes: C08G 75/02 Polythioethers

Abstract

Oligomers of polyarylene polyethers (PAPE) having a mol wt Mn in the range from 1000 to about 10,000 are converted to difunctionalized oligomers so as, in the first instance, to provide a reactive double bond (for example, a vinylbenzyl group) at each end of the PAPE; and, in the second instance, to provide a triple bond (benzylethynyl group) at each end of the PAPE. The PAPE most preferably has a repeating unit which is the residuum of two dihydric phenols or thiophenols ("DHP") linked through a C═O, --S--S--, or --SO₂ -group, or a Si or C atom, and or ether O, or thioether S atoms. The preferred repeating unit is formed by reaction of a DHP such as bisphenol A (BPA) with a halogenated DHP such as dichlorophenyl sulfone (DCPS) so as to provide an alternating configuration. The repeating unit may also include a linking residue of a reactive solvent which residue provides chain extension in the backbone. An oligomer which is a homopolymer having a repeating unit in which at least four benzenoid rings are connected through ether O atoms, may also be difunctionalized. In particular, α,ω-di(phenol)aromatic polyether sulfone oligomers ("APS") are esterified so as to have terminal methacrylyl groups; and, etherified so as to have styryl end groups which are thermally crosslinkable. Illustrated are APS oligomers having BPA-DPS repeating units. The BPA moiety may be replaced with other diphenols. The synthesis of PAPE oligomers with terminal double bonds is carried out with a fast and quantitative modified Williamson etherification of the PAPE with an electrophilic haloalkyl reactant ("HAR") such as chloromethylstyrene ("ClMS") in the presence of a major molar amount (more than 50 mol % based on the number of moles of OH or SH groups originally present in the APS) of a phase transfer catalyst ("PTC") such as tetrabutylammonium hydrogen sulfate ("TBAH"). The vinyl groups at each end of the oligomer may then be converted to ethynyl groups by bromination of the DAPS in CH₂ Cl₂ or CHCl₃, followed by dehydrobromination in the presence of potassium-tert-butoxide ("K-t-Bu"). The glass transition temperature (T_g) of the di(styrenated)APS after thermal curing is unexpectedly much higher than that of the APS from which it is derived.

Claims

1. A difunctionalized substantially linear crosslinkable thermoplastic polyarylene polyether oligomer, or polyarylene polythioether oligomer represented by the formula:

space="preserve" listing-type="equation">R.sup.e --R--["PAPE"]--R--R.sup.e

wherein,

R represents O or S in an ether or ester linkage with R^e ;

R^e represents a residuum containing a terminal carbon to carbon double bond at each end of the oligomer; and

,

"PAPE" represents the residuum of the polyarylene polyether, or polyarylene polythioether oligomer.

2. The polyarylene polyether oligomer consisting essentially of a thermally crosslinkable aromatic polyether sulfone oligomer ("APS") having alternating bisphenol A "BPA(s)" and diphenyl sulfone "DPS(s)" residua, said oligomer being terminated with styryl "St" units, optionally with each of said BPA(s), DPS(s), and St units having substituents, represented by the formula:

space="preserve" listing-type="equation">St--CH.sub.2 --O--BPA(s)--O--DPS(s)--O--BPA(s)--.sub.n O--CH.sub.2 --St

and the structure;

##STR20## wherein, (s) represents H or R¹, R², R³ or R⁴ ;

R¹, R², R³ and R⁴ are inert substituents, any of which, if present on any phenyl ring, and R⁵, may each be the same or different, and are selected from the group consisting of halogen, hydrogen, alkyl having from 1 to about 18 carbon atoms, and alkoxy having from 1 to about 18 carbon atoms, said alkyl and alkoxy being each chosen without regard for the spatial configuration of the carbon atoms;

and, n represents an integer in the range from about 2 to about 10.

3. The APS oligomer of claim 2 wherein said R⁵ are each methyl, and the remaining substituents are each hydrogen;

and, said Mn is in the range from about 1000 to about 5000.

4. The APS oligomer of claim 3 having a T_g in the range from about 100°

C. to about 200°

C.