Oxygen permeable membrane

• US 4,599,157 A
• Filed: 02/25/1985
• Issued: 07/08/1986
• Est. Priority Date: 02/24/1984
• Status: Expired due to Fees

• Current Assignee: Kabushiki Kaisha Toshiba (Toshiba Corporation)
• Original Assignee: Kabushiki Kaisha Toshiba (Toshiba Corporation)
• Inventors: Suzuki, Nobukazu, Tsuruta, Shinji
• Primary Examiner(s): NOT, DEFINED
• Application Number:
  US06/705,015
• Time in Patent Office: 498 Days
• Field of Search: 204/192 C, 204/192 SP, 204/192 P, 204/295-296, 204/432, 204/282, 204/283
• US Class Current: 204/192.15
• CPC Class Codes: H01M 12/06 with one metallic and one gaseous electrode
• CPC Class Codes: H01M 4/86 Inert electrodes with catalytic activity, e.g. for fuel cells

Abstract

There is disclosed a composite membrane and an air electrode for use in hydrogen-oxygen fuel cells, metal-air cells and oxygen sensors. The composite membrane includes a porous membrane having micropores with a thin layer affixed thereto. The thin layer having metallic oxide in a carbon matrix, so that oxygen gas is able to permeate therethrough, but water vapor in air is not allowed to permeate therethrough.

Claims

1. A composite membrane, said membrane comprising:

a porous membrane having micropores; and

a thin layer affixed to at least one surface of said porous membrane, said thin layer contains a metallic oxide in a carbon matrix;

wherein said porous membrane and said thin layer cooperatively permit the passage of oxygen gas therethrough while substantially preventing the passage of water vapor therethrough, said metallic oxide being selected from among the group consisting of tin dioxide, zinc oxide, aluminum oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, titanium dioxide, silicon dioxide, cuprous oxide, manganese monoxide, nickel oxide, tricobalt tetroxide, vanadium dioxide, molybdenum dioxide, tungsten dioxide, ruthenium dioxide, niobium dioxide, chromium dioxide, rhenium dioxide, osmium dioxide, rhodium dioxide, iridium dioxide and platinum dioxide.

2. A composite membrane according to claim 1 wherein said thin layer has a thickness in the range of 0.01 to 1.0 um.

3. A composite membrane according to claim 1 wherein the diameter of the micropores of said porous membrane is equal to or less than 1 um.

4. A composite membrane according to claim 1 which is prepared by a process comprising the step of depositing said thin layer on the surface of said porous membrane using a reactive sputtering treatment with a mixtured gas containing argon gas and a hydrocarbon compound.

5. A composite membrane according to claim 4 wherein said hydrocarbon compound is one selected from the group consisting of alkenes of the general formula CnH_2n+2, alkenes of the general formula CnH_2n, alkenes of the general formula CnH_2n-2 and fluorides in which a part or all of the hydrogen of the hydrocarbon compound has been substituted by fluorine.

6. A composite membrane according to claim 5 wherein the proportion of said hydrocarbon compound is less than 20 vol 70.

7. An air electrode for a cell comprising:

a main electrode body having the capability of electrochemical reduction of oxygen gas with a collector function; and

a thin layer integrally laminated on the gas side surface of said main electrode body directly or with a porous membrane therebetween, said thin layer containing metallic oxide in a carbon matrix, wherein said electrode body and said thin layer cooperatively permit the passage of oxygen gas therethrough while substantially preventing the passage of water vapor therethrough, said metallic oxide being selected from the group consisting of tin dioxide, zinc oxide, aluminum oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, titanium dioxide, silicon dioxide, cuprous oxide, manganese monoxide, nickel oxide, tricobalt tetroxide, vanadium dioxide, molybdenum dioxide, tungsten dioxide, ruthenium dioxide, niobium dioxide, chromium dioxide, rhenium dioxide, osmium dioxide, rhodium dioxide, iridium dioxide and platinum dioxide.

8. An air electrode according to claim 7 wherein said thin layer has a thickness in the range of 0.01 to 1.0 um.

9. An air electrode according to claim 7 wherein said porous membrane has micropores with a diameter less than 1.0 um.

10. A method for manufacturing an oxygen gas permeable composite membrane comprising the step of:

forming a thin layer on a porous membrane having micropores by a reactive sputtering treatment in a mixed gas containing argon gas and a hydrocarbon compound, wherein said porous membrane and said thin layer cooperatively permit the passage of oxygen gas therethrough while substantially preventing the passage of water vapor therethrough, and wherein the sputter source is a metallic oxide selected from the group consisting of tin dioxide, zinc oxide, aluminum oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, titanium dioxide, silicon dioxide, cuprous oxide, maganese monoxide, nickel oxide, tricobalt tetroxide, vanadium dioxide, molybdenum dioxide, tungsten dioxide, ruthenium dioxide, niobium dioxide, chromium dioxide, rhenium dioxide, osmium dioxide, rhodium dioxide, iridium dioxide and platinum dioxide.