Polyester polyurethane foams having antistatic properties

• US 4,621,106 A
• Filed: 02/05/1985
• Issued: 11/04/1986
• Est. Priority Date: 02/05/1985
• Status: Expired due to Fees

• Current Assignee: Wm. T. Burnett & Co., Inc.
• Original Assignee: Wm. T. Burnett & Co., Inc.
• Inventors: Sollers, Joseph S., Fracalossi, Roland N., Greenhouse, Walter V. V.
• Primary Examiner(s): Cockeram, Herbert S.
• Application Number:
  US06/698,535
• Time in Patent Office: 637 Days
• Field of Search: 521/130, 521/123
• US Class Current: 521/130
• CPC Class Codes: C08G 18/2885 containing halogen atoms
• CPC Class Codes: C08K 3/02 Elements
• CPC Class Codes: C08K 5/095 Carboxylic acids containing halogens
• CPC Class Codes: C08L 75/06 from polyesters

Abstract

An antistatic polyester polyurethane foam containing substantially uniformly incorporated therein as an antistatic material a combination of a particulate, electrically conductive material, such as carbon black, and a haloacetic acid, such as dichloroacetic acid. The combination of conductive material and haloacetic acid which is incorporated into the polyurethane foam during its in situ preparation is believed to be tied into the foam through reaction of the haloacetic acid and at least the diisocyanate used in the foam formulation. The polyurethane foams of this invention have excellent antistatic properties while retaining the desirable features of a good polyurethane foam including uniformity of cell size, no pinholing, and good structural stability.

Claims

1. A flexible polyurethane foam comprising the foamforming reaction product of water as a foaming agent, an isocyanate reactive polyester polyol and a polyisocyanate, and including uniformly contained in said foam an antistatic agent essentially consisting of the combination of a particulate electrically conductive material and a haloacetic acid, said water being present in an amount sufficient to provide a flexible foam, and said antistatic agent being present in an amount sufficient to provide antistatic characteristics to said foam.

2. The flexible polyurethane foam of claim 1 wherein said haloacetic acid is dichloroacetic acid.

3. The flexible polyurethane foam of claim 2 wherein said conductive material is carbon black.

4. The flexible polyurethane foam of claim 2 wherein said electrically conductive material is present in an amount of from about 0.3 to 40% by weight based on the total weight of said polyol and said dichloroacetic acid is present in an amount of from 0.5 to 5% by weight based on the total weight of said polyol.

5. The flexible polyurethane foam of claim 2 wherein said electrically conductive material is present in an amount of from about 0.5 to 20% by weight based on the total weight of said polyol and said dichloroacetic acid is present in an amount of from 0.8 to 2.0% by weight based on the total weight of said polyol.

6. The flexible polyurethane foam of claim 2 wherein said electrically conductive material is present in an amount of from about 0.5 to 20% by weight based on the total weight of said polyol and said dichloroacetic acid is present in an amount of from 1.0 to 1.5% by weight based on the total weight of said polyol.

7. The flexible polyurethane foam of claim 4 wherein said foam has an effective surface resistance of less than 1×

10¹² ohms/square.

8. The flexible polyurethane foam of claim 7 wherein said foam has an effective surface resistance of less than 1×

10¹¹ ohms/square.

9. The method of forming an antistatic flexible polyurethane foam comprising admixing a foam-forming composition including water as a foaming agent, a reactive polyester polyol, a polyisocyanate, and an antistatic agent essentially consisting of a combination of a particulate electrically conductive material and haloacetic acid;

subjecting said foaming composition to foaming conditions to form a flexible polyurethane foam having said combination of antistatic agents uniformly contained in said foam, said water being present in an amount sufficient to form a flexible foam and said antistatic agent being present in an amount sufficient to provide antistatic characteristics to said foam.

10. The method of claim 9 wherein said haloacetic acid is dichloroacetic acid.

11. The method of claim 10 wherein said conductive material is carbon black added as an aqueous dispersion.

12. The method of claim 10 wherein said conductive material is present in an amount of from about 0.3 to 40% by weight based on the total weight of said foam, and said dichloroacetic acid is present in an amount of from 0.5 to 5% by weight based on the total weight of the foam.

13. The method of claim 10 wherein said electrically conductive material is present in an amount of from about 0.5 to 20% by weight based on the total weight of said polyol and said dichloroacetic acid is present in an amount of from 0.8 to 2.0% by weight based on the total weight of said polyol.

14. The method of claim 9 wherein said electrically conductive material is present in an amount of from about 0.5 to 20% by weight based on the total weight of said polyol and said dichloroacetic acid is present in an amount of from 1.0 to 1.5% by weight based on the total weight of said polyol.

15. The method of claim 12 wherein said foam has an effective surface resistance of less than 1×

10¹² ohms/square.

16. The method of claim 15 wherein said foam has an effective surface resistance of less than 1×

10¹¹ ohms/square.