Asymmetric membranes

• US 4,629,563 A
• Filed: 08/11/1981
• Issued: 12/16/1986
• Est. Priority Date: 03/14/1980
• Status: Expired due to Term

• Current Assignee: USF Filtration and Separations Group, Inc. (Siemens AG)
• Original Assignee: Brunswick Corporation
• Inventors: Wrasidlo, Wolfgang J.
• Primary Examiner(s): Spear, Frank
• Application Number:
  US06/291,927
• Time in Patent Office: 1,953 Days
• Field of Search: 210/490, 210/500.2, 210/504
• US Class Current: 210/500.34
• CPC Class Codes: B01D 2323/08 Specific temperatures applied
• CPC Class Codes: B01D 2323/081 Heating
• CPC Class Codes: B01D 2323/12 Specific ratios of components used
• CPC Class Codes: B01D 2325/022 Asymmetric membranes
• CPC Class Codes: B01D 2325/20 Specific permeability or cut-off range
• CPC Class Codes: B01D 61/145 Ultrafiltration
• CPC Class Codes: B01D 61/147 Microfiltration
• CPC Class Codes: B01D 63/00 Apparatus in general for separation processes using semi-permeable membranes
• CPC Class Codes: B01D 65/102 Detection of leaks in membranes
• CPC Class Codes: B01D 67/0011 Casting solutions therefor
• CPC Class Codes: B01D 67/00111 Polymer pretreatment in the casting solutions
• CPC Class Codes: B01D 69/02 characterised by their properties

Abstract

Improved ultraporous and microporous membranes are provided with an entirely reticulated structure free of large finger voids. The reticulated support structure has gradually increasing pore size which reaches a maximum of from about 10 to about 20,000 times the diameter of the skin pores at the opposite face. The skin is very thin and has controllable highly uniform skin pores of from about 0.003 to about 3.0 microns in diameter. The structure offers highly desirable properties to such membranes.

Claims

1. An asymmetric integral polymer membrane having a bulk porosity greater than seventy percent, a skin face an an opposite face comprising:

A. A porous skin having skin pores with an average diameter of from about 0.003 to about 3.0 microns; and

B. A porous support comprising a substantially continuous reticular mass of a thress-dimensional network defining interconnecting flow channels communicating with said skin pores and with said opposite face, said flow channels defining support pores having diameters generally increasing gradually in size from said skin to said opposite face, to an average diameter of from about 10 to about 20,000 times the diameter of said skin pores, and said support being substantially free of voids materially larger in diameter than said gradually increasing support pores.

2. The membrane of claim 1, wherein said polymer is a polyarylsulfone.

3. The membrane of claim 1, wherein said polymer is polystyrene.

4. The membrane of claim 1, wherein said polymer is a polyamide.

5. The membrane of claim 1, wherein said polymer is a polyvinylidene halide.

6. The membrane of claim 1, wherein the ratio of the maximum pore size to the average pore size within said skin is less than about 5.

7. The membrane of claim 1, wherein the water permeability, p, is related to its retentive pore size, r, by the equation

8. The membrane of claim 1, wherein said membrane is an ultrafilter and K is larger than about 12×

10⁵ /min psi.

9. The membrane of claim 1, wherein said membrane has a substantially larger dirt-holding ability in one flow direction than in the other.

10. The membrane of claim 1, wherein said membrane is microporous.

11. The membrane of claim 1, wherein said membrane is an ultrafiltration membrane.

12. The membrane of claim 1, wherein said membrane has a skin which contains pores having an average pore diameter of from about 0.05 to about 3.0 microns and wherein said membrane may be used with its support side upstream, and when so used, the volume of fluid which may be passed through said membrane by the time the rate of flow through said membrane is reduced to 50% of the initial value is at least about 2 times as large as the volume of fluid which may be passed through the same membrane used with its skin side upstream.

13. The membrane of claim 1, wherein said membrane has a skin which contains pores having an average pore diameter of from about 0.05 to about 3.0 microns and wherein said membrane may be used with its support side upstream, and when so used, the volume of fluid which may be passed through said membrane by the time the rate of flow through said membrane is reduced to 50% of the initial value is at least about 5 times as large as the volume of fluid which may be passed through the same membrane used with its skin side upstream.

14. An asymmetric integral microporous polymer membrane having a bulk porosity greater than seventy percent a skin face and an opposite face comprising:

A. A porous skin having skin pores with an average diameter of from about 0.01 to about 3.0 microns; and

B. A porous support comprising a substantially continuous reticular mass of a three-dimensional network defining interconnecting flow channels communicating with said skin pores and with said opposite face, said flow channels defining support pores having diameters generally increasing gradually in size from said skin to said opposite face, to an average diameter at said opposite face of at least about 10 times the diameter of said skin pores, and said support being substantially free of voids materially larger in diameter than said gradually increasing support pores.

15. An asymmetric integral microporous polymer membrane having a bulk porosity greater than seventy percent, a skin face and an opposite face comprising:

A. A porous skin having skin pores with an average diameter of from about 0.01 to about 3.0 microns; and

B. A porous support comprising a substantially continuous reticular mass of a three-dimensional network defining interconnecting flow channels communicating with said skin pores and with said opposite face, said flow channels defining support pores having diameters generally increasing gradually in size from said skin to said opposite face, to an average diameter of from about 10 to about 300 times the diameter of said skin pores, and said support being substantially free of voids materially larger in diameter than said gradually increasing support pores.

16. An asymmetric integral microporous polymer membrane having a bulk porosity greater than seventy percent a skin face and an opposite face comprising:

A. A porous skin having skin pores with an average diameter of from about 0.01 to about 3.0 microns;

B. A porous support comprising a substantially continuous reticular mass of a three-dimensional network defining interconnecting flow channels communicating with said skin pores and with said opposite face, said flow channels defining support pores having diameters generally increasing gradually in size from said skin to said opposite face, to an average diameter of from about 10 to about 300 times the diameter of said skin pores, and said support being substantially free of voids materially larger in diameter than said gradually increasing support pores; and

C. Said membrane composed of at least one polymer member selected from the group consisting of polysulfone, polyarylsulfone, polyamide, polyvinylidene halide, polycarbonate, polyacrylonitrile, and polystyrene.

17. An asymmetric integral microfiltration polymer membrane having a bulk porosity greater than seventy percent, a skin face and an opposite face comprising:

A. A porous skin having skin pores with an average diameter of from about 0.01 to about 3.0 microns;

B. A porous support comprising a substantially continuous reticular mass of a three-dimensional network defining interconnecting flow channels communicating with said skin pores and with said opposite face, said flow channels defining support pores having diameters generally increasing gradually in size from said skin to said opposite face, to an average diameter of from about 10 to about 300 times the diameter of said skin pores, and said support being substantially free of voids materially larger in diameter than said gradually increasing support pores; and

C. Said membrane being composed of at least one polymer member selected from the group consisting of polysulfone, polyarylsulfone, polyamide, polyvinylidene halide, polycarbonate, polyacrylonitrile, and polystyrene.

18. The membrane of claim 17, wherein said skin comprises less than about 5% of the thickness of said membrane.

19. The membrane of claim 17, wherein the ratio of the maximum pore size to the average pore size within said skin of said membrane is less than about 5.

20. The membrane of claim 17, wherein the pore size distribution within said skin is less than about 3 and wherein said skin comprises from about 1 to about 5% of the thickness of said membrane.

21. The membrane of claim 17, wherein the water permeability, p, is related to its retentive pore size, r, by the equation

22. The membrane of claim 21, wherein said membrane is an ultrafilter and K is larger than about 12×

10⁵ /min psi, and wherein said membrane has a substantially larger dirt-holding ability in one flow direction than in the other.

23. An asymmetric integral microfiltration polymer membrane having a bulk porosity greater than seventy percent, a skin face and an opposite face comprising:

A. A porous skin having skin pores with an average diameter of from about 0.01 to about 3.0 microns;

B. A porous support comprising a substantially continuous reticular mass of a three-dimensional network defining interconnecting flow channels communicating with said skin pores and with said opposite face, said flow channels defining support pores having diameters generally increasing gradually in size from said skin to said opposite face, to an average diameter of from about 10 to about 300 times the diameter of said skin pores, and said support being substantially free of voids materially larger in diameter than said gradually increasing support pores; and

C. Said membrane being composed of polysulfone.