Method of preparing composite aluminum material

• US 4,643,241 A
• Filed: 07/23/1985
• Issued: 02/17/1987
• Est. Priority Date: 07/26/1984
• Status: Expired due to Fees

• Current Assignee: Kabushiki Kaisha Toyota Chuo Kenkyusho (Toyota Motor Corporation)
• Original Assignee: Kabushiki Kaisha Toyota Chuo Kenkyusho (Toyota Motor Corporation)
• Inventors: Takahashi, Yoshiyasu, Yonekura, Koji, Suzuki, Kenichi, Iwahori, Hiroaki
• Primary Examiner(s): NOT, DEFINED
• Assistant Examiner(s): Reid, G. M.
• Application Number:
  US06/757,876
• Time in Patent Office: 574 Days
• Field of Search: 164/55.1, 164/54, 164/67.1, 164/75, 164/101, 164/102, 164/103, 164/53, 164/91, 164/66.1, 75/259, 228/223
• US Class Current: 164/101
• CPC Class Codes: B22D 19/00 Casting in, on, or around objects which form part of the product B22D23/04 takes precedence; alumino-thermic welding B23K23/00; coating by casting molten material on the substrate C23C6/00

Abstract

A method of preparing a composite aluminum material to be formed integrally by bonding aluminum or aluminum alloy to an aluminum or aluminum alloy member which is formed in advance in a specified shape by the method of internal chill, etc. The method comprises the steps of forming a chemical conversion coating of pentafluoroaluminate (K₂ AlF₅) by bringing a solution containing potassium ions and fluorine ions in contact with the surface of the aluminum member.

Claims

1. A method of preparing a composite aluminum material comprising the steps of:

contacting an aluminum member at least partially with a treating solution containing 0.5-40 g/1 of potassium ions and 1-10 moles of fluorine ions per mole of potassium ions, said treating solution used to form a chemical conversion coating layer of potassium pentafluoroaluminate on a specified surface of said member; and

contacting said surface with a molten aluminum or aluminum alloy.

2. A method according to claim 1, wherein said treating solution is an aqueous solution containing 1-80 g/1 of KHF₂.

3. A method according to claim 1, wherein said treating solution is an aqueous solution of potassium fluoride (KF) and hydrogen fluoride (HF).

4. A method according to claim 1, wherein said aluminum member is contacted with said treating solution by a method selected from the group consisting of immersing, coating and spraying.

5. A method according to claim 1, wherein said potassium pentafluoroaluminate is formed in an amount of 0.1 to 10 g/m².

6. A method according to claim 1, wherein said surface is contacted with said molten aluminum or aluminum alloy by casting.

7. A method according to claim 1, wherein said surface is contacted with said molten aluminum or aluminum alloy by at least partially immersing the member in the molten aluminum or aluminum alloy.

8. A method according to claim 1, wherein said member is contacted with said molten aluminum or aluminum alloy in a non-oxidative atmosphere.