Method for the production of an aluminum foil for electrolytic _capacitors, and electrolytic capacitors thus produced

• US 4,676,879 A
• Filed: 02/20/1986
• Issued: 06/30/1987
• Est. Priority Date: 04/12/1985
• Status: Expired due to Fees

• Current Assignee: Becromal SpA (TDK Corporation)
• Original Assignee: Becromal SpA (TDK Corporation)
• Inventors: Salvadori, Luigi
• Primary Examiner(s): TUFARIELLO, THOMAS
• Application Number:
  US06/831,442
• Time in Patent Office: 495 Days
• Field of Search: 204/129.75, 204/129.8, 204/129.43
• US Class Current: 361/509
• CPC Class Codes: C25F 3/04 of light metals
• CPC Class Codes: H01G 9/055 Etched foil electrodes

Abstract

Method for producing an aluminum foil for use in electrolytic capacitors, wherein an aluminum foil is subjected to treatment in a satination bath prior to conventional anodic etching. The satination bath gives the foil a more uniform surface condition, so that the subsequent etching occurs in a more uniform manner.

Claims

1. In a method for the production of an aluminum foil suitable for use in an electrolytic capacitor, which comprises subjecting an aluminum foil to anodic etching in an etching bath containing an electrolyte and a counter-electrode by means of direct current superimposed by current pulses, the improvement which comprises immersing said aluminum foil in a satination bath to improve the uniformity of surface properties of said foil before said anodic etching, wherein said satination bath contains a hydrogen halide acid or a salt thereof and has a Cb value of from 2 to about 5 Cb/cm².

2. A method according to claim 1, wherein a satination current of wave shaping having a frequency of from about 20 to 400 Hz and a duty cycle of more than 40% is applied to said satination bath.

3. A method according to claim 2, wherein said duty cycle is about 50%.

4. A method according to claim 1, wherein said satination bath is maintained at a temperature of about 90°

C.

5. A method according to claim 1, wherein said satination bath contans hydrogen chloride or a salt thereof.

6. A method according to claim 1, wherein voltage pulses are applied to said etching bath to momentarily and periodically interrupt said anodic etching.

7. An electrolytic capacitor which has an aluminum foil produced by the method of claim 1.

8. In a method for the production of an aluminum foil suitable for use in an electrolytic capacitor, which comprises subjecting an aluminum foil to anodic etching in an etching bath containing an electrolyte and a counter-electrode by means of pulsating direct current, the improvement which comprises immersing said aluminum foil in a satination bath to improve the uniformity of surface properties of said foil before said anodic etching, wherein said satination bath contains a hydrogen halide acid or a salt thereof and has a Cb value of from 2 to about 5 Cb/cm².

9. A method according to claim 8, wherein a satination current of wave shape having a frequency of from about 20 to 400 Hz and a duty cycle of more than 40% is applied to said satination bath.

10. A method according to claim 9, wherein said duty cycle is about 50%.

11. A method according to claim 8, wherein said satination bath is maintained at a temperature of about 90°

C.

12. A method according to claim 8, wherein said satination bath contans hydrogen chloride or a salt thereof.

13. A method according to claim 8, wherein voltage pulses are applied to said etching bath to momentarily and periodically interrupt said anodic etching.

14. An electrolytic capacitor which has an aluminum foil produced by the method of claim 8.