Process for selective transfer of metallic foils to xerographic images

• US 4,724,026 A
• Filed: 10/14/1986
• Issued: 02/09/1988
• Est. Priority Date: 02/05/1985
• Status: Expired due to Term

• Current Assignee: PaperDirect, Inc. (Empire Financial Corp)
• Original Assignee: Omnicomm Systems Incorporated (Anju Software, Inc.)
• Inventors: Nelson, Marshall A.
• Primary Examiner(s): Czaja, Donald E.
• Assistant Examiner(s): FALASCO, LOUIS V
• Application Number:
  US06/918,365
• Time in Patent Office: 483 Days
• Field of Search: 156/150, 156/151, 156/233, 156/230, 156/234, 156/235, 156/239, 156/241, 156/249, 156/273.7, 156/276, 156/283, 156/289, 156/344, 430/2, 430/12, 430/16, 430/45, 430/49, 427/56.1, 428/200, 428/202, 428/344, 428/913, 428/914, 428/915, 29/DIG. 1, 29/DIG. 2
• US Class Current: 156/233
• CPC Class Codes: B32B 37/1284 Application of adhesive
• CPC Class Codes: B32B 38/10 Removing layers, or parts of layers, mechanically or chemically
• CPC Class Codes: B41M 7/00 After-treatment of prints, e.g. heating, irradiating, setting of the ink, protection of the printed stock pre-treatment or treatment during printing B41M5/0011; printers for treating or overcoating copy materials before, during or after printing B41J11/0015
• CPC Class Codes: B41M 7/0027 using protective coatings or layers by lamination or by fusion of the coatings or layers
• CPC Class Codes: G03G 15/225 using contact-printing
• CPC Class Codes: G03G 8/00 Layers covering the final reproduction, e.g. for protecting, for writing thereon
• CPC Class Codes: H05K 3/046 by selective transfer or selective detachment of a conductive layer

Abstract

The present invention is directed to a method for selectively transferring metallic foil and xerographic images on a receiving substrate such as paper. The method generally comprises providing a transfer sheet (including a metallic film) and a receiving substrate (including xerographic images disposed thereon.) The receiving substrate is placed in face-to-face contact with the transfer sheet to form a sandwich with the xerographic images on the inside. the sandwich is then fed through an apparatus, where heat and pressure are applied, causing the xerographic images to tackify and causing the metal film from the transfer sheet to selectively adhere to the xerographic images.

Claims

1. A selective transfer process comprising the steps of:

providing a sheet comprising toner xerographic images and a metal transfer sheet comprising, in successive layers, a carrier, a metallic film and an adhesive;

placing the sheet comprising toner xerographic images in face-to-face contact with the foil transfer sheet to form a sandwich with the toner xerographic images on the inside;

applying heat and pressure to the sandwich to cause the toner xerograhic image to become tacky and the metallic film to selectively adhere to the images, resulting in a decorated sheet; and

stripping the foil transfer sheet away from the decorated sheet.

2. The process of claim 1 comprising the additional step of preheating the sheet comprising toner xerographic images before the step of applying heat and pressure to the sandwich.

3. The process of claim 1 wherein the heat is applied at a temperature in a range of from about 200 to about 375 degrees Fahrenheit.

4. The process of claim 3 wherein the heat is applied at a temperature of about 350 degrees Fahrenheit.

5. The process of claim 1 wherein the pressure is applied in a range of from about 1 to about 20 pounds per square inch.

6. The process of claim 5 wherein the pressure is applied at about 11 pounds per square inch.

7. The process of claim 1 wherein the metal transfer sheet is made by vacuum depositing metal on a polymer backing.

8. The process of claim 7 wherein the metal is one of the group consisting of aluminum, copper, tin, silver and gold.

9. The process of claim 1 wherein the metal transfer sheet is attached to a backing sheet, and the sheet comprising toner xerographic images is placed between the backing sheet and transfer sheet.

10. The process of claim 1 further comprising the steps of:

providing a pair of rollers adapted to apply heat and pressure to the sandwich; and

passing the sandwich through the paid of rollers.

11. The process of claim 10 further comprising the step of providing a dwell time of about 0.01 to 0.4 seconds.

12. The process of claim 10 wherein the sandwich is passed through the rollers at a rate of about 100 inches per minute.

13. The process of claim 10 wherein the pair of rollers comprises a rigid roller element and a roller element comprising a flexible surface.

14. The process of claim 13 wherein the flexible rubber element is constructed with a silicone rubber surface.

15. The process of claim 13 wherein the flexible roller element has a surface hardness in a range of from about 40 durometers to about 80 durometers.

16. The process of claim 10 wherein:

the pair of rollers comprises a flexible roller element having a surface hardness in a range of from about 40 to about 80 durometers;

the sandwich is permitted to contact the rollers at a rate in a range from about 25 to 500 inches per minute; and

heat is applied to the sandwich at a temperature in a range from about 200 to 375 degrees Fahrenheit simultaneously with the formation of contact between the sandwich and the rollers.

17. A selective transfer process comprising the steps of:

providing a metal transfer sheet comprising, in layers, a carrier film, a release coat, a polymer film, a metallic film and an adhesive;

providing a receiving substrate comprising a toner xerographic image;

placing the receiving substrate in face-to-face contact with the foil transfer sheet;

while the receiving substrate and the foil transfer sheet are in face-to-face contact, applying heat and pressure to at least one of the receiving substrate and metal transfer sheet to cause the toner xerographic image to become tacky and cause the metal film to adhere to the toner xerographic image, and to thereby cause the formation of a decorated receiving substrate; and

stripping away the metal transfer sheet from the decorated receiving substrate.

18. The process of claim 17 wherein the metal transfer sheet is attached to a backing sheet, and the substrate comprising a toner xerographic image is placed between the backing sheet and the metal transfer sheet.

19. The process of claim 17 wherein said adhesive contains a resin and a dispersion of 0.5 micron or larger particulate material in a ratio of at least 1 part particulate material to one part resin.

20. The process of claim 19 wherein the particulate comprises titanium oxide at a ratio of about 4 parts titanium oxide to three parts resin.