Method for forming a hard carbon thin film on article and applications thereof

• US 4,725,345 A
• Filed: 04/17/1986
• Issued: 02/16/1988
• Est. Priority Date: 04/22/1985
• Status: Expired due to Fees

• Current Assignee: TRIO Kabushiki Kaisha
• Original Assignee: Kabushiki Kaisha Kenwood
• Inventors: Sato, Tsugio, Ohta, Shuhei, Yaguchi, Yoichi, Toshima, Hiroaki, Yamazaki, Kaoru, Iwakura, Shiro, Sakamoto, Masakatsu
• Primary Examiner(s): NOT, DEFINED
• Application Number:
  US06/853,182
• Time in Patent Office: 670 Days
• Field of Search: 204/192.31, 204/192.11, 204/192.15, 428/408, 427/38, 427/39, 427/41
• US Class Current: 427/528
• CPC Class Codes: C23C 14/0605 Carbon
• CPC Class Codes: C23C 14/32 by explosion; by evaporation and subsequent ionisation of the vapours , e.g. ion-platingC23C14/34 - C23C14/48 take precedence
• CPC Class Codes: H04R 31/003 for diaphragms or their outer suspension
• CPC Class Codes: Y10T 428/30 Self-sustaining carbon mass or layer with impregnant or other layer
• CPC Class Codes: Y10T 428/31678 Of metal

Abstract

A method of forming diamond-like carbon layer which is advantageously adaptable as a coating layer on acoustic diaphragms. In the method, carbon vaporized out of solid carbon source is deposited onto the surface of the diaphragm as the coating layer in the atmosphere of catalystic gas, for instance, H₂ +Ar or H₂ of about 10^-4 Torr. The deposited carbon layer on the surface of the diaphragm is an amorphous carbon of inclusion of hybridized orbital SP² bond and hybridized orbital SP³ bond and crystalline carbon particles of hybridized orbital SP³ bond dispersed in the amorphous carbon, or an amorphous carbon of inclusion of hybridized orbital SP² bond and hybridized orbital SP³ bond.

Claims

1. A method of forming a carbon layer on the surface of an article comprising the steps of:

respective disposing the article and a solid carbon source at opposite portions in a vacuum chamber which contains catalystic gas of a predetermined pressure wherein said catalystic gas is a hydrogen gas or mixture gas of hydrogen and argon;

vaporizing the solid carbon and applying an electric field to the vaporized carbon to ionize the vaporized carbon; and

applying an electrical potential to the article so that the ionized vapor carbon is deposited onto the surface of the article as the carbon layer.

2. A method according to claim 1, wherein said deposited carbon layer is amorphous carbon of inclusion of hybridized orbital SP² bond and hybridized orbital SP³ bond and crystalline carbon particles of hybridized orbital SP³ bond dispersed in said amorphous carbon.

3. A method according to claim 1, wherein said deposited carbon layer is amorphous carbon of inclusion of hybridized orbital SP² bond and hybridized orbital SP³ bond.

4. A method according to claim 1, wherein said solid carbon source is graphite.

5. A method according to claim 1, wherein said predetermined pressure is in the order of 10^-4 Torr.

6. A method according to claim 1, wherein the deposition rate of the carbon layer is in the range of 0.02 μ

m/min to 0.1 μ

m/min.

7. A method of forming a carbon layer and an intermediate layer on the surface of an article comprising the steps of:

respectively disposing the article, a solid carbon source and an intermediate layer material solid source in a vacuum chamber which contains intermediate layer material gas of a predetermined pressure;

vaporizing the intermediate layer material solid source and applying an electrical field to the vaporized intermediate layer material solid source to ionize it as plasma which decomposes the intermediate layer material gas, whereby an intermediate layer material compound is produced in the plasma;

applying an electrical potential to the article so that the intermediate layer material compound is deposited onto the surface of the article as the intermediate layer;

exhausting the hydrocarbon gas and introducing catalystic gas in the chamber wherein said catalystic gas is hydrogen gas or mixture gas of hydrogen and argon, and vaporizing the solid carbon and applying an electric field to the vaporized carbon to ionize the vaporized carbon; and

applying an electrical potential to the article so that the ionized vapor carbon is deposited onto the intermediate thin layer on the article as the hard carbon layer.

8. A method according to claim 7, wherein said intermediate layer material gas is hydrocarbon.

9. A method according to claim 8, wherein said hydrocarbon is CH₄.

10. A method according to claim 8, wherein said intermediate layer material compound is carbide.

11. A method according to claim 7, wherein the surface of said article is titanium.

12. A method according to claim 7, wherein said intermediate layer material solid source is titanium.

13. A method according to claim 7, wherein said solid carbon source is graphite.

14. A method according to claim 7, wherein said predetermined pressure is in the order of 10^-4 Torr.

15. A method according to claim 7, wherein the deposition rate of the carbon layer is in the range of 0.02 μ

m/min to 0.1 μ

m/min.