Transparent coating of flexible, elastic polyurethane for transparent glass or synthetic resin substrates

• US 4,745,152 A
• Filed: 02/20/1987
• Issued: 05/17/1988
• Est. Priority Date: 02/22/1986
• Status: Expired due to Fees

• Current Assignee: Saint-Gobain Vitrage
• Original Assignee: Saint-Gobain Vitrage
• Inventors: Hahn, Gunter, Fock, Juergen, Holzer, Gerhard, Radisch, Helmer
• Primary Examiner(s): WELSH JR, MAURICE
• Application Number:
  US07/016,946
• Time in Patent Office: 452 Days
• Field of Search: 524/718, 524/850, 528/71, 528/77
• US Class Current: 524/718
• CPC Class Codes: B32B 17/1077 containing polyurethane
• CPC Class Codes: C08G 18/0828 containing sulfonate groups or groups forming them
• CPC Class Codes: C08G 18/5072 containing sulfur
• CPC Class Codes: C08G 18/7831 containing biuret groups
• CPC Class Codes: C08G 18/792 formed by oligomerisation of aliphatic and/or cycloaliphatic isocyanates or isothiocyanates

Abstract

A transparent coating for windows or other transparent substrates made of glass or synthetic resin, consisting of a flexible elastic polyurethane, serves as a shatterproofing coating for substrates made of silicate glass or as a coating improving the scratch resistance of substrates made of synthetic resin. To reduce or prevent the formation of a deposit of moisture on the surface of the coating, the polyol component of the reaction mixture for preparing a coating pursuant to the invention consists of a difunctional sulfonated polyether polyol containing approximately 1 to 10% of OH groups by weight and a trifunctional polyol containing approximately 8 to 12% of OH groups by weight and having an average molecular weight of approximately 400 to approximately 1000 g/mole.

Claims

1. Transparent coating for windows or other substrates made of glass or synthetic resin, comprising a flexible elastic polyurethane that is prepared from a reaction mixture consisting essentially of an isocyanate component which consists essentially of trifunctional aliphatic polyisocyanates of biuret or isocyanurate structure based on 1,6-hexamethylenediisocyanate, containing 15 to 25% by weight of NCO groups and with an average molecular weight of approximately 450 to approximately 1000 g per mole, and a polyol component which contains at least one polyfunctional polyol, and which may contain a reaction catalyst and other auxiliary substances, wherein said polyol component of the reaction mixture comprises a difunctional sulfonated polyether polyol containing 1 to 10% by weight of OH groups and a trifunctional polyol containing approximately 8 to 12% by weight of OH groups and having an average molecular weight of approximately 400 to approximately 1000 g per mole.

2. Transparent coating pursuant to claim 1, wherein said polyether polyol comprises a polyoxyalkylene ether of the formula

3. Transparent coating pursuant to claim 1, wherein said sulfonated polyoxyalkylene ether has an average molecular weight of approximately 500 to approximately 5000 g per mole.

4. Transparent coating of claim 3, wherein said molecular weight is approximately 2000 g per mole.

5. Transparent coating pursuant to claim 1, wherein the sulfonated polyoxyalkylene ether used is comprised of ethoxy and propoxy groups with at least 50% by weight of ethoxy groups in the chain.

6. Transparent coating pursuant to claim 5, wherein the sulfonated polyoxyalkylene ether has an ethoxy/propoxy ratio of approximately 80:

20.

7. Transparent coating pursuant to claim 1, wherein the proportion of the sulfonated polyoxyalkylene ether in the reaction mixture is 5 to 15% by weight.

8. Transparent coating pursuant to claim 1, wherein the trifunctional polyol comprises a polyether polyol comprised of one of the group consisting of trimethylolpropane and the reaction product of glycerin and propylene oxide.

9. Transparent coating pursuant to claim 1, wherein a polyester polyol lactone based on trimethylolpropane or the reaction product of glycerin and epsilon-caprolactone is used as the trifunctional polyol.

10. Transparent coating pursuant to claim 1, wherein said reaction mixture has an NCO/OH ratio of 0.8 to 1.1.

11. Transparent coating pursuant to claim 10, wherein said NCO/OH ratio is approximately 0.9.

12. Transparent coating pursuant to claim 1, wherein said reaction mixture comprises one or more leveling agents in an amount of 0.05 to 0.15% by weight.

13. Transparent coating pursuant to claim 1, wherein the reaction mixture contains 0.5 to 2% by weight of bis(1,2,2,6,6-pentamethyl-4-piperidyl) sebacate as an agent for protection against light.

14. Transparent coating pursuant to one claim 1, wherein the reaction mixture contains agents that absorb ultraviolet light in an amount of 0.5 to 5% by weight.

15. Monolithic window or pane made of glass and/or plastic material, provided with a coating pursuant to one claim 1.