Thin-film magnetic head provided with a magnetic film having regions of different magnetostriction constants and method of fabricating the same

• US 4,750,072 A
• Filed: 02/11/1986
• Issued: 06/07/1988
• Est. Priority Date: 02/20/1985
• Status: Expired due to Fees

• Current Assignee: Hitachi, Ltd.
• Original Assignee: Hitachi, Ltd.
• Inventors: Takagi, Masayuki
• Primary Examiner(s): Hecker, Stuart N.
• Assistant Examiner(s): Urcia, Benjamin E.
• Application Number:
  US06/828,348
• Time in Patent Office: 847 Days
• Field of Search: 360/110, 360/113, 360/119, 360/122, 360/125-127, 29/603
• US Class Current: 360/125.54
• CPC Class Codes: G11B 5/3113 for improving the magnetic domain structure or avoiding the formation or displacement of undesirable magnetic domains
• CPC Class Codes: G11B 5/3163 Fabrication methods or processes specially adapted for a particular head structure, e.g. using base layers for electroplating, using functional layers for masking, using energy or particle beams for shaping the structure or modifying the properties of the basic layers

Abstract

A thin-film magnetic head provided with a magnetic thin film having a magnetostrictive characteristic is disclosed in which a central part of magnetic core formed of the magnetic thin film has a positive magnetostriction constants, and side parts of the magnetic core on both sides of the central part have negative magnetostriction constants. Thus, when a stress due to the patterning of the magnetic core varies the magnetic characteristic of the magnetic core, the permeability of the magnetic core becomes high, and the magnetic stability thereof is improved. Accordingly, a signal reproduced by this magnetic head has a high output level, and is low in noise level.

Claims

1. A thin-film magnetic head comprising:

a lower thin film made of a magnetic material;

an insulating member formed on an end portion of said lower thin film;

an upper thin film made of a magnetic material and overlying said lower thin film and said insulating gap member, one end of said upper thin film being bonded to one end of said lower thin film, the other end of said upper thin film and the other end of said lower thin film facing each other through said insulating member to form a magnetic gap, each of said lower thin film and said upper thin film being divided into a central region and a side region existing in substantially the same plane, said central region having one of a positive magnetostriction constant and a negative magnetostriction constant, said side region having the other magnetostriction constant; and

a thin-film coil conductor disposed so as to pass through a space surrounded by said upper and lower thin films.

2. A thin-film magnetic head according to claim 1, wherein said positive magnetostriction constant is less than or equal to 0.6×

10^-6, and said negative magnetostriction constant is greater than or equal to -0.6×

10^-6.

3. A thin-film magnetic head according to claim 1, wherein the central region of each of said upper and lower thin films has said positive magnetostriction constants, and the side region of each of said upper and lower thin films has said negative magnetostriction constants.

4. A thin-film magnetic head according to claim 3, wherein said upper and lower thin films are made of a Ni-Fe alloy.

5. A thin-film magnetic head according to claim 1, wherein in each of said upper thin film and said lower thin film, said central region is different in composition from said side region.

6. A thin-film magnetic head comprising:

an insulating substrate;

a lower thin-film magnetic core formed on said insulating substrate, having a central part and side parts existing in substantially the same plane and made of a Ni-Fe alloy, central part of said lower thin-film magnetic core said extending from one end thereof where a magnetic gap is formed to the other end opposite to said one end and having positive magnetostriction constants, said side parts of said lower thin-film magnetic core existing on both sides of said central part and having negative magnetostriction constants;

a coil conductor and an insulator both formed on said lower thin-film magnetic core; and

an upper thin-film magnetic core made of a Ni-Fe alloy, having a central part and side parts existing in substantially the same plane and extended on said coil conductor and said insulator in such a manner that said one end of said lower thin-film magnetic core and one end of said upper thin-film magnetic core face each other through said insulator to form said magnetic gap, and the other end of said upper thin-film magnetic core is kept in contact with the other end of said lower thin-film magnetic core, said central part of said upper thin-film magnetic core extending from said one end to said other end thereof and having positive magnetostriction constants, said side parts of said upper thin-film magnetic core existing on both sides of said central part and having negative magnetostriction constants.

7. A thin-film magnetic head according to claim 6, wherein the absolute value of each of said positive magnetostriction constants and said negative magnetostriction constants lies in a range from zero to 0.6×

10^-6.

8. A thin-film magnetic head according to claim 6, wherein said insulating substrate includes an insulating plate which is made of at least one material selected from a group consisting of Al₂ O₃ -TiC ceramics, Al₂ O₃ -TiO₂ ceramics, SiC, Zn ferrite, Ni-Zn ferrite, and Mn-Zn ferrite, and an Al₂ O₃ film formed on said insulating plate.

9. A thin-film magnetic head according to claim 6, wherein said coil conductor is made of copper.

10. A thin-film magnetic head according to claim 6, wherein said insulator includes an Al₂ O₃ film for forming said magnetic gap and a polyimide layer for insulating said coil conductor.

11. A method of fabricating a thin-film magnetic head, comprising the steps of:

forming a central region of a lower thin-film magnetic core on an underlying layer, said central region of said lower thin-film magnetic core having one of positive magnetostriction constants and negative magnetostriction constants;

forming side regions of said lower thin-film magnetic core in substantially the same plane and on both sides of said central region of said lower thin-film magnetic core, said side regions of said lower thin-film magnetic core having the other magnetostriction constants;

forming an insulating magnetic-gap layer on an end portion of said lower thin-film magnetic core;

forming a coil conductor above said lower thin-film magnetic core, said coil conductor being buried in an insulator; and

forming a central region of an upper magnetic core, said central region having one of positive magnetostriction constants and negative magnetostriction constants;

forming side regions of said upper thin-film magnetic core in substantially the same plane and on both sides of sides of said central region of said upper thin-film magnetic core, said side regions of said upper thin-film magnetic core having the other magnetostriction constants;

wherein said upper thin-film magnetic core is formed in such a manner that one end of said upper thin-film magnetic core is kept in contact with one of said lower thin-film magnetic core, the other end of said upper end thin-film magnetic core and the other end of said lower thin-film magnetic core face each other through said insulating magnetic-gap layer, and part of said coil conductor is surrounded by said upper and lower thin-film magnetic cores through said insulator.

12. A method of fabricating a thin-film magnetic head according to claim 11, wherein the step of forming said lower thin-film magnetic core and the step of forming said upper thin-film magnetic core include a step of making a thin film of a magnetic material through sputtering techniques.

13. A method of fabricating a thin-film magnetic head according to claim 11, wherein the step of forming said lower thin-film magnetic core and the step of forming said upper thin-film magnetic core include a step of making a thin film of a magnetic material through plating techniques.

14. A method of fabricating a thin-film magnetic head according to claim 11, wherein the step of forming said lower thin-film magnetic core and the step of forming said upper thin-film magnetic core include a step of forming said central region and said side region by different processes.

15. A method of fabricating a thin-film magnetic head according to claim 12, wherein the step of forming said insulating magnetic-gap layer includes a step of forming an insulating layer by sputtering, and the step of forming said coil conductor includes a step of forming a metal film by sputtering.

16. A method of fabricating a thin-film magnetic head according to claim 14, wherein said central region is made of a first Ni-Fe alloy, and said side region is made of a second Ni-Fe alloy which is different in composition from said first Ni-Fe alloy.