Metal halogen electrochemical cell

• US 4,766,045 A
• Filed: 05/04/1987
• Issued: 08/23/1988
• Est. Priority Date: 03/03/1986
• Status: Expired due to Fees

• Current Assignee: Exxon Research and Engineering Company (Exxon Mobil Corporation)
• Original Assignee: Exxon Research and Engineering Company (Exxon Mobil Corporation)
• Inventors: Bellows, Richard J., Kantner, Edward
• Primary Examiner(s): Skapars, Anthony
• Application Number:
  US07/045,377
• Time in Patent Office: 477 Days
• Field of Search: 429/101, 429/105, 429/199, 429/252, 429/248, 429/15, 429/50, 429/198, 429/13
• US Class Current: 429/105
• CPC Class Codes: H01M 10/365 Zinc-halogen accumulators
• CPC Class Codes: H01M 12/085 Zinc-halogen cells or batteries
• CPC Class Codes: Y02E 60/10 Energy storage using batteries

Abstract

It has now been discovered that reduction in the coulombic efficiency of metal halogen cells can be minimized if the microporous separator employed in such cells is selected from one which is preferably wet by the aqueous electrolyte and is not wet substantially by the cathodic halogen.

Claims

1. An electrochemical cell having a metal bromine couple, said cell comprising:

an electrode structure on which the metal of the couple is deposited during charging of the cells;

the counterelectrode structure at which cathodic bromine is generated during charging of the cell;

an aqueous electrolyte comprising an aqueous metal bromide solution, the metal being the same as the metal of the metal bromine couple, said aqueous electrolyte containing a water soluble complexing agent capable of forming a water immiscible complex with cathodic bromine; and

a microporous separator between said electrode and said counterelectrode structure, said microporous separator being selected from separators which are preferentially wet by aqueous electrolyte and are not wet by the water immiscible complex of cathodic bromine.

2. The cell of claim 1 wherein said separator is selected from the material which when vertically immersed in a container containing aqueous electrolyte and a water immiscible bromine complex, the resultant level of bromine complex in the separator is substantially equal to the level of the bromine complex in the container.

3. The cell of claim 1 wherein separator selected from one which is placed in contact with a water immiscible complex of cathodic bromine to form a negative angle.

4. The cell of claim 1 wherein said metal is zinc.

5. In an electrochemical cell of the type having a zinc bromine couple;

an electrode structure on which zinc is deposited during charging of the cell;

a counterelectrode structure at which cathodic bromine is generated during charging of the cell;

an aqueous zinc bromide electrolyte solution including a water soluble complexing agent capable of forming a water immiscible complex with cathodic bromine; and

wherein said cell includes a microporous separator between the electrode and counterelectrode structure, the improvement comprising;

selecting as the microporous separator a material which is preferentially wet by aqueous electrolyte and is not wet by the water immiscible complex of cathodic bromine.

6. A method of enhancing the coulombic efficiency of electrochemical cells having microporous separators and employing as the electrolyte an aqueous metal bromide solution containing a water soluble complexing agent capable of forming a water immiscible complex with bromine, said method comprising:

using a microporous separator selected from separators which are preferentially wet by aqueous electrolyte and are not wet by said water immiscible bromine complex.