Thermoplastic moulding compositions having flame-retarding properties

• US 4,766,165 A
• Filed: 06/05/1986
• Issued: 08/23/1988
• Est. Priority Date: 06/14/1985
• Status: Expired due to Fees

• Current Assignee: Bayer AG
• Original Assignee: Bayer AG
• Inventors: Lindner, Christian, Muller, Friedemann, Peters, Horst, Kress, Hans-Jurgen, Buekers, Josef, Todtemann, Gert
• Primary Examiner(s): Kight, John
• Assistant Examiner(s): Morgan, Kriellion
• Application Number:
  US06/870,840
• Time in Patent Office: 810 Days
• Field of Search: 524/140, 524/141, 524/142, 524/504, 524/520, 524/130, 524/132, 524/135, 524/139, 525/67, 525/68, 525/69, 525/146, 525/148
• US Class Current: 524/140
• CPC Class Codes: C08K 5/51 Phosphorus bound to oxygen
• CPC Class Codes: C08L 25/02 Homopolymers or copolymers of hydrocarbons
• CPC Class Codes: C08L 2666/02 Organic macromolecular compounds, natural resins, waxes or and bituminous materials
• CPC Class Codes: C08L 27/18 Homopolymers or copolymers or tetrafluoroethene
• CPC Class Codes: C08L 51/04 grafted on to rubbers
• CPC Class Codes: C08L 69/00 Compositions of polycarbonates; Compositions of derivatives of polycarbonates

Abstract

The present invention relates to flame-retarding moulding compositions which are based on thermoplastic polycarbonates, copolymers of styrenes and maleic anhydride, phosphorus compounds of the formula (I) ##STR1## tetrafluoroethylene polymers, small amounts of graft polymers and optionally halogen compounds and which in addition can contain stabilizers, pigments, flow agents, release agents and/or antistatics, and to a process for their preparation.

Claims

1. A thermoplastic moulding composition, containing

(A) 50-90 parts by weight of a thermoplastic aromatic polycarbonate, based on the diphenols consisting essentially of the formula ##STR4## wherein A is a single bond, C₁ -C₅ -alkylene, C₂ -C₅ -alkylidene, C₅ -C₆ -cycloalkylidene, --S-- or --SO₂ --, Hal is chlorine or bromine, x is 0, 1 or 2 and "n" is 1 or 0;

(B) 10-50 parts by weight of a copolymer of random structure of

3. A moulding composition according to claim 1, in which the thermoplastic aromatic polycarbonate of component (A) is a bisphenol A homopolycarbonate or is a copolycarbonate of bisphenol A with up to 15% by weight, relative to the total weight of diphenols, of 2,2-bis-(3,5-dibromo-4-hydroxyphenyl)-propane.

4. A moulding composition according to claim 1, in which the copolymer of component (B) comprises, as the nuclear-alkylated styrene of monomer(s) 1 , p-methylstyrene, vinyltoluene, 2,4-dimethylstyrene or a mixture thereof.

5. A moulding composition according to claim 1, in which the compolymer of component (B) consists of monomer(s) 1 in an amount of 90-75% by weight and maleic anhydride in an amount of 10 to 25% by weight.

6. A moulding composition according to claim 1, in which the halogen compound of component (C) is a bromine compound.

7. A moulding composition according to claim 1, in which the halogen compound of component (C) is any of those hereinbefore specifically mentioned.

8. A moulding composition according to claim 1, in which component (D) is present in a quantity of 2 to 15 parts by weight.

9. A moulding composition according to claim 1, in which component (E) is present in a quantity of 0.1 to 1.0 part by weight.

10. A moulding composition according to claim 1 in which the graft polymer (F) has been prepared from 30 to 80 parts by weight of the mixture (1) on 70 to 20 parts by weight of the rubber (2).

11. A moulding composition according to claim 1, additionally containing at least one additive selected from stabilizers, pigments, flow agents, release agents and antistatics.

12. Any one of the moulding compositions according to claim 1, which are hereinbefore specifically indentified.

13. A process for the production of a moulding composition according to claim 1, in which the components (A), (B), (D), (E) and (F) and, if present, (C) are mixed together and then melt-compounded or melt-extruded at temperatures of 200°

to 330°

C. in a melt-compounding or melt-extrusion unit.

14. A process for the production of a moulding compositions according to claim 1, in which a solution of components (A), (B), (D), (E) and (F) and, if present, (C) is mixed in suitable organic solvent(s) and the solution mixture is then evaporated in an evaporation unit.

15. A process according to claim 12 or the production of a moulding composition in which at least one additive selected from stabilizers, pigments, flow agents, release agents and antistatics is included in the mixture or solution.

16. A moulding composition whenever produced by the process of claim 12.

17. A moulded article whenever formed of a moulding composition according to claim 1.

2. 95-70% by weight of vinyl aromatic(s) selected from styrene, α

-methylstyrene, nuclear-alkylated styrene and mixtures thereof and

2. 5-30% by weight of maleic anhydride,

(C) 0-15 parts by weight of a low-molecular or high-molecular halogen compound, in each case relative to 100 parts by weight of components (A) and (B) and (C), the halogen content which results from the components (A) and (C) being in each case between 3 and 10% by weight, relative to the total weight of the components (A) and (C), characterized in that they additionally contain 1-20 parts by weight, relative to 100 parts by weight of components (A) and (B) and, if present, (C), of a phosphorous compound of the formula ##STR5## wherein R₁, R₂ and R₃ independently of one another represent an optionally halogenated C₆ -C₂₀ -aryl radical and n and m independently of each other are 0 or 1, and

(E) 0.05-2.0 parts by weight, relative to 100 parts by weight of (A) and (B) and, if present, (C), of a tetrafluoroethylene polymer with mean particle sizes of 0.05-20 μ

m and a density of 1.2-1.9/cm³, the component (E) being employed in the form of a coagulated mixture of emulsions of the tetrafluoroethylene polymers (E) with emulsions of graft polymers (F) obtained from

(1) 5-90 parts by weight of a mixture of;

(i) 50-95% weight of styrene, α

-methylstyrene, nuclear-substituted styrene, methyl methacrylate or mixtures thereof and

(ii) 50-5% by weight of (meth)-acrylonitrile, methyl methacrylate, maleic anhydride, N-substituted maleimide or mixtures thereof on

(2) 95-10 parts by weight of a rubber having a glass temperature T_G of ≦

10°

C., and the weight ratio of (F)/(E) being between 95;

5 and 60;

40 and the content of component (F), relative to 100 parts by weight of (A) and (B) and, if present (C) being between 0.1 and 3.0 parts by weight.