• US 4,768,859 A
• Filed: 10/22/1987
• Issued: 09/06/1988
• Est. Priority Date: 01/24/1984
• Status: Expired due to Term

• Current Assignee: Showa Electric Wire & Cable Company Limited, Kabushiki Kaisha Toshiba (Toshiba Corporation)
• Original Assignee: Showa Electric Wire & Cable Company Limited, Kabushiki Kaisha Toshiba (Toshiba Corporation)
• Inventors: Maki, Hironori, Kokubo, Osamu, Yagi, Kenji, Imagawa, Hiroshi, Kasori, Mituo
• Primary Examiner(s): Sikes, William L.
• Assistant Examiner(s): Ullah, Akm E.
• Application Number:
  US07/111,153
• Time in Patent Office: 320 Days
• Field of Search: 350/96.29, 350/96.31, 350/96.34, 501/35, 501/66, 501/69
• US Class Current: 385/144
• CPC Class Codes: C03C 13/046 Multicomponent glass compositions
• CPC Class Codes: C03C 3/118 containing aluminium

Abstract

A cladding glass for optical fiber comprises 60 to 80% by weight of silicon dioxide (SiO₂), 0.5 to 10% by weight of aluminum oxide (Al₂ O₃), 9 to 17% by weight of an alkali metal oxide, 3 to 15% by weight of boron oxide (B₂ O₃) and more than 0 but not more than 3% by weight of fluorine (F). The cladding glass of this invention can simultaneously satisfy low refractive index and lowered viscosity, and is also excellent in water resistance and weathering resistance.

Claims

1. A cladding glass for optical fiber, which consists essentially of 60 to 80% by weight of silicon dioxide (SiO₂);

4 to 7% by weight of aluminum oxide (Al₂ O₃);

7 to 12% by weight of boron oxide (B₂ O₃), 6 to 8% by weight of sodium oxide (Na₂ O), 3.5 to 6% by weight of potassium oxide (K₂ O), and 2 to 4% by weight of lithium oxide (Li₂ O), such that the total content of alkali metal oxide in said cladding glass ranges between about 9 and 17% by weight;

from 0 to 8% by weight of an alkaline earth metal oxide;

more tha 0 and up to 7% by weight of at least one selected from the group consisting of zinc oxide (ZnO), zirconium dioxide (ZrO₂) and titanium dioxide (TiO₂), wherein the amount of TiO₂ is less than 1% of the cladding glass composition; and

more than 0 but not more than 3% by weight of fluorine (F), said cladding glass having a refractive index value of not more than 1.511 4.

2. The cladding glass for optical fiber according to claim 1, wherein the content of fluorine is 0.5 to 3.0% by weight.

3. The cladding glass for optical fiber according to claim 1, containing 0 to 3% by weight of an alkalilne earth metal oxide and 0 to 3% by weight of at least one selected from the group consisting of zinc oxide (ZnO), zirconium dioxide (ZrO₂) and titanium dioxide (TiO₂).

4. The cladding glass for optical fiber according to claim 1, wherein the alkali metal oxide comprises 6 to 8 1% by weight of sodium oxide (Na₂ O), 3.5 to 6% by weight of potassium oxide (K₂ O) and 2 to 4% by weight of lithium oxide (Li₂ O), and further containing 0 to 3% by weight of an alkaline earth metal oxide and 0 to 3% by weight of at least one selected from the group consisting of zinc oxide (ZnO), zirconium dioxide (ZrO₂) and titanium dioxide (TiO₂).

5. The cladding glass for optical fiber according to claim 4, wherein the alkaline earth metal oxide is one or both of calcium oxide (CaO) and magnesium oxide (MgO).

6. A cladding glass for optical fiber according to claim 1, wherien the total amount of sodium oxide (Na₂ O), potassium oxide (K₂ O) and lithium oxide (Li₂ O) in said cladding glass is 12 to 16% by weight.

7. The cladding glass for optical fiber according to claim 1 wherein the amount of silicon dioxide is from 66 to 71% by weight.

8. An optical fiber comprising a core glass, and a cladding glass according to claim 1.

9. An optical fiber according to claim 8, wherein said core glass comprises from 35 to 45% by weight of SiO₂ ;

35 to 45% by weight of BaO;

3 to 7% by weight of SiO₂ ;

35 to 45% by weight of BaO;

3 to 7% by weight of Al₂ O₃ ;

9 to 13% by weight B₂ O₃ ;

1.2 to 6% by weight of at least one selected from the group consisting of Na₂ O, K₂ O and Li₂ O, with Na₂₀ being more than 2.5% weight; and

4 to 11% by weight of at least one selected from the group consisting of MgO and CaO.

10. An optical fiber according to claim 8, wherein said core glass comprises from 50 to 70% by weight of SiO₂ ;

0.5 to 7% by weight of Al₂ O₃ ;

4 to 15% by weight B₂ O₃ ;

10 to 23% by weight of at least one selected from the group consisting of Na₂ O, and Li₂ 0;

10% by weight or less of CAO; and

5% or less by weight of MgO.

11. An opitcal fiber according to claim 8, wherein said core glass additionally comprises fluorine.

12. A cladding glass according to claim 1, wherein said alkaline earth metal oxide is absent.