Electrophotosensitive member having an overcoat layer and a process for preparing the same

• US 4,804,607 A
• Filed: 09/28/1987
• Issued: 02/14/1989
• Est. Priority Date: 10/04/1986
• Status: Expired due to Term

• Current Assignee: Minolta Camera Kabushiki Kaisha
• Original Assignee: Minolta Camera Kabushiki Kaisha
• Inventors: Atsumi, Fumitoshi
• Primary Examiner(s): NOT, DEFINED
• Application Number:
  US07/101,485
• Time in Patent Office: 505 Days
• Field of Search: 430/67, 430/130, 430/132, 430/128, 427/257, 428/409
• US Class Current: 430/67
• CPC Class Codes: G03G 5/14704 comprising inorganic material
• CPC Class Codes: Y10T 428/31 Surface property or characteristic of web, sheet or block

Abstract

Disclosed is an electrophotosensitive member and its preparing method. The electrophotosensitive member comprises an electrically conductive substrate, a photosensitive layer, and an overcoat layer having a rough surface with convexities and concavities. The number of convexities and concavities are about 500 to 3000 per 1 cm in a linear distance, and the maximum depth difference of the convexities and concavities is about 0.05 to 1.5 μm. The rough surface having the convexities and concavities is formed directly on the overcoat layer. The electrophotosensitive member according to the present invention reduces the friction coefficient of the contacting area between the electrophotosensitive member and a cleaning device, and improves the durability of the overcoat layer and the photosensitive layer.

Claims

1. In an electrophotosensitive member which comprises;

an electrically conductive substrate,

a photosensitive layer formed on said substrate,

and an overcoat layer formed on said photosensitive layer,

the improvement wherein said overcoat layer has a rough surface having convexities and concavities with a maximum depth difference of about 0.05 to about 1.5 μ

m in an amount of about 500 to about 3000 per 1 cm in linear distance.

2. An electrophotosensitive member according to claim 1, wherein said rough surface of the overcoat layer is a heat-treated layer.

3. An electrophotosensitive member according to claim 1, wherein said overcoat layer is a heat-treated ceramic layer comprising substantially silicon.

4. An electrophotosensitive member according to claim 1, wherein said photosensitive layer is a layer composed of an organic resin and a phthalocyanine pigment dispersed in said organic resin, and said overcoat layer is a layer composed of an inorganic material selected from the group consisting of silicon oxide (SiO), silicon dioxide (SiO₂), titanium oxide (TiO₂), aluminum oxide (Al₂ O₃) and silicon carbide (SiC), and is formed by evaporating said inorganic material in a vacuum.

5. A process for preparing an electrophotosensitive member which comprises;

an electrically conductive substrate, a photosensitive layer formed on said substrate, and an overcoat layer formed on said photosensitive layer comprising;

a first step of coating a photoconductive material on said substrate to form said photosensitive layer;

a second step of evaporating an inorganic material in a vacuum to form said overcoat layer on said photosensitive layer; and

a third step of heating said support coated with said photosensitive layer and said overcoat layer under a predetermined temperature to form a rough surface on said overcoat layer having convexities and concavities with a maximum depth difference of about 0.05 to about 1.5 μ

m in an amount of about 500 to about 3000 per 1 cm in a linear distance.

6. A process according to claim 5, wherein said support coated with said photosensitive layer and said overcoat layer is heated at a temperature of about 40°

C. to 70°

C. at said third step.

7. A process according to claim 5, wherein said support coated with said photosensitive layer and said overcoat layer is heated in a protective case at said third step.

8. A process according to claim 7, wherein said third step is carried out in a thermostatic chamber.