Use of radiation-crosslinked polyethylene

• US 4,809,612 A
• Filed: 04/06/1987
• Issued: 03/07/1989
• Est. Priority Date: 12/11/1981
• Status: Expired due to Fees

• Current Assignee: Dynamit Nobel AG
• Original Assignee: Dynamit Nobel AG
• Inventors: Umbach, Hans, Rammensee, Horst, Ballreich, Kurt, Homburg, Axel
• Primary Examiner(s): Kyle, Deborah L.
• Assistant Examiner(s): WASIL, DANIEL D
• Application Number:
  US07/034,989
• Time in Patent Office: 701 Days
• Field of Search: 102/444, 102/464, 102/465, 102/466, 102/467, 102/430, 102/513, 102/501
• US Class Current: 102/466
• CPC Class Codes: B29C 2035/0877 using electron radiation, e.g. beta-rays
• CPC Class Codes: B29C 71/04 by wave energy or particle radiation , e.g. for curing or vulcanising preformed articles during moulding, e.g. in a mould B29C35/08
• CPC Class Codes: B29K 2023/06 PE, i.e. polyethylene
• CPC Class Codes: B29K 2105/24 crosslinked or vulcanised
• CPC Class Codes: B29L 2031/7772 Cartridges
• CPC Class Codes: F42B 5/30 of plastics , i.e. the cartridge-case tube is of plastics
• CPC Class Codes: F42B 8/04 Blank cartridges, i.e. primed cartridges without projectile but containing an explosive or combustible powder charge

Abstract

Polyethylene crosslinked by high-energy radiation, preferably electron beams, is an effective material for the manufacture of ammunition elements, preferably cases for cartridges. The case is produced by irradiating a molded case component of polyethylene with high-energy radiation.

Claims

1. A cartridge case of training ammunition useful in an automatic firearm having a cartridge case with walls heated during firing up to temperatures at which non-crosslinked polyethylene starts to melt and to which a non-crosslinked polyethylene-containing cartridge case sticks to cause contamination of the firearm, said cartridge case comprising a tubular component molded of polyethylene and, thereafter, exposed to energy radiation to crosslink the polyethylene from an outer exposed surface of the component practically throughout the entire component so that the cartridge case has the ability to be removed from a cartridge chamber of an automatic firearm heated to temperatures up to 250°

C. without residues of the crosslinked polyethylene sticking to heated walls of the cartridge chamber.

2. A cartridge case according to claim 1, wherein the polyethylene of the tubular molded component is crosslinked with electron beams to exhibit a degree of crosslinking of between 40 and 90%.

3. A cartridge case according to claim 2, wherein the polyethylene of the tubular component has a molecular weight of between 80,000 and 120,000 and a density higher than 0.94 g/cm³.

4. A cartridge case of ammunition useful in automatic firearm having a cartridge chamber with walls heated during firing up to temperatures at which non-crosslinked polyethylene starts to melt and to which a non-crosslinked polyethylene-containing cartridge case sticks to cause contamination of the firearm, said cartridge case comprising a tubular molded component formed of polyethylene having a molecular weight between 80,000 and 120,000 and a density higher than 0.94 g/cm³ and, thereafter, exposed to energy radiation to crosslink the polyethylene from an outer exposed surface of the tubular component practically throughout the entire component so that the polyethylene of the tubular component is crosslinked to exhibit a degree of crosslinking of between 40 and 90% and so that the cartridge case has the ability to be removed from a cartridge chamber of an automatic firearm heated to temperatures up to 250°

C. without residues of the crosslinked polyethylene sticking to heated walls of the cartridge chamber.

5. A cartridge of training ammunition useful in an automatic firearm having a cartridge chamber with walls heated during firing up to temperatures at which non-crosslinked polyethylene starts to melt and to which a non-crosslinked polyethylene-containing cartridge case sticks to cause contamination of the firearm, said cartridge comprising a radiation crosslinked polyethylene case and an associated dummy projectile, said case having been formed by injection molding of polyethylene into an appropriate configuration and the polyethylene of the injection molded case thereafter crosslinked by irradiating with energy radiation from an outer exposed surface of the case practically throughout the entire case so that the case of crosslinked polyethylene exhibits the ability to be removed from a cartridge chamber of an automatic firearm heated to temperatures up to 250°

C. without residues of the crosslinked polyethylene sticking to heated walls of the cartridge chamber.

6. A cartridge according to claim 5, wherein the polyethylene of the injection molded case is crosslinked with electron beams.

7. A cartridge case of training ammunition useful in an automatic firearm having a cartridge chamber with walls heated up during firing to temperatures at which non-crosslinked polyethylene starts to melt and to which a non-crosslinked polyethylene-containing cartridge case sticks to cause contamination of the firearm, said training cartridge comprising a radiation crosslinked polyethylene case and associated dummy projectile, said case having been formed by injection molding of polyethylene having a molecular weight between 80,000 and 120,000 and a density higher than 0.94 g/cm³ into an appropriate configuration and the polyethylene of the injection molded case thereafter having been crosslinked by energy radiation from an outer exposed surface of the case practically throughout the entire case, said radiation comprising electron beams accelerated at 3 to 10 million volts and at a dosage rate of 10 to 1,000 Mrad/minute, so that the crosslinked polyethylene cartridge case exhibits a degree of crosslinking of between 40 and 90% and so that the crosslinked polyethylene case exhibits the ability to be removed from a cartridge chamber of an automatic firearm heated to temperatures up to 250°

C. without residues of the crosslinked polyethylene sticking to heated walls of the cartridge chamber.

8. A method for producing a case for a training ammunition cartridge to be used in an automatic firearm having a cartridge chamber with walls heated during firing up to temperatures at which non-crosslinked polyethylene starts to melt and to which a non-crosslinked polyethylene-containing cartridge case sticks to cause contamination of the firearm, said method comprising forming the cartridge case by molding polyethylene into an appropriate tubular configuration and, thereafter, exposing the polyethylene of the molded cartridge case to energy radiation to crosslink the polyethylene from an outer exposed surface of the case practically throughout the entire case so that the cartridge case exhibits the ability to be removed from a cartridge chamber of an automatic firearm heated to temperatures up to 250°

C. without residues of the crosslinked polyethylene sticking to heated walls of the cartridge chamber.

9. A method according to claim 8, wherein the energy radiation consists of electron beams accelerated at 3 to 10 million volts and at a dosage rate of 10 to 1,000 Mrad/minute and wherein the polyethylene of the molded case is crosslinked to exhibit a degree of crosslinking of between 40 and 90%.

10. A cartridge case of training ammunition in a cartridge chamber of an automatic firearm, said cartridge chamber having walls that during the firing of the firearm heat up to temperatures at which non-crosslinked polyethylene starts to melt and to which a non-crosslinked polyethylene-containing cartridge case sticks to cause contamination of the firearm, said cartridge case comprising a tubular component molded of polyethylene and, thereafter, exposed to energy radiation to crosslink the polyethylene from an outer exposed surface of the component practically throughout the entire component so that the cartridge case has the ability to be removed from a cartridge chamber of an automatic firearm heated to temperatures up to 250°

C. without residues of the crosslinked polyethylene sticking to heated walls of the cartridge chamber.