Process for the preparation of aqueous polyurethane dispersions and solutions

• US 4,829,122 A
• Filed: 02/27/1987
• Issued: 05/09/1989
• Est. Priority Date: 06/07/1977
• Status: Expired due to Fees

• Current Assignee: Bayer AG
• Original Assignee: Bayer AG
• Inventors: Nachtkamp, Klaus, Grammel, Jurgen, Pedain, Josef, Noll, Klaus
• Primary Examiner(s): Ziegler, Jacob
• Application Number:
  US07/019,902
• Time in Patent Office: 802 Days
• Field of Search: 524/591
• US Class Current: 524/591
• CPC Class Codes: C03C 25/00 Surface treatment of fibres or filaments made from glass, minerals or slags
• CPC Class Codes: C08G 18/0804 Manufacture of polymers containing ionic or ionogenic groups
• CPC Class Codes: C08G 18/10 Prepolymer processes involving reaction of isocyanates or isothiocyanates with compounds having active hydrogen in a first reaction step
• CPC Class Codes: C08G 18/3256 Reaction products of polyamines with aldehydes or ketones
• CPC Class Codes: Y10T 428/31551 Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]

Abstract

The present invention therefore relates to a process for the preparation of aqueous solutions or dispersions of polyurethane-polyureas by the reaction in the aqueous phase of prepolymers which contain chemically built-in hydrophilic groups and/or external emulsifiers which are not bound chemically as well as at least two free isocyanate groups with organic compounds containing at least two primary and/or secondary amino groups, characterized in that the isocyanate prepolymer which has been hydrophilically modified and/or contains an external emulsifier is mixed, in the absence of water, with compounds containing at the most one free primary or secondary amino group and at least one blocked group which releases a free primary or secondary amino group in the presence of water and a total of at least two at least partially blocked primary and/or secondary amino groups, and the mixture is subsequently mixed with water.

The invention also relates to the dispersions or solutions obtained by this process and to their use for coating flexible and rigid substrates.

Claims

1. A process for the preparatio of aqueous dispersions of polyurthane polyureas by the reaction of (1) prepolymers which have at least two free isocyanate groups and contatin chemically fixed hydrophilic groups or external emulsifiers which are not chemically fixed with (2) organic compounds containingn at least two groups selected from the group consisting of primary and secondary amino groups characterized in that the isocyanate-contatining prepolymer component (1), which is hydrophilically modified or contains an external emulsifier, is mixed, in the absence of water, with the organic compound component (2) which contains at least two groups selected from the group consisting of primary and secondary amino groups wherein at most one amino group is a free primary or secondary amino group and at least one amino group is a blocked amino group which is substantially inert toward isocyanate groups at room temperature in the absence of moisture and which releases a free primary or secondary amino group in the presence of water, and the mixture obtained is subsequently mixed with an amount of water sufficient to provide aqueous dispersions with a solids content of less than about 70% by weight.

2. The process according to claim 1, characterized in that the nature and proportions of the reactants are chosen so that from about 0.25 to 1.5 free plus blocked amino groups which are reactive with isocyanate groups are present for each isocyanate group of the isocyanate prepolymer.

9. An aqeuous polyurethane polyurea dispersion produced by the process of claim 1.

3. A process for the production of an aqueous dispersion of a polyurethane polyurea comprising mixing in the absence of water

(a) a hydrophilic NCO-prepolymer having

(i) an average isocyanate functionality of from about 1.8 to 2.2,

(ii) an average molecular weight of from about 500 to 10,000, and

(iii) its hydrophilic properties contributed by dispersing centers selected from the group consisting of chemically incorporated cationic or anionic groups present in said NCO-prepolymer in from about 0.1 to 100 milliequivalents per 100 g of NCO-prepolymer, chemically incorporated ethylene oxide units present in said NCO-prepolymer in from about 0.5 to 30% by weight, based on the weight of the NCO polymer, and external emulsifiers present in about 1 to 30% by weight, based on the weight of the NCO-prepolymer, with

(b) a polyamine having

(i) at least two amino groups selected from the group consisting of primary amino groups and secondary amino groups,

(ii) at most one free primary of secondary amino group,

(iii) at least one blocked amino group which is substantially inert toard isocyanate groups at room temperature in the absence of moisture and which releases a free primary or secondary amino group in the presence of water, and

(iv) a molecular weight of from about 60 to 500, and subsequently mixing the mixture of components (a) and (b) with an amount of water sufficient to provide an aqueous dispersion with a solids content of less than about 70% by weight.

4. The process of claim 3 wherein the blocked amino groups are blocked with compounds selected from the group consisting of aldehydes and ketones.

5. The process of claim 3 wherein the equivalent ratio of isocyanate groups of the NCO-prepolymer to free plus blocked amino groups of the polyamine is between about 4:

1 and 1;

1.5.

6. An aqueous polyurethane polyurea dispersion produced by the process of claim 3.

7. The aqueous polyurethane polyurea dispersion of claim 6 wherein the particle size is from about 20-200 mm.

8. The aqueous polyurethane polyurea dispersion of claim 6 wherein the solids content is from about 40 to 70% by weight.