Method for rendering a substrate surface antithrombogenic

• US 4,865,870 A
• Filed: 07/07/1988
• Issued: 09/12/1989
• Est. Priority Date: 07/07/1988
• Status: Expired due to Fees

• Current Assignee: Becton, Dickinson & Co
• Original Assignee: Becton, Dickinson & Co
• Inventors: Solomon, Donald D., Hu, Can B., Shields, Nancy L.
• Primary Examiner(s): LUSIGNAN, MICHAEL R
• Application Number:
  US07/215,974
• Time in Patent Office: 432 Days
• Field of Search: 427/2, 427/322, 523/112, 525/54.1, 525/54.2, 525/54.22
• US Class Current: 427/2.1
• CPC Class Codes: A61L 33/0017 using a surface active agent

Abstract

A method for heparinizing a substrate includes applying a coating of ammonium salt to a substrate by steeping the substrate in a solution of the salt at an alkaline pH and contacting the coated substrate with a solution of a salt of heparin.

Claims

1. A method for heparinizing a polymeric substrate comprising:

(a) adjusting the pH of a solution of a surface active agent of the ammonium salt type in a solvent to above 7.5, said surface active agent having at least one alkyl group of 8 to 20 carbon atoms;

(b) steeping a polymeric substrate in said solution of adjusted pH whereby a coating of said surface active agent forms on said substrate;

(c removing said substrate having said coating from said solution of adjusted pH; and

(d) immersing said substrate having said coating in a solution of heparin whereby said heparin reacts with said coating of surface active agent to give a heparinized substrate.

2. The method of claim 1 wherein said polymeric substrate is selected from the group consisting of polyolefin, polyvinyl, polyacrylic, polyester, polyamide, polycarbonate, fluorinated polymer, cellulose acetate, silicone rubber and natural rubber, polyurethane, polyurethaneurea and silicone urethane copolymer.

3. The method of claim 1 wherein surface active agent is selected from the group consisting of a salt of a primary amine, secondary amine, tertiary amine, alkylenediame and a quaternary salt.

4. The method of claim 3 wherein said surface active agent is a secondary amine salt having at least one alkyl group of about 1 to 4 carbon atoms.

5. The method of claim 4 wherein said salt is dodecylmethylamine hydrochloride.

6. The method of claim 1 wherein said pH after adjusting is between from about 8 and 14.

7. The method of claim 1 wherein said adjusting is performed by adding an alkalinizing agent.

8. The method of claim 6 wherein said alkalinizing agent is selected from the group consisting of an amine soluble in said solvent, a metal hydroxide and ammonium hydroxide.

9. The method of claim 7 wherein said alkalinizing agent is an alkali metal hydroxide.

10. The method of claim 1 further comprising treating said heparinized substrate with a dialdehyde to stabilize said heparin.

11. The method of claim 10 wherein said dialdehyde is glutaraldehyde.

12. The method of claim 1 further comprising treating said polymeric substrate with a plasma prior to immersing said substrate in said solution of ammonium salt.

13. The method of claim 12 wherein said polymeric substrate is selected from the group consisting of polypropylene and polytetrafluoro ethylene

14. A method for rendering a substrate antithrombogenic comprising:

(a) adjusting the pH of a dispersion of a surface active agent of the ammonium salt type in a solvent to above 7.5;

(b) steeping a substrate in said solution of adjusted pH thereby causing a coating of said surface active agent to form on said substrate;

(c) removing said substrate having said coating thereon from said solution of adjusted pH; and

(d) immersing said substrate having said coating thereon in a solution of a sulfonated polysaccharide whereby said polysaccharide reacts with said coating of surface active agent to give an antithrombogenic substrate.

15. The method cf claim 14 wherein said substrate may be of a material selected from the group consisting of metal, glass, ceramic and polymer.

16. A method for heparinizing a polymeric substrate comprising:

(a) adjusting the pH of a solution of dodecylmethylammonium chloride in aqueous medium by adding a sufficient quantity of an alkalinizing agent to raise the pH of said solution to about 10.2;

(b) steeping a polymeric substrate in said solution of pH about 10.2 whereby a coating of dodecylmethylamine forms on said substrate;

(c) removing said substrate having said coating from said solution of pH about 10.2; and

(d) immersing said substrate having said coating in a solution of heparin, said heparin reacting with said coating to give a heparinized substrate.

17. The method of claim 16 wherein said alkalinizing agent is selected from the group consisting of a water soluble amine, ammonium hydroxide and an alkali metal hydroxide.

18. The method of claim 16 wherein said substrate is polyurethane.

19. The method of claim 16 further comprising treating said heparinized surface with glutaraldehyde to stabilize said heparin.

20. The method of claim 16 wherein said substrate is selected from the group consisting of polypropylene and polytetrafluoroethylene.

21. The method of claim 20 further comprising treating said substrate with a plasma prior to immersing said substrate in said solution of dodecyl methyl ammonium chloride.