Catalytic washcoat and method of preparation of the same
First Claim
1. The method of preparing a washcoating composition for use as a component of a catalytic coating which comprises the steps of preparing an aqueous colloidal solution of particles of one or more catalytically active non-noble metal doping oxide(s), contacting said solution with particles of a preformed washcoat base comprising a high surface area crystalline alumina, thereby uniformly adsorbing said doping particles thereon, limiting the amount of said doping oxide particles to amounts less than about 20% by weight of said doped preformed particles, and drying and calcining said doped preformed particles.
1 Assignment
0 Petitions
Accused Products
Abstract
The invention is concerned with a method of adsorbing uniformly onto preformed high surface area crystalline alumina one or more catalytically active non-noble (doping) oxide(s) and preferably alumina-stablilizing non-noble doping oxide(s), both from substantially neutral aqueous colloidal solutions thereof, drying and calcining the doped alumina to form an improved washcoating composition for receiving additionally catalytic noble metal particles.
42 Citations
17 Claims
- 1. The method of preparing a washcoating composition for use as a component of a catalytic coating which comprises the steps of preparing an aqueous colloidal solution of particles of one or more catalytically active non-noble metal doping oxide(s), contacting said solution with particles of a preformed washcoat base comprising a high surface area crystalline alumina, thereby uniformly adsorbing said doping particles thereon, limiting the amount of said doping oxide particles to amounts less than about 20% by weight of said doped preformed particles, and drying and calcining said doped preformed particles.
- 8. In a method of producing a catalytic structure comprising a support, a high surface area alumina-containing washcoat preformed thereon and a noble metal catalyst, the improvement of adsorbing onto said washcoat uniform particles of at least one catalytically active non-noble metal doping oxide and at least one alumina-stabilizing non-noble metal doping oxide, both from aqueous colloidal solutions.
- 11. A wash-coated catalytic support comprising a high surface area preformed crystalline alumina-containing washcoat base, a predominant amount of which carries uniformly adsorbed catalytically active colloidal particles of one or more non-noble metal doping oxides in amounts less than about 20% by weight.
-
15. A washcoated catalytic support as claimed in 12 and in which said doping oxides are selected from the group consisting of colloidal particle titania, zirconia, iron oxide, cerium oxide, lanthanum oxide, nickel oxide and chromium oxide adsorbed in amounts less than about 20% of the total weight of doping oxides and preformed particles.
-
17. A washcoated catalytic support comprising a high surface area preformed crystalline alumina-containing washcoat base, a predominant amount of which carries, uniformly adsorbed, a catalytically active non-noble colloidal metal doping oxide and an alumina-stabilizing non-noble colloidal metal doping oxide.
Specification