Azide gas generating composition for inflatable devices

• US 4,931,111 A
• Filed: 11/06/1989
• Issued: 06/05/1990
• Est. Priority Date: 11/06/1989
• Status: Expired due to Fees

• Current Assignee: Automotive Systems Laboratory, Incorporated (Ningbo Junsheng Investment Group Co., Ltd.)
• Original Assignee: Automotive Systems Laboratory, Incorporated (Ningbo Junsheng Investment Group Co., Ltd.)
• Inventors: Wilson, Michael A., Poole, Donald R.
• Primary Examiner(s): Lechert, Jr., Stephen J.
• Application Number:
  US07/432,150
• Time in Patent Office: 211 Days
• Field of Search: 149/35, 149/61, 149/77, 280/741
• US Class Current: 149/35
• CPC Class Codes: C06B 35/00 Compositions containing a metal azide
• CPC Class Codes: C06D 5/06 by reaction of two or more solids

Abstract

Gas generating compositions containing an inorganic metal azide, a primary metal oxide oxidizing compound and a secondary oxidizing compound in combination with clay as a means of controlling the burn rate. Metal nitrates are preferred as the secondary oxidizing compound.

Claims

1. An increased burn rate gas generating composition comprising a mixture of:

(a) about 50 to about 70 percent by weight of an inorganic metal azide,

(b) about 2 to about 30 percent by weight of a primary metal oxide oxidizing compound, and

(c) about 2 to about 40 percent by weight of a burn rate controlling mixture of a secondary metal oxidizing compound and clay wherein the weight ratio of said secondary oxidizing compound to said clay is about 1;

1 to about 1;

8.

2. The gas generating mixture of claim 1 wherein said inorganic metal azide is selected from at least one of an alkali metal azide and an alkaline earth metal azide and said secondary oxidizing compound is a metal nitrate or metal perchlorate.

3. The gas generating mixture of claim 2 wherein said primary metal oxide oxidizing compound is selected from the group consisting of at least one of the oxides of iron, nickel, silicon, manganese, aluminum, tantalum, niobium, and tin.

4. The gas generating mixture of claim 3 wherein said secondary oxidizing compound is selected from the group consisting of at least one of the nitrates of lithium, sodium, potassium, magnesium, calcium, strontium, and barium or the perchlorates of lithium, sodium, potassium, and barium.

5. The gas generating composition of claim 4 wherein said alkali metal azide is sodium azide, said primary metal oxide oxidizing compound is ferric oxide, said secondary metal nitrate oxidizing compound is potassium nitrate, and said clay is a bentonite clay.

6. A method of inflating an automobile or aircraft safety crash bag comprising the combustion of a pyrotechnic material at an increased burn rate with the production of only non-toxic gases, wherein an increased burn rate is obtained by utilizing a mixture of particles comprising:

(a) about 50 to about 70 percent by weight of an inorganic metal azide,

(b) about 2 to about 30 percent by weight of a primary metal oxide oxidizing compound, and

(c) about 2 to about 40 percent by weight of a burn rate controlling mixture of a secondary metal oxidizing compound and clay, wherein the ratio of said secondary metal oxidizing compound to clay is about 1;

1 to about 1;

8.

7. The process of claim 6 wherein said increased burn rate is obtained utilizing a pelletized mixture wherein said inorganic azide is selected from the group consisting of at least one of an alkali metal azide and an alkaline earth metal azide, said primary metal oxidizing compound is iron oxide, said secondary metal oxidizing compound is potassium nitrate, and said clay is bentonite clay.