Process of vitrifying radioactive liquid waste with suppressed formation of gaseous ruthenium

• US 4,943,395 A
• Filed: 03/23/1989
• Issued: 07/24/1990
• Est. Priority Date: 03/28/1988
• Status: Expired due to Term

• Current Assignee: Japan Nuclear Cycle Development Institute
• Original Assignee: Doryokuro Kakunenryo Kaihatsu Jigyodan
• Inventors: Matsunaka, Kazuhisa, Sasaki, Noriaki
• Primary Examiner(s): Locker, Howard J.
• Application Number:
  US07/327,773
• Time in Patent Office: 488 Days
• Field of Search: 252/629, 252/631, 65/32.1, 65/32.2, 250/506.1, 264/56, 501/35, 423/22
• US Class Current: 588/11
• CPC Class Codes: G21F 9/12 by absorption; by adsorption; by ion-exchange
• CPC Class Codes: G21F 9/305 Glass or glass like matrix C03B5/005 takes precedence; compositional aspects C03C

Abstract

An improved process of vitrifying a radioactive liquid waste by absorbing a radioactive liquid waste into a glass frit cartridge made of molded glass fibers and heat-melting the cartridge to vitrify the liquid waste. The invention is characterized by absorbing a radioactive liquid waste containing ruthenium into the glass frit cartridge together with a reducing agent. By the process of the invention, the formation of gaseous ruthenium is effectively suppressed during the heat-melting.

Claims

1. A process of vitrifying a radioactive liquid waste by absorbing a radioactive liquid waste into a glass frit cartridge made of molded glass fibers and heat-melting said cartridge to vitrify said liquid waste, characterized in that a radioactive liquid waste containing ruthenium is absorbed together with a reducing agent in liquid form into said glass frit cartridge, thereby suppressing the formation of gaseous ruthenium during the heat melting.

2. The process according to claim 1, wherein a mixture of said liquid waste and said reducing agent in liquid form is absorbed into said glass frit cartridge.

3. The process according to claim 1, wherein said liquid waste is absorbed into said glass frit cartridge and said reducing agent in liquid form is then absorbed into said cartridge.

4. The process according to claim 1, wherein said reducing agent in liquid form is absorbed into said glass frit cartridge and said liquid waste is &

hen absorbed into said cartridge.

5. The process according to claim 1, wherein said glass frit cartridge is a cylindrically-shaped glass fiber aggregate prepared by rolling a sheet of glass fibers.

6. The process according to claim 1, wherein said glass frit cartridge is a cylindrically-shaped glass fiber aggregate prepared by sintering glass fibers in a mold.

7. The process according to claim 1, 2, 3, or 4, wherein said reducing agent in liquid form is selected from the group consisting of formic acid, formalin and aqueous solutions of sugar and corn starch.

8. A process of vitrifying a radioactive liquid waste by absorbing a radioactive liquid waste into a glass frit cartridge made of molded glass fibers and heat-melting said cartridge to vitrify said liquid waste, characterized in that a reducing agent in solid form is previously incorporated in said glass frit cartridge made of molded glass fibers, and a radioactive liquid waste containing ruthenium is then absorbed in to said glass frit cartridge containing said reducing agent, thereby suppressing the formation of gaseous ruthenium during the heat-melting.

9. The process according to claim 8, wherein said reducing agent in solid form is selected from the group consisting of sugar and corn starch.

10. The process according to claim 8, wherein said glass frit cartridge is a cylindrically-shaped glass fiber aggregate prepared by rolling a sheet of glass fibers.

11. The process according to claim 8, wherein said glass frit cartridge is a cylindrically-shaped glass fiber aggregate prepared by sintering glass fibers in a mold.