Process using melt accelerator for the conversion of solid waste substances into glass

• US 4,944,785 A
• Filed: 06/23/1989
• Issued: 07/31/1990
• Est. Priority Date: 12/13/1988
• Status: Expired due to Fees

• Current Assignee: Metallgesellschaft AG (GEA Group AG)
• Original Assignee: Metallgesellschaft AG (GEA Group AG), SORG GmbH & Company KG
• Inventors: Zschocher, Hartmut, Merlet, Heinz, Sorg, Helmut, Pieper, Helmut
• Primary Examiner(s): Lindsay, Robert L.
• Application Number:
  US07/370,593
• Time in Patent Office: 403 Days
• Field of Search: 65/18.2, 65/27, 65/134, 65/136, 422/168, 501/155
• US Class Current: 65/134.3
• CPC Class Codes: B09B 3/29 involving a melting or softening step
• CPC Class Codes: C03B 19/109 Glass-melting furnaces specially adapted for making beads
• CPC Class Codes: C03B 3/023 Preheating
• CPC Class Codes: C03B 5/005 of glass-forming waste materials disposal or transformation of solid waste in general B09B; treatment of radioactive waste G21F9/00
• CPC Class Codes: C03B 5/03 Tank furnaces
• CPC Class Codes: C03B 5/04 in tank furnaces C03B5/02 takes precedence
• CPC Class Codes: C03B 5/235 Heating the glass C03B5/02, C03B5/18, C03B5/225 take precedence
• CPC Class Codes: F01N 2550/00 Monitoring or diagnosing the deterioration of exhaust systems
• CPC Class Codes: Y02P 40/50 Glass production, e.g. reusing waste heat during processing or shaping

Abstract

Waste substance such as incineration ash is mixed with cullet and alkaline earth salt to form a mixed batch which is added to a glass melt heated solely by electrodes, producing an exhaust gas which is introduced into the batch thereby cooling the gas to produce condensation products. The alkaline earth salt reacts with alkali in the gas and the condensation products to produce a gall layer of alkali salts and alkaline earth salts which serve as a melt accelerator and are readily removed when accumulated. According to a further step the gas is purified by separating dust therefrom and introducing it into the batch as a slurry.

Claims

1. Process for converting solid, dehydrated waste substance into glass, comprising

mixing the waste substances with at least one additive to form a mixed batch,

generating a gall layer of alkali salt or alkaline earth salt on the surface of a glass melt heated solely by electrodes, and

introducing the mixed batch onto said glass melt surface so that a major portion is melted into the melt and a minor portion produces an exhaust gas emerging from the melt, said gall layer serving as a melt accelerator,

introducing the exhaust gas into the batch to be melted, thereby cooling said gas and producing condensation products in the batch, and

reintroducing said condensation products into the melt with the batch.

2. Process as in claim 1 wherein part of said gall layer is periodically removed to maintain a thickness between 2 and 5 cm.

3. Process as in claim 1 wherein said exhaust gas and the resulting condensation products contain alkali therein, said gall layer comprising one or more alkali salts from the group consisting of Na₂ SO₄, K₂ SO₄, Li₂ SO₄, and LiCl, said gall layer being generated during the melting process by adding one or more alkaline earth salts from the group consisting of CaSO₄, CaCl₂, MgSO₄, and Mgcl₂, said alkaline earth salts reacting with said alkali to produce said alkali salts.

4. Process as in claim 3 wherein said alkaline earth salts are added to the melt with the batch.

5. Process as in claim 3 wherein said alkaline earth salts are added to the melt separately from the batch.

6. Process as in claim 1 wherein said gall layer comprises one or more alkaline earth salts from the group consisting of CaSO₄ and MgSO₄.

7. Process as in claim 6 wherein said exhaust gas and the resulting condensation products contain little or no alkali.

8. Process as in claim 1 wherein said solid, dehydrated waste substance is incineration ash.

9. Process as in claim 1 further comprising purifying the exhaust gas emerging from the batch to be melted, said purifying comprising removing dust from said exhaust gas and reintroducing said dust into the batch to be melted.

10. Process as in claim 9 wherein said dust is slurried before being reintroduced into said batch.

11. Process as in claim 9 wherein said exhaust gas is cooled before purification.

12. Process as in claim 9 wherein said exhaust gas is cooled after purification.