Method of making an electrosurgical spatula blade

• US 4,958,539 A
• Filed: 06/02/1989
• Issued: 09/25/1990
• Est. Priority Date: 02/29/1988
• Status: Expired due to Fees

• Current Assignee: Everest Medical Corp. (Olympus Corporation)
• Original Assignee: Everest Medical Corp. (Olympus Corporation)
• Inventors: Solberg, Jeffrey J., Stasz, Peter, Grabinger, Scott R.
• Primary Examiner(s): Hall, Carl E.
• Assistant Examiner(s): Arbes, Carl J.
• Application Number:
  US07/360,856
• Time in Patent Office: 480 Days
• Field of Search: 65/61, 65/62, 65/60.4, 30/346.53, 30/346.54, 30/346.55, 30/350, 76/104.1, 76/101.1, 29/527.2
• US Class Current: 76/104.1
• CPC Class Codes: A61B 18/1402 Probes for open surgery
• CPC Class Codes: A61B 2018/00083 low, i.e. electrically insulating
• CPC Class Codes: A61B 2018/00107 Coatings on the energy applicator
• CPC Class Codes: A61B 2018/00119 with metal oxide nitride
• CPC Class Codes: A61B 2018/1412 Blade
• CPC Class Codes: A61B 2018/1422 Hook
• CPC Class Codes: Y10T 29/49982 Coating

Abstract

A surgical cutting blade for use in an electrosurgical scalpel includes a thin flat ceramic substrate having a rounded tip where the edge portion of the substrate on the opposed major surfaces thereof are beveled. A pattern of metallization is provided on the opposed major surfaces of the blade substrate with the metallization extending over the tapered portions. The substrate is then back-ground to form a blunt edge extending between the tapered surfaces at the edge of the substrate. The metallization pattern further includes traces extending from the conductors along the blunt working edge of the blade to the handle receiving portion thereof and provide a means whereby RF energy may be conducted to the metallized working edge of the blade.

Claims

1. A method of fabricating an electrosurgical blade comprising the steps of:

(a) forming a thin, flat substrate of a desired shape from a ceramic material;

(b) grinding a taper along a selected portion of the major surfaces of said substrate leading to the edge of said substrate;

(c) depositing a pattern of metallization on each side pattern extending over the tapered portion; and

(d) backgrinding the substrate to form a blunt edge surface face of metallization which extends between said tapered portions of said major surfaces.

2. The method as in claim 1 and further including the step of coating said blade with a high temperature insulating material exhibiting high electrical impedance.

3. The method as in claim 2 wherein said insulating material is selected from the group consisting of aluminum oxide, boron nitride, silicon dioxide, zirconium oxide, titanium nitride and silicon nitride.