Reinforced bone cement, method of production thereof and reinforcing fiber bundles therefor

• US 4,963,151 A
• Filed: 12/28/1988
• Issued: 10/16/1990
• Est. Priority Date: 12/28/1988
• Status: Expired due to Fees

• Current Assignee: Trustees Of The University Of Pennsylvania (University of Pennsylvania)
• Original Assignee: Trustees Of The University Of Pennsylvania (University of Pennsylvania)
• Inventors: Cuckler, John M., Topoleski, L. D. Timmie, Ducheyne, Paul
• Primary Examiner(s): Cannon, Alan W.
• Application Number:
  US07/291,157
• Time in Patent Office: 657 Days
• Field of Search: 623/16, 623/66, 428/288, 428/293, 428/294, 428/375, 428/378
• US Class Current: 623/23.62
• CPC Class Codes: A61B 17/8802 Equipment for handling bone cement or other fluid fillers
• CPC Class Codes: A61F 2/30965 Reinforcing the prosthesis by embedding particles or fibres during moulding or dipping
• CPC Class Codes: A61F 2/32 for the hip
• CPC Class Codes: A61F 2002/30224 cylindrical
• CPC Class Codes: A61F 2002/30261 parallelepipedal
• CPC Class Codes: A61F 2002/4631 the prosthesis being specially adapted for being cemented
• CPC Class Codes: A61F 2230/0069 cylindrical
• CPC Class Codes: A61F 2230/0082 parallelepipedal
• CPC Class Codes: A61L 24/0089 containing inorganic fillers not covered by groups A61L24/0078 or A61L24/0084
• CPC Class Codes: A61L 2430/02 for reconstruction of bones; weight-bearing implants
• CPC Class Codes: C08L 33/06 of esters containing only carbon, hydrogen and oxygen, which oxygen atoms are present only as part of the carboxyl radical
• CPC Class Codes: Y10T 428/24994 Fiber embedded in or on the surface of a polymeric matrix
• CPC Class Codes: Y10T 428/2933 Coated or with bond, impregnation or core
• CPC Class Codes: Y10T 428/2938 Coating on discrete and individual rods, strands or filaments

Abstract

The distribution of short, fine, reinforcing fibers homogeneously throughout surgical bone cement is accomplished by adding the fibers in the form of bundles of several hundred fibers with the fibers bonded to each other with an adhesive binder that is soluble in the liquid monomer component of the bone cement. The fiber bundles are either premixed with the powdery polymer bead component of the bone cement followed by addition of the liquid monomer or the polymer and liquid are premixed into a viscous liquid and the fiber bundles are gradually added with stirring to the viscous liquid. In either case, as the adhesive binder dissolves in the liquid monomer the individual fibers are freed and continued stirring mixes the fibers homogeneously throughout the cement mass.

Claims

1. A fiber reinforcing material for incorporation into a two component bone cement including particulate polymer component and a polymerizable liquid monomer component and which reinforcing material can be readily incorporated by manual mixing into the bone cement by a surgeon during a surgical operation, said reinforcing material comprising a bundle of reinforcing fibers held together by an adhesive material which is soluble in the liquid monomer component of the two component bone cement, the fibers of said bundle having a diameter in the range of from about 5 to about 100 microns and a length in the range of from about 0.5 to about 10 millimeters, and the length-to-diameter ratio of said bundle being in the range of from about 10:

1 to about 1;

10.

2. The fiber reinforcing material of claim 1 wherein the reinforcing fibers comprise metallic fibers.

3. The fiber reinforcing material of claim 2 wherein the metal fibers comprise titanium fibers.

4. The fiber reinforcing material of claim 1 wherein the adhesive material comprises an acrylic adhesive.

5. The fiber reinforcing material of claim 4 wherein the acrylic adhesive comprises an acrylate or methacrylate adhesive.

6. The fiber reinforcing material of claim 1 wherein the reinforcing fibers have a diameter of from about 10 to about 80 microns and a length of from about 1 to about 8 millimeters.

7. The fiber reinforcing material of claim 1 which comprises from about 50 to about 500 fibers per bundle.

8. The fiber reinforcing material of claim 1 which comprises from about 100 to about 300 fibers per bundle.

9. The fiber reinforcing material of claim 1 wherein the length-to-diameter ratio is from about 3:

1 to about 1;

3.

10. A bone cement treatment kit for bone repair or other treatment of a bone defect, said kit comprising (1) finely divided acrylic polymer and (2) polymerizable liquid acrylic monomer for preparation of bone cement useful in bone repair or other bone treatment, and (3) a reinforcing material comprising bundles of reinforcing fibers wherein the fibers of said bundles are bonded to each other by an adhesive material which is soluble in said liquid monomer (2), whereby when said components (1), (2) and (3) are combined the adhesive material dissolves in said liquid monomer and allows said fibers to be homogeneously distributed throughout said bone cement by manual mixing.

11. The kit of claim 10 wherein said fibers are comprised of metal and have a diameter in the range of from about 10 to about 100 microns and a length in the range of from about 0.5 to about 10 millimeters.

12. The kit of claim 11 wherein the metal reinforcing fibers comprise titanium fibers.

13. The kit of claim 12 wherein said bundles of reinforcing fibers have a length-to-diameter ratio of from about 1 to about 1:

10.

14. The kit of claim 10 wherein said bundles of reinforcing fibers have a length-to-diameter ratio of from about 1 to about 1:

10.

15. The kit of claim 10 wherein said prepolymer (1) comprises a methacrylate or acrylate polymer, said liquid monomer (2) comprises a polymerizable acrylate, methacrylate or methylmethacrylate monomer, and the adhesive material (3) comprises an acrylate or methacrylate based adhesive.

16. The kit of claim 10 wherein each of components (1), (2) and (3) are separately packaged.

17. The kit of claim 10 wherein components (1) and (3) are premixed and component (2) is packaged separately.

18. The kit of claim 16 wherein said package containing said prepolymer (1) further comprises a polymerization initiator.

19. A method for forming a fiber reinforced bone cement for bone repair or other treatment of bone, said method comprising first mixing a powdery polymer component of said bone cement and a plurality of reinforcing fiber bundles, each of said bundles comprising a plurality of short reinforcing fibers bonded together by an adhesive material, and thereafter mixing said fiber-polymer mixture with a polymerizable liquid monomer component of said bone cement which can dissolve said adhesive material and thereby promote uniform and homogeneous distribution of said reinforcing fibers throughout said bone cement.

20. The method of claim 19 which further comprises chilling the polymerizable liquid monomer prior to mixing the liquid monomer with said fiber-polymer mixture.

21. The method of claim 19 wherein the amount of fibers mixed with said powdery polymer comprises up to about 5% by volume, based on the total volume of the bone cement.

22. The method of claim 19 wherein said fiber bundles comprise from about 50 to about 500 reinforcing fibers, per bundle, said reinforcing fibers having a diameter of from about 5 to about 100 microns and a length of from about 0.5 to about 10 millimeters, said bundles having a length-to-diameter ratio of from about 10:

1 to about 1;

10.

23. The method of claim 22 wherein said reinforcing fibers comprise titanium fibers.

24. A method of forming a fiber reinforced bone cement for bone repair or other treatment of bone, said method comprising premixing a powdery or granular polymer component of said bone cement and a liquid polymerizable monomer component of said bone cement which is a solvent for said polymer component to form a viscous liquid mixture, gradually adding to said liquid mixture a plurality of bundles of short reinforcing fibers, the fibers of said bundles being glued together by an adhesive which is soluble in said liquid monomer and stirring the resulting mixture to distribute the fiber bundles throughout the mixture, while allowing the adhesive component to dissolve in said liquid monomer whereby the individual fibers of said fiber bundles are released into and randomly distributed throughout the bone cement.

25. The method of claim 24 wherein the fiber bundles are added in an amount to provide from about 1 to about 10% by volume of the bone cement.

26. The method of claim 24 wherein the fiber bundles are added in an amount to provide from about 3 to about 10% by volume of the bone cement.

27. The method of claim 24 which further comprises chilling the liquid monomer prior to premixing with the powdery polymer.

28. The method of claim 24 wherein said fiber bundles comprise from about 50 to about 500 reinforcing fibers, per bundle, said reinforcing fibers having a diameter of from about 5 to about 100 microns and a length of from about 0.5 to about 10 millimeters, said bundles having a length-to-diameter ratio of from about 10:

1 to about 1;

10.

29. The method of claim 28 wherein said reinforcing fibers comprise titanium fibers.