Process for the manufacture of a substantially wrinkle-free non-planar laminate and pre-laminate

• US 4,973,364 A
• Filed: 01/23/1989
• Issued: 11/27/1990
• Est. Priority Date: 01/27/1988
• Status: Expired due to Term

• Current Assignee: Hoechst Diafoil Company
• Original Assignee: Hoechst Celanese Corporation (Sanofi )
• Inventors: Swofford, H. Wayne, Inman, Samuel M., Lazar, Jack M., Gust, Stephen J., Farrar, Grover L.
• Primary Examiner(s): Weston, Caleb
• Application Number:
  US07/299,583
• Time in Patent Office: 673 Days
• Field of Search: 156/84, 156/85, 156/212, 156/213, 156/229, 156/245, 156/285, 156/267, 156/289, 264/230, 264/231, 264/259, 264/342 R
• US Class Current: 156/84
• CPC Class Codes: B29C 61/02 Thermal shrinking
• CPC Class Codes: B32B 17/10009 characterized by the number, the constitution or treatment of glass sheets
• CPC Class Codes: B32B 17/10853 the membrane being bag-shaped
• CPC Class Codes: B32B 17/10935 as a preformed layer, e.g. formed by extrusion
• CPC Class Codes: B32B 27/08 of synthetic resin
• CPC Class Codes: B60J 1/02 arranged at the vehicle front , e.g. structure of the glazing, mounting of the glazing on windscreen mounted antenna wire H01Q1/1271
• CPC Class Codes: Y10T 156/1028 by bending, drawing or stretch forming sheet to assume shape of configured lamina while in contact therewith
• CPC Class Codes: Y10T 156/108 Flash, trim or excess removal

Abstract

A substantially wrinkle-free, high modulus, thermoplastic film having at least one compound curve is disclosed. The substantially wrinkle-free film may form a part of a laminate which itself has utility in automotive glazing applications.

An improved lamination process is also disclosed for the production of non-planar laminates from planar sheets of heat-shrinkable films through the use of a negative image mold of the non-planar article to be laminated. Heat-shrinkable films which may be used in the practice of the invention include polyester films, polyolefin films, polyamide films, polyurethane films, polycarbonate films, polyvinylchloride films, and polystyrenic films.

The method is applicable to a wide range of non-planar articles and is particularly suitable to articles having at least one compound curve forming at least part of its surface. The improved lamination process of the present invention has specific utility in the manufacture of automotive glazing products such as windshields and rear windows.

Claims

1. A process for the manufacture of a substantially wrinkle-free, non-planar pre-laminate comprising:

(i) placing a heat-shrinkable, thermoplastic film over a negative-image mold of a non-planar article;

(ii) conforming said film to the shape of said mold by heating said film to a temperature above its glass transition temperature while maintaining said film under dimensional restraint, thereby forming conformed film;

(iii) placing an adhesive layer over said conformed film;

(iv) conforming said adhesive layer to the shape of said conformed film by heating said adhesive layer under pressure, thereby forming a two layer pre-laminate.

2. The process of claim 1 wherein said heat-shrinkable film is selected from the group consisting of polyester films, polyolefin films, polyamide films, polyurethane films, polycarbonate films, polyvinyl chloride films, and polystyrenic films.

3. The process of claim 2 wherein said heat-shrinkable film is a polyester film.

4. The process of claim 1 wherein said non-planar article has at least one compound curve forming at least part of its surface.

5. The process of claim 1 wherein said film is heated to a maximum conforming temperature of about 250 °

C.

6. The process of claim 1 wherein a mold release coating is interposed between said film and said mold prior to heating said film.

7. The process of claim 6 wherein said mold release coating is affixed to said film.

8. The process of claim 7 wherein said mold release coating additionally improves the abrasion resistance of said film.

9. The process of claim 1 wherein said conformed film is cooled to below its glass transition temperature prior to placing an adhesive layer over said conformed film.

10. The process of claim 1 wherein said adhesive layer comprises a layer of polyvinylbutyral having a thickness effective to bond the conformed pre-laminate to glass.

11. A process for the manufacture of a non-planar laminate comprising:

(i) placing a heat-shrinkable, thermoplastic film over a negative-image mold of a non-planar article;

(ii) conforming said film to the shape of said mold by heating said film to a temperature above its glass transition temperature while maintaining said film under dimensional restraint, thereby forming conformed film;

(iii) aligning the exposed surface of said conformed film into image-wise relationship with the concave surface of said non-planar article;

(iv) placing an adhesive layer between said conformed film and said non-planar article, thereby forming a pre-laminate;

(v) subjecting said pre-laminate to heat and pressure sufficient to laminate said conformed film, said adhesive layer, and said non-planar article together.

12. The process of claim 11 wherein said heat-shrinkable film is selected from the group consisting of polyester films, polyolefin films, polyvinyl chloride films, polycarbonate films, polyamide films, polyurethane films and polystyrenic films.

13. The process of claim 12 wherein said heat-shrinkable film is a polyester film.

14. The process of claim 11 wherein any excess material is trimmed from said conformed film prior to placing said film into image-wise alignment with said non-planar article.

15. The process of claim 11 wherein said non-planar article is transparent.

16. The process of claim 15 wherein said transparent non-planar article has at least one compound curve forming at least part of its surface.

17. The process of claim 16 wherein said transparent non-planar article is selected from the group consisting of glass, polycarbonate, and polyacrylate.

18. The process of claim 15 wherein said adhesive layer comprises a layer of polyvinylbutyral having a thickness effective to bond said conformed film to said transparent non-planar article.

19. The process of claim 11 wherein said film is heated to a maximum conforming temperature of about 250 °

C.

20. The process of claim 11 wherein a mold release coating is interposed between said film and said mold prior to heating said film.

21. The process of claim 20 wherein said mold release coating is affixed to said film.

22. The process of claim 21 wherein said mold release coating additionally improves the abrasion resistance of said film.

23. The process of claim 11 wherein said conformed film is cooled to a temperature below its glass transition temperature prior to contacting said film with said adhesive layer.

24. A process for the manufacture of a substantially wrinkle-free, non-planar pre-laminate comprising:

(i) forming a pre-laminate of a heat shrinkable, high modulus thermoplastic film and an adhesive;

(ii) placing said pre-laminate over a negative-image mold of a non-planar article such that said thermoplastic film contacts said negative-image mold; and

(iii) conforming, by shrinking, said pre-laminate to the shape of said mold by heating said pre-laminate to a temperature above its glass transition temperature while maintaining said pre-laminate under dimensional restraint, thereby forming conformed pre-laminate.

25. The process of claim 24, wherein said heat-shrinkable thermoplastic film is selected from the group consisting of polyester films, polyolefin films, polyamide films, polyurethane films, polycarbonate films, polyvinyl chloride films, and polystyrenic films.

26. The process of claim 24, wherein said non-planar article has at least one compound curve forming at least part of its surface.

27. The process of claim 24, wherein said adhesive layer comprises a layer of polyvinylbutyral having a thickness effective to bond the conformed pre-laminate to glass.