Process for producing a planar glass substrate coated with a dielectric layer system

• US 4,975,103 A
• Filed: 09/07/1989
• Issued: 12/04/1990
• Est. Priority Date: 09/07/1988
• Status: Expired due to Term

• Current Assignee: Schott AG (Carl-Zeiss-Stiftung)
• Original Assignee: Schott Glaswerke
• Inventors: Ruetze, Uwe, Paquet, Volker, Kersten, Ralf T., Etzkorn, Heinz-Werner, Ackermann, Ulrich
• Primary Examiner(s): Lacey, David L.
• Assistant Examiner(s): BURNS, TODD
• Application Number:
  US07/403,967
• Time in Patent Office: 453 Days
• Field of Search: 427/165, 427/166, 427/167, 427/366, 65/18.2, 65/108, 65/110, 65/3.12, 65/60.2, 65/60.53, 65/60.8, 65/60.1, 65/29, 65/105, 65/112
• US Class Current: 65/386
• CPC Class Codes: C03B 23/037 by drawing
• CPC Class Codes: C03C 17/34 with at least two coatings having different compositions C03C17/44 takes precedence
• CPC Class Codes: G02B 1/10 Optical coatings produced by application to, or surface treatment of, optical elements G02B1/08 takes precedence

Abstract

A process is provided for producing a planar glass substrate coated with a dielectric layer system in which the individual layers are formed by a chemical vapor deposition coating process. After the layers have been applied, the glass substrate is either drawn, compressed, or its surface enlarged until the coating layers are reduced in thickness. A planar glass substrate having a multiplicity of extremely thin dielectric layers can be fabricated according to this process.

Claims

1. In a process for producing a planar glass substrate having one or more dielectric layers of optical quality, the improvement comprising heating a glass tube having one or more dielectric layers on one or both sides of said glass tube applied by chemical vapor deposition or modified chemical vapor deposition to a sufficient temperature so that the glass tube can be blown, flowing the glass tube to expand it and reduce the thickness of the dielectric layers, measuring the optical properties of the blown glass tube and continuing to expand the tube until desired optical properties are obtained, cutting the blown glass tube and heating it to its softening point, and flattening it to produce a planar glass substrate.

2. The process according to claim 1, wherein the glass tube is expanded until the dielectric layers are from about 1/2 to 1/20 of their original thickness.

3. The process according to claim 1, wherein the glass tube is expanded until the thinnest individual dielectric layer is from about 0.05 to 1 micrometers thick.

4. A process according to claim 1 wherein, said glass tube has 100-1000 dielectric layers of alternating composition, each of said dielectric layers are 1-10 μ

m in thickness, before said glass tube is expanded.

5. A process according to claim 4, wherein the glass tube is expanded until the dielectric layers are from about 1/2 to 1/20 of their original thickness.

6. A process according to claim 5, said dielectric layers being:

(a) alternating layers of SiO₂ doped with 0.5 mol % F., and SiO₂ doped with 10-20 mol % Ge and 0.5 mol % F., or

(b) alternating layers of pure SiO₂ and SiO₂ doped with about 2 mol % F., or

(c) alternating layers of borosilicate glasses having different refractive indices.