Method of pretreating metallic works

• US 4,975,147 A
• Filed: 02/23/1990
• Issued: 12/04/1990
• Est. Priority Date: 12/22/1989
• Status: Expired due to Term

• Current Assignee: Air Water Incorporated
• Original Assignee: Daidousanso Co., Ltd.
• Inventors: Kitano, Kenzo, Tahara, Masaaki, Tomoda, Takakazu
• Primary Examiner(s): Powell, William A.
• Application Number:
  US07/483,709
• Time in Patent Office: 284 Days
• Field of Search: 156/646, 156/655, 156/656, 156/665, 156/664, 156/668, 134/31, 134/38, 134/39, 134/40
• US Class Current: 216/77
• CPC Class Codes: C23C 8/02 Pretreatment of the material to be coated C23C8/04 takes precedence
• CPC Class Codes: C23C 8/34 more than one element being applied in more than one step

Abstract

The primary object of the invention is to clean and activate the surface of metallic works prior to such thermal treatment as nitriding, thermal spraying or dip plating by removing oxidized and other passive layers and foreign matters from the metallic work surface.

The method of pretreating metallic works comprises heating a metallic work in a furnace and introducing a fluorine- or fluoride-containing gas into the furnace in that state to thereby cause destruction and elimination of the foreign matters adhering to the metallic work surface and of the oxidized layer occurring on the metallic work surface and simultaneous formation of a fluorinated layer. Just prior to the main thermal treatment, for example nitriding, the fluorinated layer is decomposed and eliminated by introducing an appropriate gas, for example H₂, into the furnace. In this way, the metallic work reveals its cleaned and activated surface.

Claims

1. A method of pretreating metallic works which comprises holding a metallic work in a heated condition in a fluorine- or fluoride-containing gas atmosphere and then removing the resulting fluorinated layer to thereby clean and activate the surface of said metallic work.

2. A method of pretreating metallic works as claimed in claim 1, wherein said metallic work is made essentially of steel, aluminum, titanium or nickel.

3. A method of pretreating metallic works as claimed in claim 1 or 2, wherein the fluorine- or fluoride-containing gas is a dilution, in an inert gas, of at least one fluorine source component selected from the group consisting of NF₃, BF₃, CF₄, HF, SF₆ and F₂.