Calcification mitigation of bioprosthetic implants

• US 5,002,566 A
• Filed: 04/18/1989
• Issued: 03/26/1991
• Est. Priority Date: 02/17/1989
• Status: Expired due to Term

• Current Assignee: Edwards Lifesciences Corporation
• Original Assignee: Baxter International Inc.
• Inventors: Carpentier, Alain, Nashef, Aws, Carpentier, Sophie
• Primary Examiner(s): NOT, DEFINED
• Application Number:
  US07/339,787
• Time in Patent Office: 707 Days
• Field of Search: 623/1-3, 623/11, 623/12, 623/66, 427/2, 128/DIG. 8, 8/94.28, 8/94.19
• US Class Current: 600/36
• CPC Class Codes: A61L 2400/02 Treatment of implants to prevent calcification or mineralisation in vivo
• CPC Class Codes: A61L 27/3687 characterised by the use of chemical agents in the treatment, e.g. specific enzymes, detergents, capping agents, crosslinkers, anticalcification agents
• CPC Class Codes: Y10S 623/918 Heart

Abstract

Calcification resistant bioprosthetic implants are made from tanned biological materials, such as porcine heart valves, bovine pericardium, human dura mater or the like, which has been impregnated with a calcification-mitigating effective amount of a ferric and/or stannic salt. The impregnated biological materials and processes are particularly advantageous for the preparation of bioprosthetic heart valves. These implants have been found to be highly resistant to calcification in vivo.

Claims

1. A process for making a calcification-resistant biological material comprising applying to said material a solution comprising an ion selected from the group consisting of ferric ions, stannic ions, or a combination of ferric and stannic ions to impregnate said material with a calcification-mitigating effective amount of said ferric ions, stannic ions, or a combination of ferric and stannic ions, wherein the biological material is tanned prior to said step of applying said solution.

2. The process of claim 1 wherein the biological material is tanned subsequent to said step of applying said solution of ferric and/or stannic salt.

3. The process of claim 1 wherein the biological material is impregnated with ferric ion.

4. The process of claim 1 wherein the biological material is impregnated with stannic ion.

5. The process of claim 1 wherein the biological material is impregnated with a mixture of ferric and stannic ions.

6. The process of claim 1, which further comprises forming the bioprosthesis into a heart valve.

7. The process of claim 1 which further comprises sterilizing the bioprosthesis.

8. The process of claim 1 wherein the biological material is impregnated with the ferric or stannic ions by treatment with a solution of a soluble, substantially non-toxic ferric or stannic salt.

9. The process of claim 8 wherein the salt is a nitrate, sulfate, borate, carbonate, halide, citrate or acetate of ferric or stannic.

10. The process of claim 9 wherein the salt is dissolved in an aqueous solution of water-miscible alcohol, glycol, triol, or aldehyde.

11. The process of claim 9 wherein the salt is dissolved in an aqueous solution of ethanol, formaldehyde, glutaraldehyde, or glycerol.

12. The process of claim 11 wherein the pH of the solution ranges from about 2 to about 7.

13. The process of claim 11 wherein the pH of the solution ranges from about 2 to about 3.

14. The process of claim 11 wherein the solution contains from about 0.01% to about 2.5% by weight of the ferric or stannic salt.

15. The process of claim 14, wherein the solution contains from about 0.05% to about 1.5% of the ferric or stannic salt.

16. The process of claim 9 wherein the solution contains up to about 30% ethanol, up to about 5% formaldehyde, up to about 1% glutaraldehyde, or up to about 30% glycerol, or mixtures thereof.

17. The process of claim 8 wherein the salt is ferric nitrate, stannic nitrate, ferric sulfate, stannic sulfate, ferric chloride, stannic chloride, ferric citrate, stannic citrate, ferric acetate or stannic acetate.

18. A process for making a calcification-resistant biological material comprising applying to said material a solution comprising an ion selected from the group consisting of ferric ions, stannic ions, or a combination of ferric and stannic ions to impregnate said material with a calcification-mitigating effective amount of said ferric ions, stannic ions, or a combination of ferric and stannic ions, and wherein the solution contains up to about 30% ethanol, up to about 5% formaldehyde, up to about 1% glutaraldehyde, or up to about 30% glycerol,or mixtures thereof.