Matrix for release of active ingredients

• US 5,008,115 A
• Filed: 03/02/1990
• Issued: 04/16/1991
• Est. Priority Date: 04/22/1988
• Status: Expired due to Fees

• Current Assignee: Dow, Inc.
• Original Assignee: Dow, Inc.
• Inventors: Lee, Chi-Long, Gornowicz, Gerald A.
• Primary Examiner(s): Page, Thurman
• Assistant Examiner(s): Webman, Edward J.
• Application Number:
  US07/487,478
• Time in Patent Office: 410 Days
• Field of Search: 424/486, 424/501, 424/411, 424/76.8, 424/84, 514/788, 523/102, 523/122
• US Class Current: 424/486
• CPC Class Codes: A01N 25/10 Macromolecular compounds
• CPC Class Codes: A01N 25/18 Vapour or smoke emitting compositions with delayed or sustained release
• CPC Class Codes: A61L 9/042 with the help of a macromolecular compound as a carrier or diluent A61L9/048 takes precedence
• CPC Class Codes: C08G 18/61 Polysiloxanes
• CPC Class Codes: Y10S 424/10 Insect repellent

Abstract

A matrix for delivery of active substances such as fragrances and pheromones into the atmosphere is provided which matrix is active substance permeable (including to hydrophilic substances) and is formed of a copolymer which can be softened sufficiently at temperature between 45° C. and 160° C. to incorporate the substances therein without damage caused by heat or chemical reactions, the matrix being formed of a substantially linear block copolymer which is a reaction product of a polydiorganosiloxane which forms soft segments in said reaction product and a diisocyanate which forms hard segments, said copolymer having a glass transition temperature between 45° C. and 160° C. said soft segments comprising from 70 to 99 percent by weight, based on the weight of said copolymer, the average molecular weight of the copolymer being between 15,000 and 500,000.

Claims

1. An improved method for forming active substance delivery reservoir comprising

(A) selecting a polymeric material consisting substantially of a linear thermoplastic block copolymer comprising from 1 to 30 weight percent of hard segments consisting essentially of polyurethane units derived from an organic diisocyanate and an alkylene diol containing from 2 to about 10 carbon atoms, and from 70 to 99 weight percent to soft segments comprising from 15 to 99 percent by weight, based on the weight of said copolymer, of polydiorganosiloxane units, based on the weight of said copolymer, said copolymer having a glass transition temperature between 40°

and 160°

C., (B) heating said copolymer to a temperature sufficient to soften it, (C) admixing into said softened copolymer an active substance chosen from the group consisting of synthetic perfumes, fragrances, insect repellants, air deodorizers, bactericides, herbicides, plant growth regulators, sex pheromones, and air fresheners, and (D) cooling the resultant composition to harden and form a matrix.

2. A method according to claim 1 where said active substance is of an hydrophilic character, and the hard segment of the copolymer constitutes from 1 to 30 percent by weight of the copolymer, the polydiorganosiloxane units which have an average molecular weight between about 1200 and 30,000.

3. A method according to claim 1 wherein said composition is formed into a layer having a thickness of from 0.01 to 1 cm.

4. A method according to claim 2 where the organic diisocyanate is p-tolylene diisocyanate, 4,4'"'"'diphenylmethanediisocyanate or 4,4'"'"'dicyclohexylmethanediisocyanate, the alkylene diol is 1,4-butanediol, the polydiorganosiloxane units contain from 20 to 40 diorganosiloxane repeating units.

5. A method according to claim 1 wherein said soft segments comprise from 0 to 65 percent by weight, based on the weight of said copolymer, of a hydrophilic portion consisting essentially of at least one polyalkylene oxide unit.

6. A method according to claim 3 wherein the organic diisocyanate is p-tolylene diisocyanate, 4,4'"'"'diphenylmethanediisocyanate or 4,4'"'"'dicyclohexylmethanediisocyanate, and the alkylene diol is 1,4-butanediol, the polydiorganosiloxane units contain from 20 to 40 diorganosiloxane repeating units, the molar ratio of diisocyanate units to alkylene diol units and polydiorganosiloxane units is 1:

1.

7. Method according to claim 5 wherein said polyalkylene oxide is polyethylene oxide.