Process for preparing an asymmetrical macroporous membrane polymer

• US 5,009,824 A
• Filed: 10/23/1989
• Issued: 04/23/1991
• Est. Priority Date: 12/17/1981
• Status: Expired due to Term

• Current Assignee: Hoechst Aktiengesellschaft (Sanofi )
• Original Assignee: Hoechst Aktiengesellschaft (Sanofi )
• Inventors: Wildhardt, Juergen, Walch, Axel, Beissel, Dieter
• Primary Examiner(s): Lorin, Hubert C.
• Application Number:
  US07/425,446
• Time in Patent Office: 547 Days
• Field of Search: 264/41, 264/45.1, 264/48, 264/232, 264/340, 210/500.28, 210/500.33, 210/500.41, 210/500.42, 427/245
• US Class Current: 264/45.1
• CPC Class Codes: B01D 2323/12 Specific ratios of components used
• CPC Class Codes: B01D 2325/022 Asymmetric membranes
• CPC Class Codes: B01D 2325/34 Molecular weight or degree of polymerisation
• CPC Class Codes: B01D 2325/36 Hydrophilic membranes
• CPC Class Codes: B01D 69/02 characterised by their properties
• CPC Class Codes: B01D 71/441 Polyvinylpyrrolidone
• CPC Class Codes: B01D 71/56 Polyamides, e.g. polyester-amides
• CPC Class Codes: B01D 71/68 Polysulfones; Polyethersulfones
• CPC Class Codes: C08L 2666/14 Macromolecular compounds according to C08L59/00 - C08L87/00; Derivatives thereof
• CPC Class Codes: C08L 39/06 Homopolymers or copolymers of N-vinyl-pyrrolidones

Abstract

A process for preparing an asymmetrical macroporous membrane from a polymer solution comprised as the dissolved portion fraction a polymeric mixture comprised of about 5-70% by weight of polyvinylpyrrolidone having a molecular weight of ≧100,000 Dalton and about 95-30% by weight of a polymer selected from the group consisting of polysulfone, a polyether sulfone, and an aromatic or araliphatic polyamide, said weight being relative to the total weight of the dissolved polymeric fraction, by action of a coagulating liquid, wherein the coagulation is effected under conditions such that skin formation, asymmetrical port formation and retention of the polyvinylpyrrolidone are achieved, recovering the asymmetrical macroporous membrane comprising the polymeric mixture.

Claims

1. A process for preparing an asymmetrical macroporous membrane, comprising the steps of:

(A) forming a macroporous asymmetrical membrane from a polymer solution by action of a coagulating liquid, said polymer solution comprising as the dissolved fraction a polymeric mixture comprised of about 5-70% by weight of polyvinylpyrrolidone having a molecular weight of ≧

100,000 Dalton and about 95-30% by weight of a polymer selected from the group consisting of a polysulfone, a polyether sulfone, and an aromatic or araliphatic polyamide, said weight being relative to the total weight of the dissolved polymeric fraction, wherein coagulation is effected under conditions such that skin formation, asymmetrical pore formation and retention of said polyvinylpyrrolidone are achieved and

(B) recovering the resultant asymmetrical macroporous membrane comprising said polymeric mixture.

2. A process as claimed in claim 1, wherein the polymer solution comprises in a dissolved state from about 5-70% by weight of polyvinylpyrrolidone and from about 95-30% by weight of a polysulfone, each relative to the total weight of the dissolved polymeric fraction.

3. A process as claimed in claim 1, wherein the polymer solution comprises in a dissolved state from about 5-70% by weight of polyvinylpyrrolidone and from about 95-30% by weight of a polyether sulfone, each relative to the total weight of the dissolved polymeric fraction.

4. A process as claimed in claim 1, wherein the polymer solution comprises in a dissolved state from about 5-70% by weight of polyvinylpyrrolidone and from about 95-30% by weight of an aromatic or araliphatic polyamide, each relative to the total weight of the dissolved polymeric fraction.

5. A process as claimed in claim 1, wherein the polymer solution further comprises a chemical compound capable of crosslinking the polymers, in an amount of from about 0.1-15% by weight, relative to the total weight of the dissolved polymeric fraction.

6. A process as claimed in claim 1, further comprising the step of treating the coagulated membrane with a chemical compound capable of crosslinking the polymers.

7. A process as claimed in claim 1, further comprising the step of crosslinking the polyvinylpyrrolidone by chemico-physical catalysis before or after the coagulation of the membrane.

8. A process as claimed in claim 1, further comprising the step of generating or bonding a reactive or permselective layer in or on the membrane.

9. A process as claimed in claim 1, wherein the solvent of said polymer solution is a polar organic solvent which is miscible with water.

10. A process as claimed in claim 9, wherein said solvent is selected from the group consisting of N-methyl-pyrrolidone dimethyl sulfoxide, dimethylformamide and dimethylacetamide.

11. A process as claimed in claim 1, wherein said coagulating liquid is water.

12. A process as claimed in claim 1, wherein said recovered resultant membrane has a water absorbency of at least 11% by weight of water, relative to its total weight, at 100% relative humidity and 25°

C.