• US 5,011,638 A
• Filed: 12/09/1988
• Issued: 04/30/1991
• Est. Priority Date: 06/17/1988
• Status: Expired due to Fees

• Current Assignee: Masco VT Incorporated
• Original Assignee: Vapor Technologies, Inc. (Masco Corporation)
• Inventors: Pinkhasov, Eduard
• Primary Examiner(s): Lowe, James
• Assistant Examiner(s): Fiorilla, Christopher A.
• Application Number:
  US07/283,174
• Time in Patent Office: 872 Days
• Field of Search: 264/44, 264/59, 264/81, 428/613, 204/192.38, 427/37, 164/46
• US Class Current: 264/414
• CPC Class Codes: B22F 2998/00 Supplementary information concerning processes or compositions relating to powder metallurgy
• CPC Class Codes: B22F 3/1121 by using decomposable, meltable or sublimatable fillers
• CPC Class Codes: C23C 14/0005 Separation of the coating from the substrate
• CPC Class Codes: C23C 14/32 by explosion; by evaporation and subsequent ionisation of the vapours , e.g. ion-platingC23C14/34 - C23C14/48 take precedence
• CPC Class Codes: C25B 11/031 Porous electrodes
• CPC Class Codes: H01M 4/80 Porous plates, e.g. sintered carriers
• CPC Class Codes: H01M 4/808 Foamed, spongy materials
• CPC Class Codes: H01M 4/8621 containing only metallic or ceramic material, e.g. made by sintering or sputtering
• CPC Class Codes: H01M 4/8885 Sintering or firing
• CPC Class Codes: H01M 4/9016 Oxides, hydroxides or oxygenated metallic salts
• CPC Class Codes: H01M 4/9041 Metals or alloys H01M4/92 takes precedence
• CPC Class Codes: Y02E 60/10 Energy storage using batteries
• CPC Class Codes: Y02E 60/50 Fuel cells

Abstract

The formation of an openwork structure e.g., of metal, utilizing low-temperature arc vapor deposition on a foam which is destroyed by pyrolysis is enhanced by applying a portion of the metal in a metal spray of powders in a binder which is also pyrolytically destroyed. The product has essentially the same properties as one made exclusively by the low-temperature arc vapor deposition method.

Claims

1. A method of fabricating an open-pore structure, comprising:

(a) depositing by arc vapor deposition on and in an openwork synthetic-resin pyrolyzable support a coating of at least one material selected from the group which consists of metals, semiconductors and ceramics by juxtaposing said support with a pair of electrodes at least one of which is composed of at least one element of said material, advancing said electrodes into contact to strike an electric arc between said electrodes and evaporate said element from said one of said electrodes and effect deposition of said material on said support, and evacuating a space in which said support is juxtaposed with such electrodes prior to or during deposition of said coating, whereby a fraction of a total amount of said material adapted to ultimately form said open-pore structure is deposited in the form of said coating;

(b) spraying onto at least one of said support and said coating in at least one spray-deposition operation a quantity of said material sufficient to make up the remainder of said total amount;

(c) pyrolyzing said support after at least one of step (a) and step (b) to form an openwork skeleton consisting essentially of said material; and

(d) sintering said skeleton into a coherent body constituting said open-pore structure.

2. The method defined in claim 1 wherein said spray-deposition operation includes spraying said material in admixture with a pyrolyzable binder and step (c) follows step (b).

3. The method defined in claim 2 wherein said spray-deposition operation of step (b) precedes step (a) and the arc vapor deposition of step (a) is effected upon a layer of said material applied in said spray-deposition operation directly upon said support.

4. The method defined in claim 2 wherein said spray-deposition operation of step (b) follows step (a).

5. The method defined in claim 1 wherein said spray-deposition operation of step (b) precedes step (a) and the arc vapor deposition of step (a) is effected upon a layer of said material applied in said spray-deposition operation directly upon said support.

6. The method defined in claim 1 wherein said spray-deposition operation of step (b) follows step (a).

7. The method defined in claim 6 wherein a further arc vapor deposition deposits an additional portion of said material on the material deposited by said spray-deposition operation.

8. The method defined in claim 1, further comprising the step of compressing said metallic open-pore structure to a reduced thickness while retaining porosity thereof.

9. The method defined in claim 1 wherein step (a) is carried out by applying a vacuum at a pressure no greater than 10^-3 torr to said steps, applying a voltage of 20 to 150 volts across said electrodes and supplying an arc current of 40 to 150 amperes.

10. The method defined in claim 1 wherein said support is a reticulated synthetic resin foam material.

11. The method defined in claim 10 wherein said foam material is a polyurethane foam.

12. The method defined in claim 1 wherein said element is a metal capable of forming an electrode for an electrochemical cell.

13. The method defined in claim 12 wherein said metal is nickel.

14. The method defined in claim 1 wherein said pyrolysis is carried out in the presence of air at a temperature of about 350°

C. for a period sufficient to substantially completely eliminate said support.

15. The method defined in claim 14 wherein said sintering is carried out in a vacuum oven in the absence of air or in an inert gas or reducing atmosphere at a temperature between substantially 950°

C. to 1250°

C. for a period sufficient to sinter said body into a structurally self-supporting state.

16. The method defined in claim 1 wherein 20 to 70 grams per square foot of metal is deposited on said support as said total amount.

17. The method defined in claim 2 wherein said binder is a synthetic resin material pyrolyzable under pyrolysis conditions identical to those at which said support can be pyrolyzed.

18. The method defined in claim 1 wherein the arc-vapor deposition, spray-deposition operations, pyrolysis and sintering are carried out continuously on a continuously advancing web of said support to continuously produce a web of said open-pore metal structure.