Low density, self-extinguishing epoxide composition

• US 5,019,605 A
• Filed: 03/15/1989
• Issued: 05/28/1991
• Est. Priority Date: 03/15/1989
• Status: Expired due to Fees

• Current Assignee: 3M Company
• Original Assignee: 3M Company
• Inventors: Jannic, Patrice
• Primary Examiner(s): Jacobs, Lewis T.
• Application Number:
  US07/324,237
• Time in Patent Office: 804 Days
• Field of Search: 523/218, 523/219, 523/445, 523/457, 523/451
• US Class Current: 523/219
• CPC Class Codes: C08K 3/22 of metals
• CPC Class Codes: C08K 3/38 Boron-containing compounds
• CPC Class Codes: C08K 7/22 Expanded, porous or hollow particles
• CPC Class Codes: C08L 63/00 Compositions of epoxy resins; Compositions of derivatives of epoxy resins

Abstract

A low density self-extinguishing epoxide composition employing an epoxide, an epoxide hardener, a smoke suppressant and a low density filler is provided. The composition contains from 3 to 10 weight percent bromine.

Claims

1. A low density, fire-resistant epoxide composition comprising:

(a) from 10 to 75 percent by weight of an organic epoxide compound having an epoxide functionality of at least 1;

(b) from 1 to 25 percent by weight of an epoxide hardener;

(c) from 20 to 50 percent by weight of a smoke suppressant;

(d) from 10 to 25 percent by weight of a filler capable of reducing the density of said composition; and

(e) from 1 to 10 percent by weight of an organic phosphorous-containing compound selected from the group consisting of alkyl phosphates, aryl phosphates, alkylphosphonates, arylphosphonates, and mixtures thereof,

wherein said composition contains from about 3 to 10 weight percent bromine.

2. A low density composition according to claim 1 wherein said organic epoxide is selected from the group consisting of epichlorohydrins, alkylene oxides, alkenyl oxides, glycidyl esters, glycidyl ethers, epoxy novolacs, copolymers of acrylic acid esters of glycidol and copolymerizable vinyl compounds, and polyurethane polyepoxides.

3. A low density composition according to claim 2 wherein said organic epoxide has an epoxide functionality of from 2 to 4.

4. A low density composition according to claim 3 wherein said organic epoxide is selected from the group consisting of diglycidyl ethers of bisphenol A and epoxy novolacs.

5. A low density composition according to claim 4 wherein said organic epoxide comprises from 15 percent to 25 percent by weight relative to the total weight of said composition.

6. A low density composition according to claim 1 wherein said epoxide hardener is selected from the group consisting of amines, acid anhydrides, Boron trifluoride complexes, guanidines, and dicyandiamide.

7. A low density composition according to claim 6 wherein said epoxide hardener is an acid anhydride.

8. A low density composition according to claim 6 wherein the weight ratio of said epoxide to said epoxide hardener is in the range of from about 0.7/1 to 1.5/1.

9. A low density composition according to claim 1 wherein said smoke suppressant comprises a material which gives off water when heated.

10. A low density composition according to claim 9 wherein said smoke suppressant is selected from the group consisting of alkaline earth metal hydroxides, aluminum group hydroxides, boric acid, and mixtures thereof.

11. A low density composition according to claim 10 wherein said smoke suppressant is an aluminum group hydroxide.

12. A low density composition according to claim 10 wherein said smoke suppressant is selected from the group consisting of aluminum hydroxide and a mixture of aluminum hydroxide and up to 10 weight percent magnesium hydroxide.

13. A low density composition according to claim 10 wherein said smoke suppressant comprises from 25 percent to 35 percent by weight with respect to the total weight of said composition.

14. A low density composition according to claim 1 wherein said low density filler is hollow microspheres.

15. A low density composition according to claim 14 wherein said low density filler has a density of less than 0.6 g/cm³.

16. A low density composition according to claim 14 wherein said hollow microspheres are selected from the group consisting of glass microspheres, ceramic microspheres zirconia microspheres, metal microspheres and polymeric microspheres.

17. A low density filler according to claim 16 wherein said microspheres have a density in the range of from 0.10 g/cm² to 0.45 g/cm³.

18. A low density composition according to claim 17 wherein said microspheres have a diameter in the range of from about 20 to 100 micrometers.

19. A low density filler according to claim 18 wherein said microspheres are glass microballoons.

20. A low density composition according to claim 1 further comprising

(f) up to 10 percent by weight of a boron-containing compound selected from the group consisting of alkaline earth borates and metaborates, alkali earth borates and metaborates, oxides of boron, and mixtures thereof.

21. A low density composition according to claim 20 wherein said boron-containing compound is selected from the group consisting of barium metaborate, calcium metaborate, zinc metaborate, zinc borate, and mixtures thereof.

22. A low density composition according to claim 1 wherein said phosphorous-containing compound comprises from 1% to 3% by weight with respect to the total weight of said composition.

23. A low density composition according to claim 1 wherein said phosphorous-containing compound comprises from 1.5% to 2% by weight with respect to the total weight of said composition.

24. A low density composition according to claim 1 further comprising

(g) up to 5 percent by weight of a wetting agent.

25. A low density composition according to claim 1 having a weight ratio of organic compounds to inorganic compounds of 1.2 to 1 or less.

26. A low density composition according to claim 1 further comprising

(i) up to 5 percent by weight of an accelerator for the curing of said epoxide.

27. A low density composition according to claim 1 wherein said bromine is provided by

(j) from 1 to 20 percent by weight of a brominated material selected from the group consisting of brominated epoxy resins, decabromodiphenyloxides, hexabromocyclododecane, tetradecabromodiphenyloxybenzene, and ethylene bis(tetrabromophthalimide).

29. A void filling composition according to claim 1, having a density of 0.35 to 1.0 g/cm³.

30. A void filling composition according to claim 1, having a compressive strength at room temperature above 15 N/mm² and above 7 N/mm² at 80°

C.

31. A void filling composition according to claim 1 which, upon being hardened, has a non-flaming smoke density of less than 100 after 90 seconds and less than 200 after 240 seconds

32. A composition according to claim 1 which, upon being hardened, has a flaming smoke density of less than 100 after 90 seconds and less than 200 after 240 seconds.

33. A composition according to claim 1 which, upon being hardened, has

i) a burn rate of less than 150 mm;

ii) a flame time of less than 15 seconds; and

iii) a drip flame time of less than 3 seconds;

when said hardened composition is held in a vertical position and ignited for 60 seconds.

34. A composition according to claim 1 which, upon being hardened, has

i) a burn rate of less than 200 mm;

ii) a flame time of less than 15 seconds; and

iii) a drip flame time of less than 5 seconds;

when said hardened composition is held in a horizontal position and ignited for 12 seconds.

35. A composition according to claim 1 which, upon being hardened, has a non-flaming smoke density of less than 100 after 90 seconds and less than 150 after 240 seconds.

36. A composition according to claim 1 which, upon being hardened, has a flaming smoke density of less than 100 after 90 seconds and less than 150 after 240 seconds.

28. A low density, one part, self-extinguishing epoxide composition comprising

(a) from 15 to 25 percent by weight of an organic epoxide compound having an epoxide functionality of from 2 to 4;

(b) a liquid epoxide hardener present in a quantity sufficient to provide a weight ratio of said epoxide to said hardener in the range of from about 0.7/1 to 1.5/1;

(c) from about 25 to 35 percent by weight of an inorganic hydroxide smoke suppressant;

(d) from 10 to 25 percent by weight of an inorganic, filler capable of reducing the density of said composition;

(e) up to about 10 percent by weight of an inorganic boron-containing compound;

(f) from 1 to 10 percent by weight of an inorganic phosphorous-containing compound;

(g) up to about 5 percent by weight of a wetting agent;

wherein said composition comprises from about 3 to 10 weight percent bromine and has a weight ratio of organic compounds to inorganic compounds of 1.2 to 1 or less.