Ruthenium supported catalyst, its preparation and its use in the preparation of substituted or unsubstituted cyclohexylamine and substituted or unsubstituted dicyclohexylamine

• US 5,023,226 A
• Filed: 01/09/1989
• Issued: 06/11/1991
• Est. Priority Date: 01/22/1988
• Status: Expired due to Fees

• Current Assignee: Bayer AG
• Original Assignee: Bayer AG
• Inventors: Immel, Otto, Schwarz, Hans-Helmut, Thiel, Reinhard
• Primary Examiner(s): Sneed, H. M.
• Assistant Examiner(s): Saba, Thomas
• Application Number:
  US07/294,836
• Time in Patent Office: 883 Days
• Field of Search: 502/313, 502/330, 502/332, 502/333, 502/334, 502/344, 502/184, 502/243, 564/450, 564/462
• US Class Current: 502/313
• CPC Class Codes: B01J 23/462 Ruthenium
• CPC Class Codes: B01J 23/6522 Chromium
• CPC Class Codes: B01J 23/6562 Manganese
• CPC Class Codes: C07C 209/72 by reduction of six-membered aromatic rings

Abstract

Substituted or unsubstituted cyclohexylamine and substituted or unsubstituted dicyclohexylamine can be produced by catalytic hydrogenation of substituted or unsubstituted aniline by using a ruthenium catalyst which in addition to ruthenium also contains palladium, platinum or palladium and platinum on a support from the group consisting of Al₂ O₃ and aluminum spinel treated with chromium and manganese and containing the noble metals in a total amount of 0.05-5% by weight and a weight ratio of Ru:Pd, Ru:Pt, or Ru:Pd/Pt of 1:9-9:1. All percentages are based on the total weight of the catalyst.

Claims

1. A Ruthenium catalyst also containing palladium, platinum or palladium and platinum in addition to ruthenium on a support treated with chromium and manganese from the group of Al₂ O₃ and aluminum spinel containing the noble metals in a total amount of 0.05-5% by weight and a weight ratio of Ru:

Pd, Ru;

Pt, or Ru;

Pd/Pt of 1;

9-9;

1, the percentages being based on the total weight of the catalyst.

2. The catalyst according to claim 1, characterized in that the noble metal content is 0.05-3% by weight.

3. The catalyst according to claim 2, characterized in that the nobel metal content is 0.1-2% by weight.

4. The catalyst according to claim 1, characterized in that the weight ratio of Ru:

Pd, Ru;

Pt, or Ru;

Pd/Pt is 2;

8-8;

2.

5. The catalyst according to claim 4, characterized in that the weight ratio of Ru:

Pd, Ru;

Pt, or Ru;

Pd/Pt is 3;

7-7;

3.

6. The catalyst according to claim 1, characterized in that up to 20% by weight of the total amount of ruthenium and palladium is replaced by other noble metals from the group consisting of iridium, rhodium, silver and gold.

7. The catalyst according to claim 1, characterized in that it contains 0.01-10% by weight, based on the total weight of the catalyst, of a basic alkali metal compound.

8. The catalyst according to claim 7, characterized in that the content of a basic alkali metal compound is 0,1-5% by weight.

9. The catalyst according to claim 7, characterized in that the basic alkali metal compounds are the oxides, hydroxides, alcoholates or salts of weak acids of Li, Na, K, Rb or Cs.

10. The catalyst according to claim 9, characterized in that the basic alkali metal compounds are the hydroxides, alcoholates or salts of weak acids of Li, Na or K.

11. The catalyst according to claim 1, characterized in that the treatment of the support with chromium and manganese is carried out up to a combined percentage of 0.05-8% weight, based on the total weight of the catalyst and the weight ratio of the elements chromium and manganese is set to 5:

1-1;

5.

12. The catalyst according to claim 11, characterized in that the combined chromium and manganese content is 0.2-5% by weight.

13. The catalyst according to claim 11, characterized in that the weight ratio of chromium and manganese is 10:

9-1;

2.

14. The catalyst according to claim 1, characterized in that it is treated with hydrogen at a temperature of 150°

-350°

C. prior to use.

15. A process for the preparation of a mixture of substituted or unsubstituted cyclohexylamine and substituted or unsubstituted dicyclohexylamine by hydrogenation of substituted or unsubstituted aniline with hydrogen in the presence of a ruthenium catalyst, characterized in that the ruthenium catalyst also containing palladium, platinum or palladium and platinum in addition to ruthenium on a support treated with chromium and manganese from the group consisting of Al₂ O₃ and aluminum spinel containing the noble metals in a total amount of 0.05-5% by weight and a weight ratio of Ru:

Pd, Ru;

Pt, or Ru;

Pd/Pt of 1;

9-9;

1, the percentages being based on the total weight of the catalyst is used and the reaction is carried out at 80°

-240°

C. at a pressure of 50-500 bar.

16. The process according to claim 15, characterized in that to increase the dicyclohexylamine percentage a higher temperature within the range of 80°

-240°

C. is chosen.

17. The process according to claim 15, characterized in that the space velocity of the catalyst is set to 0.05-2 kg of aniline per liter of catalyst per hour.

18. The process according to claim 15, characterized in that an aniline of the formula.