Process for making rapidly recoverable PTFE

• US 5,026,513 A
• Filed: 05/22/1989
• Issued: 06/25/1991
• Est. Priority Date: 10/19/1987
• Status: Expired due to Term

• Current Assignee: W. L. Gore & Associates (W.L. Gore & Associates)
• Original Assignee: W. L. Gore & Associates (W.L. Gore & Associates)
• Inventors: House, Wayne D., Myers, David J.
• Primary Examiner(s): Thurlow, Jeffery
• Application Number:
  US07/355,236
• Time in Patent Office: 764 Days
• Field of Search: 264/127, 264/288.8, 264/230, 264/210.2, 264/566, 264/154, 264/295
• US Class Current: 264/127
• CPC Class Codes: B29C 55/005 characterised by the choice of materials
• CPC Class Codes: B29C 67/20 for porous or cellular articles, e.g. of foam plastics, coarse-pored chemical aspects of working up macro-molecular substances to porous or cellular articles C08J9/00
• CPC Class Codes: B29K 2027/18 PTFE, i.e. polytetrafluorethene , e.g. ePTFE, i.e. expanded polytetrafluorethene
• CPC Class Codes: B29K 2105/04 cellular or porous
• CPC Class Codes: C08J 2327/18 Homopolymers or copolymers of tetrafluoroethylene
• CPC Class Codes: C08J 5/18 Manufacture of films or sheets
• CPC Class Codes: Y10S 264/47 Processes of splitting film, webs or sheets

Abstract

This invention relates to porous polytetrafluoroethylene (hereinafter PTFE) materials having the property of rapid recovery and a method for producing these materials. The microstructure of the porous PTFE material consists of nodes interconnected by fibrils, substantially all of the fibrils having a bent or wavy appearance. Articles made from these materials are particularly suitable for use in the medical field, but are also useful in other areas such as filtration and fabric applications.

Claims

1. A process for making rapid recoverable polytetrafluoroethylene (PTFE) material having a microstructure of nodes and fibrils comprising extruding a preformed billet of a mixture of coagulated dispersion of PTFE and liquid lubricant, expanding said PTFE after removal of liquid lubricant by stretching said PTFE longitudinally and maintaining said PTFE at a temperature between about 35°

C. and the crystalline melt point during stretching, compressing said extruded and expanded PTFE in the direction of the fibrils to reduce its size, restraining said PTFE in its compressed state, and heating said compressed PTFE.

2. A process as claimed in claim 1 wherein said compressed polytetrafluoroethylene is heated to a temperature above about its crystalline melt point.

3. A process for manufacturing a porous polytetrafluoroethylene tube with a microstructure of nodes and fibrils having rapid recovery in excess of about 5.5% comprising the steps of:

a) compressing and restraining said tube to less than about 50% of its original length;

b) heating at an elevated temperature for a period of time;

c) allowing it to cool; and

d) stretching the tube to approximately its original length.

4. A process for manufacturing a porous polytetrafluoroethylene tube with a microstructure of nodes and fibrils having rapid recovery in excess of about 5.5% comprising the steps of:

a) compressing and restraining said tube to less than about 50% of its original length;

b) maintaining the tube in a compressed and restrained state for a period of time; and

c) stretching the tube to approximately its original length.