Method for production of hydrophilic porous membrane of polyvinylidene fluoride

• US 5,032,331 A
• Filed: 02/26/1990
• Issued: 07/16/1991
• Est. Priority Date: 01/12/1987
• Status: Expired due to Fees

• Current Assignee: Terumo Kabushiki Kaisha (Terumo Corporation)
• Original Assignee: Terumo Kabushiki Kaisha (Terumo Corporation)
• Inventors: Onishi, Makoto, Koyama, Noriyuki, Seita, Yukio
• Primary Examiner(s): Lorin, Hubert C.
• Application Number:
  US07/484,838
• Time in Patent Office: 505 Days
• Field of Search: 204/296, 525/200, 525/366, 526/344, 521/27, 521/31, 264/48, 264/41, 264/232, 264/340, 210/500.42
• US Class Current: 264/48
• CPC Class Codes: B01D 67/0093 Chemical modification
• CPC Class Codes: B01D 69/02 characterised by their properties
• CPC Class Codes: B01D 71/34 Polyvinylidene fluoride
• CPC Class Codes: C08J 2327/16 Homopolymers or copolymers of vinylidene fluoride
• CPC Class Codes: C08J 9/40 Impregnation
• CPC Class Codes: Y10S 521/918 Physical aftertreatment of a cellular product

Abstract

A method for the production of a hydrophilic porous membrane of polyvinylidene fluoride excelling in perviousness to water and other various properties and enjoying high commercial value, having uniform hydrohilicity imparted to the surface of pores therein, which porous membrane is characterized by the fact that the reflection spectrum thereof in the visible zone is substantially unchanged from that which existed before the treatment for impartation of hydrophilcity. The method for the production of the hydrophilic porous membrane is characterized by chemically treating the porous membrane is a strong alkali solution containing an oxidizing agent.

Claims

1. A method for the production of hydrophilic porous membrane of polyvinylidene fluoride, comprising forming a porous membrane of polyvinylidene fluoride, impregnating an aqueous type solvent into the pores of said porous membrane, and subjecting the impregnated porous membrane to a chemical treatment in a strong alkali solution containing an oxidizing agent.

2. A method according to claim 1, wherein said oxidizing agent is potassium permanganate.

3. A method according to claim 1 or claim 2, wherein said strong alkali solution is an aqueous solution having potassium hydroxide or sodium hydroxide dissolved therein.

4. A method according to claim 1, wherein the concentration of said strong alkali solution is approximately 10 to 60% by weight.

5. A method according to claim 4, wherein the amount of said oxidizing agent in said strong alkali solution is approximately 1.0 to 15.0% by weight.

6. A method according to claim 1, wherein said impregnation is carried out for 1 to 60 minutes.

7. A method according to claim 6, wherein the temperature of said strong alkali solution is 20°

C. to 100°

C.