Method to prepare high strength ultrahigh molecular weight polyolefin articles by dissolving particles and shaping the solution

• US 5,032,338 A
• Filed: 05/22/1989
• Issued: 07/16/1991
• Est. Priority Date: 08/19/1985
• Status: Expired due to Term

• Current Assignee: Alliedsignal Inc. (Honeywell International Inc.)
• Original Assignee: Alliedsignal Inc. (Honeywell International Inc.)
• Inventors: Sun, Jim C., Weedon, Gene C., Tam, Thomas Y.
• Primary Examiner(s): Lorin, Hubert C.
• Application Number:
  US07/355,234
• Time in Patent Office: 785 Days
• Field of Search: 264/205, 264/210.8, 264/290.5, 264/211.14, 264/210.7, 264/203, 264/210.4, 264/211.15, 264/211.16, 264/211.18, 264/211.19, 264/237, 264/348, 526/352
• US Class Current: 264/203
• CPC Class Codes: B29C 55/005 characterised by the choice of materials
• CPC Class Codes: D01D 5/00 Formation of filaments, threads, or the like
• CPC Class Codes: D01F 6/04 from polyolefins

Abstract

A method to prepare high strength high modulus polyolefin shaped articles comprising forming a heated solution of the polyolefin from particles of which about 75 to 100% by weight have a particle size of from about 100 to about 400 microns and having a weight average molecular weight of from about 300,000 to 7,000,000, then shaping the heated soltion then cooling the shaped solution. To further increase the strength of the article it can be stretched.

Claims

1. A method to prepare high strength, high modulus polyolefin shaped articles comprising

forming a heated solution of said polyolefin from particles of which about 75 to about 100% by weight have a particle size of from about 100 to about 400 microns and having a weight average molecular weight of from about 300,000 to 7,000,000, the particle size being distributed in a substantially Gaussian curve of particle sizes centered at about 125 to 200 microns so that the polyolefin particles are completely dissolved and the solution obtained therefrom is substantially uniform in properties throughout,

extruding said heated solution,

cooling said extruded solution, and

stretching said extruded solution.

2. The method of claim 1 wherein said cooling is after removal of solvent from said shaped solution.

3. The method of claim 1 wherein said cooling is during removal of solvent from said shaped solution.

4. The method of claim 1 wherein said cooling is before removal of solvent from said shaped solution.

5. The method of claim 1 wherein about 85 to 100% of the particles have a particle size between about 120 and about 350 microns.

6. The method of claim 1 wherein the molecular weight is between about 700 000 and 5 000 000.

7. The method of claim 1 wherein the polyolefin is polyethylene.

8. The method of claim 7 wherein the molecular weight of the polyethylene is about 700 000 to about 5 000 000.

9. The method of claim 8 wherein the article is a fiber.

10. The method of claim 8 wherein the polyethylene intrinsic viscosity is between about 6 and b 30.

11. The method of claim 1 wherein at least about 40% of the particles are retained on a No. 80 mesh screen.

12. The method of claim 1 wherein the solvent is a hydrocarbon having a boiling point over 100°

C.

13. The method of claim 12 wherein the solvent is selected from the group consisting of halogenated hydrocarbons, mineral oil, decalin, tetralin, naphthalene, xylene, toluene, dodecane, undecane, decane, nonane, octane, and low molecular weight polyethylene wax.

14. The method of claim 1 wherein the solution consists of about 1% to about 35% polyolefin by weight.

15. The method of claim 14 wherein the solution consists of from about 2 to about 25% by weight polyolefin.

16. The method of claim 1 wherein said stretching is after removal of solvent from the shaped solution.

17. The method claim 1 where said stretching is before removal of solvent from the shaped solution.

18. The method of claim 1 wherein the shaped solution is stretched both before and after removal of solvent from said shaped solution.

19. The method of claim 1 wherein the shaped article has been stretched to a length at least five times its original length.