PTC devices and their composition
First Claim
1. An electrically conductive self-regulating heater article capable of operation at high temperatures, said article comprising at least two spaced elongated electrodes electrically interconnected by and embedded in a self-regulating semiconductive composition exhibiting a positive temperature coefficient of electrical resistance, said composition containing (a) a fluoropolymer having (i) at least 20% crystallinity as determined by X-ray diffraction and (ii) a melting point of at least 170°
- C. and (b) a particulate filler component which is dispersed in the polymer and which comprises carbon black in an amount from 12 to 20% by weight of the composition the improvement which comprises;
the carbon black comprising three carbon blacks, each characterized by low structure and high resistivity, first and second ones of the carbon blacks being selected to impart the positive temperature coefficient and the third carbon black being selected to adjust the resistive properties of the composition into the range of commercial usage.
2 Assignments
0 Petitions
Accused Products
Abstract
PTC Devices and PTC compositions described herein comprise a blend of at least three carbon blacks as a particulate filler in a fluorinated polymer to achieve a substantial PTC effect and operability over a wide temperature range including temperatures prevailing in a steam environment. Two of the carbon blacks are selected to impart PTC effect to the composition. The third carbon black is selected to adjust the resistive properties of the composition into the range of commercial usage and to impart uniformity of the resistive properties within a given batch as well as from one batch of mix to the next.
-
Citations
14 Claims
-
1. An electrically conductive self-regulating heater article capable of operation at high temperatures, said article comprising at least two spaced elongated electrodes electrically interconnected by and embedded in a self-regulating semiconductive composition exhibiting a positive temperature coefficient of electrical resistance, said composition containing (a) a fluoropolymer having (i) at least 20% crystallinity as determined by X-ray diffraction and (ii) a melting point of at least 170°
- C. and (b) a particulate filler component which is dispersed in the polymer and which comprises carbon black in an amount from 12 to 20% by weight of the composition the improvement which comprises;
the carbon black comprising three carbon blacks, each characterized by low structure and high resistivity, first and second ones of the carbon blacks being selected to impart the positive temperature coefficient and the third carbon black being selected to adjust the resistive properties of the composition into the range of commercial usage.
- C. and (b) a particulate filler component which is dispersed in the polymer and which comprises carbon black in an amount from 12 to 20% by weight of the composition the improvement which comprises;
-
2. An electrically conductive self-regulating heater article as set forth in claim 1 wherein the first carbon black has a relatively high volatile content and the second carbon black has a volatile content which is one-half or less than that of the first carbon black.
-
3. A self regulating heater article as set forth in claim 2 wherein the third carbon black has a volatile content that is less than one-third that of the first carbon black.
-
4. A self-regulating heater article as set forth in claim 1 wherein the percentage by weight proportion of the third carbon black is less than the combined percentage by weight proportions of the first and second carbon blacks.
-
5. A self-regulating heater article as set forth in claim 4 wherein the first carbon black has a relatively high volatile content and the second carbon black has a volatile content which is one-half or less than that of the first carbon black.
-
6. A self regulating heater article as set forth in claim 5 wherein the third carbon black has a volatile content that is less than one-third that of the first carbon black.
-
7. An electrically conductive self-regulating heater article in accordance with claim 6 wherein the percentage by weight of the first carbon black based upon the total mixture weight is at least 6%.
-
8. An electrically conductive self-limiting semiconductive composition exhibiting a positive temperature coefficient of electrical resistance, said composition containing (a) a fluoropolymer having (i) at least 20% crystallinity as determined by X-ray diffraction and (ii) a melting point of at least 170°
- C. and (b) a particulate filler component which is dispersed in the polymer and which comprises carbon black in an amount from 12 to 20% by weight of the composition the improvement which comprises;
the carbon black comprising three carbon blacks, each characterized by low structure and high resistivity, first and second ones of the carbon blacks being selected to impart the positive temperature coefficient and the third carbon black being selected to adjust the resistive properties of the composition into the range of commercial usage.
- C. and (b) a particulate filler component which is dispersed in the polymer and which comprises carbon black in an amount from 12 to 20% by weight of the composition the improvement which comprises;
-
9. An electrically conductive self-regulating heater article as set forth in claim 8 wherein the first carbon black has a relatively high volatile content and the second carbon black has a volatile content which is one-half or less than that of the first carbon black.
-
10. A self regulating heater article as set forth in claim 9 wherein the third carbon black has a volatile content that is less than one-third that of the first carbon black.
-
11. A self-regulating heater article as set forth in claim 8 wherein the percentage by weight proportion of the third carbon black is less than the combined percentage by weight proportions of the first and second carbon blacks.
-
12. A self-regulating heater article as set forth in claim 11 wherein the first carbon black has a relatively high volatile content and the second carbon black has a volatile content which is one-half or less than that of the first carbon black.
-
13. A self regulating heater article as set forth in claim 12 wherein the third carbon black has a volatile content that is less than one-third that of the first carbon black.
-
14. An electrically conductive self-regulating heater article in accordance with claim 13 wherein the percentage by weight of the first carbon black based upon the total mixture weight is at least 6%.
Specification