Process for firing ceramic shaped bodies and a tunnel kiln used therefor
First Claim
1. A method of firing cordierite ceramic honeycomb shaped bodies to produce substantially crack-free sintered bodies, the method sequentially comprising the following steps:
- heating said bodies at a first heating rate between room temperature and a decomposition temperature of a shaping aid contained in said bodies; and
heating said bodies at a second heating rate between said decomposition temperature and a sintering temperature, said first heating rate being less than said second heating rate;
wherein said bodies are heated at a constantly changing temperature between said room temperature and said sintering temperature.
0 Assignments
0 Petitions
Accused Products
Abstract
A process for firing ceramic shaped bodies is disclosed, which comprises the step of making a heating temperature in a temperature range up to a decomposing temperature of a shaping aid contained in the ceramic shaped body smaller than that in a temperature range from the decomposing temperature to a firing temperature. A tunnel kiln is also disclosed, which comprises a preheating zone, a firing zone, a waste heat zone, combustion burners provided at the firing zone, an exhaust means provided at an inlet side of the preheating zone for evacuating combustion gases from the combustion burners outside the kiln, and another exhaust means provided at an outlet side of the preheating zone for evacuating the combustion gases outside the kiln.
22 Citations
2 Claims
-
1. A method of firing cordierite ceramic honeycomb shaped bodies to produce substantially crack-free sintered bodies, the method sequentially comprising the following steps:
-
heating said bodies at a first heating rate between room temperature and a decomposition temperature of a shaping aid contained in said bodies; and heating said bodies at a second heating rate between said decomposition temperature and a sintering temperature, said first heating rate being less than said second heating rate; wherein said bodies are heated at a constantly changing temperature between said room temperature and said sintering temperature. - View Dependent Claims (2)
-
Specification
-
- Resources
-
Current AssigneeNGK Insulators Limited
-
Original AssigneeNGK Insulators Limited
-
InventorsOgura, Koji, Yasuda, Keiji, Miyahara, Kazuhiro
-
Primary Examiner(s)Bennet, Henry A.
-
Assistant Examiner(s)Kilner, Christopher B.
-
Application NumberUS07/555,796Time in Patent Office414 DaysField of Search432/128, 432/129, 432/133, 432/136, 432/137, 432/141, 432/143, 432/144, 432/145, 432/146, 432/149, 432/150, 432/152, 432/153, 432/11, 432/12, 432/13, 432/18, 264/64, 264/59, 264/63, 264/66, 428/116US Class Current264/631CPC Class CodesF27B 9/3011 arrangements for circulatin...Y10T 428/24149 Honeycomb-like