Composition and method for treatment of conversion coated metal surfaces with an aqueous solution of 3-aminopropyltriethoxy silane and titanium chelate
First Claim
Patent Images
1. A composition of matter, useful for treating a conversion coated metal surface to provide enhanced siccative coating adhesion and corrosion resistance properties thereto, comprising an aqueous solution of:
- (a) about 0.2-300 g/l of 3-aminopropyltriethoxysilane; and
(b) about 0.01-100 g/l of an organic titanium chelate comprising, as its reactive components, a tetraalkytitanate, a beta-diketone and an alkanolamine, said chelate containing 8.6% titanium and having a specific gravity (25°
C./25°
C.) of 1.03, a viscosity (cP) at 25°
of about 50, a thickening point of less than -25° and
a flash point of 13°
C. (closed cup), as determined by a Pensky-Martens Closed Tester.
3 Assignments
0 Petitions
Accused Products
Abstract
A final rinse composition, for enhancing the siccative coating adhesion and corrosion resistance properties of conversion coated metal surfaces, comprising an aqueous solution of a selected organosilane and a selected organotitanate, and a method of use thereof.
68 Citations
9 Claims
-
1. A composition of matter, useful for treating a conversion coated metal surface to provide enhanced siccative coating adhesion and corrosion resistance properties thereto, comprising an aqueous solution of:
-
(a) about 0.2-300 g/l of 3-aminopropyltriethoxysilane; and (b) about 0.01-100 g/l of an organic titanium chelate comprising, as its reactive components, a tetraalkytitanate, a beta-diketone and an alkanolamine, said chelate containing 8.6% titanium and having a specific gravity (25°
C./25°
C.) of 1.03, a viscosity (cP) at 25°
of about 50, a thickening point of less than -25° and
a flash point of 13°
C. (closed cup), as determined by a Pensky-Martens Closed Tester. - View Dependent Claims (2, 3, 4, 5)
-
-
6. A composition of matter consisting essentially of an aqueous solution of:
-
(a) about 8 w/o 3-aminopropyltriethoxysilane; and (b) about 1 w/o an organic titanium chelate comprising, as its reactive components, a tetraalkyltitanate, a beta-diketone and an alkanolamine, said chelate containing 8.6% titanium and having a specific gravity (25°
C./25°
C.) of 1.03, a viscosity (cP) at 25°
C. of about 50, a thickening point of less than -25°
C. and a flash point of 13°
C. (closed cup), as determined by a Pensky-Martens Closed Tester.
-
-
7. A method of imparting enhanced siccative coating adhesion and corrosion resistance properties to a conversion coated metal surface by contacting said surface with a composition of matter comprising an aqueous solution of:
-
(a) about 0.2-50 g/l of 3-aminopropyltriethoxysilane; and (b) about 0.01-20 g/l of an organic titanium chelate comprising, as its reactive components, a tetraalkyltitanate, a beta-diketone and an alkanolamine, said chelate containing 8.6% titanium and having a specific gravity (25°
C./25°
C.) of 1.03, a viscosity (cP) at 25°
C. and a flash point of 13°
C. (closed cup), as determined by a Pensky-Martens Closed Tester. - View Dependent Claims (8, 9)
-
Specification