Carrier for catalyst and method for production thereof

• US 5,055,442 A
• Filed: 02/16/1990
• Issued: 10/08/1991
• Est. Priority Date: 02/17/1989
• Status: Expired due to Fees

• Current Assignee: Nippon Shokubai Company Limited
• Original Assignee: Nippon Shokubai Kagaku Kogyo Co., Ltd.
• Inventors: Takashashi, Tsukasa, Hata, Kazuo, Osaka, Shigemi
• Primary Examiner(s): Shine, W. J.
• Assistant Examiner(s): McGinty, D. J.
• Application Number:
  US07/480,961
• Time in Patent Office: 599 Days
• Field of Search: 502/527, 502/439, 502/349
• US Class Current: 502/439
• CPC Class Codes: B01J 23/26 Chromium
• CPC Class Codes: B01J 23/42 Platinum
• CPC Class Codes: B01J 35/50 characterised by their shape or configuration
• CPC Class Codes: B01J 35/58 Fabrics or filaments
• CPC Class Codes: B01J 37/0207 Pretreatment of the support

Abstract

A carrier for catalyst using refractory particles as cores and having a refractory inorganic powder and optionally whiskers, inorganic oxide sols, or mixtures thereof deposited on the cores, and a method for the production thereof.

Claims

1. A carrier for catalyst comprising refractory inorganic particles as cores and having a refractory inorganic powder deposited on said cores, wherein the amount of said refractory inorganic powder is in the range of 1 to 500 g, based on 100 ml of said refractory inorganic particles, and said refractory inorganic particles possess particle diameters in the range of 0.3 to 12 mm and said refractory inorganic powder possesses an average particle diameter in the range of 0.05 to 1,200 μ

m.

2. A carrier according to claim 1, wherein said refractory inorganic particles and said powder are formed of at least one member substance selected from the group consisting of metal oxides, composite metal oxides, and non-oxides.

3. A carrier for catalyst comprising refractory inorganic particles as cores and having a refractory inorganic powder and whiskers deposited on the cores.

4. A carrier according to claim 3, wherein the amount of said refractory inorganic powder is in the range of 1 to 500 g, based on 100 ml of said refractory inorganic particles and the amount of said whiskers is in the range of 1 to 50% by weight, based on the amount of said refractory inorganic powder.

5. A carrier according to claim 4, wherein said refractory inorganic particles possess particle diameters in the range of 0.3 to 12 mm and said refractory inorganic powder possesses an average particle diameter in the range of 0.05 to 1,200 μ

m and said whiskers possess an average diameter in the range of 0.1 to 5 μ

m and a length in the range of 5 to 1,000 μ

m.

6. A carrier according to claim 5, wherein said refractory inorganic particles and said powder are formed of at least one member substance selected from the group consisting of metal oxides, composite metal oxides, and non-oxides.

7. A carrier for catalyst using refractory inorganic particles as cores and having a refractory inorganic powder and inorganic oxide sols deposited on said cores.

8. A carrier according to claim 7, wherein the amount of said refractory inorganic powder is in the range of 1 to 500 g, based on 100 ml of said refractory inorganic particles and the amount of said inorganic oxide sol is in the range of 0.5 to 20 % by weight calculated as an oxide, based on the amount of said refractory inorganic powder.

9. A carrier according to claim 8, wherein said refractory inorganic particles possess particle diameters in the range of 0.3 to 12 mm and said refractory inorganic powder possesses an average particle diameter in the range of 0.05 to 1,200 μ

m.

10. A carrier according to claim 9, wherein said refractory inorganic particles and said powder are formed of at least one ceramic substance selected from the group consisting of metal oxides, composite metal oxides, and non-oxides.

11. A carrier according to claim 8, wherein said inorganic oxide sol is zirconia sol.

12. A carrier for catalyst comprising refractory inorganic particles as cores and having a refractory inorganic powder, whiskers, and inorganic oxide sol deposited on said cores.

13. A carrier according to claim 12, wherein the amount of said refractory inorganic powder is in the range of 1 to 500 g, based on 100 ml of said refractory inorganic particles and the amount of said whiskers is in the range of 1 to 50% by weight and the amount of said inorganic oxide sol is in the range of 0.5 to 20 % by weight calculated as an oxide, based on the amount of said refractory inorganic powder.

14. A carrier according to claim 13, wherein said refractory inorganic particles possess particle diameters in the range of 0.3 to 12 mm and said refractory inorganic powder possesses an average particle diameter in the range of 0.05 to 1,200 μ

m and said whiskers possess an average diameter in the range of 0.1 to 5 μ

m and a length in the range of 5 to 1,000 μ

m.

15. A carrier according to claim 14, wherein said refractory inorganic particles and said powder are formed of at least one member substance selected from the group consisting of metal oxides, composite metal oxides, and non-oxides.

16. A carrier according to claim 13, wherein said inorganic oxide sol is zirconia sol.

17. A method for the production of a carrier for catalyst comprising refractory inorganic particles as cores and having a refractory inorganic powder deposited on the cores, which method comprises applying a slurry of the refractory inorganic powder to the refractory inorganic particles and drying the resultant wet refractory inorganic particles;

wherein the amount of said refractory inorganic powder is in the range of 1 to 500 g, based on 100 ml of said refractory inorganic particles and said refractory inorganic particles possess particle diameters in the range of 0.3 to 12 mm and said refractory inorganic powder possesses an average particle diameter in the range of 0.05 to 1,200 μ

m.

18. A method according to claim 17, wherein after the drying an inorganic oxide sol is further applied to said carrier.

19. A method according to claim 17, wherein said carrier is further calcined.

20. A method for the production of a carrier for catalyst using refractory inorganic particles as cores and having a refractory inorganic powder and whiskers deposited on the cores, which method comprises applying a mixed slurry of the refractory inorganic powder and whiskers to the refractory inorganic particles and drying the resultant wet refractory inorganic particles.

21. A method according to claim 20, wherein the amount of said refractory inorganic powder is in the range of 1 to 500 g, based on 100 ml of said refractory inorganic particles and the amount of said whiskers is in the range of 1 to 50% by weight, based on the amount of said refractory inorganic powder.

22. A method according to claim 21, wherein said refractory inorganic particles possess particle diameters in the range of 0.3 to 12 mm and said refractory inorganic powder possesses an average particle diameter in the range of 0.05 to 1,200 μ

m and said whiskers possess an average diameter in the range of 0.1 to 5 μ

m and a length in the range of 5 to 1,000 μ

m.

23. A method according to claim 20, wherein after the drying an inorganic oxide sol is further applied to said carrier.

24. A method according to claim 20, wherein said carrier is further calcined.

33. A method for production of a carrier for catalyst according to any one of claims 20, 25, or 29, which comprises using a centrifugal flow coating device in the applying step.

25. A method for the production of a carrier for catalyst using refractory inorganic particles as cores and having a refractory inorganic powder and inorganic oxide sol deposited on the cores, which method comprises applying a mixed slurry of the refractory inorganic powder and the inorganic oxide sol to the refractory inorganic particles and drying the resultant wet refractory inorganic particles.

26. A method according to claim 25, wherein the amount of said refractory inorganic powder is in the range of 1 to 500 g, based on 100 ml of said refractory inorganic particles and the amount of said inorganic oxide sol is in the range of 0.5 to 20% by weight calculated as an oxide, based on the amount of said refractory inorganic powder.

27. A method according to claim 26, wherein said refractory inorganic particles possess particle diameters in the range of 0.3 to 12 mm and said refractory inorganic powder possesses an average particle diameter in the range of 0.05 to 1,200 μ

m.

28. A method according to claim 25, wherein said carrier is, further calcined.

29. A method for the production of a carrier for catalyst using refractory inorganic particles as cores and having a refractory inorganic powder, whiskers, and inorganic oxide so deposited on the cores, which method comprises applying a mixed slurry of the refractory inorganic powder, the whiskers, and the inorganic oxide sol to the refractory inorganic particles and drying the resultant wet refractory inorganic particles.

30. A method according to claim 29, wherein the amount of said refractory inorganic powder is in the range of 1 to 500 g, based on 100 ml of said refractory inorganic particles and the amount of said whiskers is in the range of 1 to 50% by weight and the amount of said inorganic oxide sol is in the range of 0.5 to 20% by weight calculated as an oxide, based on the amount of said refractory inorganic powder.

31. A method according to claim 30, wherein said refractory inorganic particles possess particle diameters in the range of 0.3 to 12 mm and said refractory inorganic powder possesses an average particle diameter in the range of 0.05 to 1,200 μ

m and said whiskers possess an average diameter in the range of 0.1 to 5 μ

m and a length in the range of 5 to 1,000 μ

m.

32. A method according to claim 29, wherein said carrier is further calcined.