Fibrous base web bonding system and method

• US 5,063,104 A
• Filed: 01/03/1990
• Issued: 11/05/1991
• Est. Priority Date: 01/03/1990
• Status: Expired due to Term

• Current Assignee: Ahlstrom Dexter LLC
• Original Assignee: Dexter Corp. (Thermo Fisher Scientific Incorporated)
• Inventors: Byalik, Ludmila, Robertson, Diane M.
• Primary Examiner(s): Cannon, James C.
• Application Number:
  US07/460,405
• Time in Patent Office: 671 Days
• Field of Search: 138/118.1, 138/146, 427/342, 427/411, 426/105, 426/135, 428/34.3, 428/34.8, 428/286, 428/287
• US Class Current: 442/165
• CPC Class Codes: A22C 13/0013 Chemical composition of synthetic sausage casings
• CPC Class Codes: A22C 2013/0059 thermoplastic casings, casings with at least one layer of thermoplastic material
• CPC Class Codes: Y10T 428/1324 Flexible food casing [e.g., sausage type, etc.]
• CPC Class Codes: Y10T 428/1352 Polymer or resin containing [i.e., natural or synthetic]
• CPC Class Codes: Y10T 428/28 Web or sheet containing structurally defined element or component and having an adhesive outermost layer
• CPC Class Codes: Y10T 428/31895 Paper or wood
• CPC Class Codes: Y10T 442/2869 Coated or impregnated regenerated cellulose fiber fabric

Abstract

A bonded porous sheet material for use in the manufacture of food casing, said material being produced by treating a fibrous web with a thermoplastic film forming material which bonds the fibers of the web and imparts high alkaline strength to the treated wet and subsequently treating the bonded fiber web with a solution of film forming material and an insolubilizing agent for the film forming material.

Claims

1. A bonded porous fibrous sheet material for use in the manufacture of food casings and the like comprising a fibrous base web containing about 10% by weight and less of a bonding system comprising a first treatment of a thermoplastic film forming material effective for imparting high alkaline strength to the base web and a subsequent treatment of a film forming material and an insolubilizing agent for the film forming material, said subsequent treatment being effective to impart high wet strength and absorption to the first treated web without substantially reducing the alkaline strength thereof.

2. The bonded sheet material of claim 1 wherein the thermoplastic film forming material is poly(vinyl alcohol).

3. The bonded sheet material of claim 1 wherein the thermoplastic film forming material includes at least about 25% by weight of poly(vinyl alcohol).

4. The bonded sheet material of claim 1 wherein the thermoplastic film forming material comprises at least about 80% by weight of poly(vinyl alcohol).

5. The bonded sheet material of claim 1 wherein the film forming material of the subsequent treatment is a cellulose based material.

6. The bonded sheet material of claim 1 wherein the cellulose based material is selected from the group consisting of hydroxyethyl cellulose, hydroxypropyl cellulose, hydroxypropylmethyl cellulose, carboxymethyl cellulose and methyl cellulose.

7. The bonded sheet material of claim 1 wherein the film forming material of the subsequent treatment is selected from the group consisting of cellulose based materials, cationic and anionic starches and modified proteins.

8. The bonded sheet material of claim 1 wherein the insolubilizing agent is selected from the group consisting of dialdehydes, alkaline curing resins, melamine formaldehyde, glyoxylated polyacrylamides, multivalent metal ions, inorganic salts, urea formaldehyde and polyamides.

9. The bonded sheet material of claim 1 wherein the ratio of insolubilizing agent to film former falls within the range of about 1:

10 to 1;

1.

10. The bonded sheet material of claim 1 wherein the amount of the binder system in the base web falls within the range of about 2% to 6% by weight.

11. The bonded sheet material of claim 1 wherein the binder system includes less than 1% by weight of a surfactant.

12. The bonded sheet material of claim 1 wherein the sheet material has a caustic tensile strength of at least about 300 grams.

13. A food packaging material comprising a fibrous base web and a coating thereon comprising a first treatment of a poly(vinyl alcohol) film forming material and a subsequent treatment of a film forming material selected from the group consisting of celulose based materials, cationic and anionic starches and modified proteins and an insolubilizing agent for the film forming material selected from the group consisting of dialdehydes, alkaline curing resins, melamine formaldehyde, glyoxylated polyacrylamides, multivalent metal ions, inorganic salts, urea formaldehyde and polyamides.

15. The process of claim 13 wherein the first bonding solution is a solution of poly(vinyl alcohol).

16. The process of claim 15 wherein the solution of poly(vinyl alcohol) comprises an aqueous solution of vinyl polymers wherein the poly(vinyl alcohol) moiety constitutes at least about 25% by weight of the vinyl polymer content.

17. The process of claim 16 wherein the poly(vinyl alcohol) moiety constitutes at least about 80% by weight of the vinyl polymer content.

19. The process of claim 16 wherein the concentration of thermoplastic material falls within the range of about 5% to 1.5% by weight.

14. A process for producing a bonded porous fibrous sheet material for use in the manufacture of food casings comprising the steps of treatment the base web material with a first bonding solution of a thermoplastic film forming material effective for imparting high alkaline strength to the web and subsequently treating the thermoplastic bonded web with a solution of a film forming material and an insolubilizing agent for the film forming material, said subsequent treatment being effective to impart high wet strength and absorption to the first treated web without substantially reducing the alkaline strength thereof.

18. The process of claim 14 wherein the first bonding solution is an aqueous solution having a concentration of thermoplastic material of about 5% by weight and less.

20. The process of claim 14 wherein the film forming solution of the subsequent treatment is an aqueous solution having a concentration of film forming material of about 8% by weight and less.