Foamable thermosetting polyurethane structural adhesive compositions and processes for producing the same

• US 5,075,407 A
• Filed: 04/10/1989
• Issued: 12/24/1991
• Est. Priority Date: 04/10/1989
• Status: Expired due to Term

• Current Assignee: Royal Adhesives & Sealants, LLC (Republic Services Incorporated)
• Original Assignee: Rheox, Inc. (Elementis PLC)
• Inventors: Hartman, Terrence L., Cody, Charles A.
• Primary Examiner(s): Kight, III, John
• Assistant Examiner(s): Mosley, T.
• Application Number:
  US07/336,002
• Time in Patent Office: 988 Days
• Field of Search: 521/92, 521/123, 525/453, 528/59, 528/71
• US Class Current: 528/71
• CPC Class Codes: C08G 18/08 Processes
• CPC Class Codes: C08G 18/10 Prepolymer processes involving reaction of isocyanates or isothiocyanates with compounds having active hydrogen in a first reaction step
• CPC Class Codes: C08G 18/12 using two or more compounds having active hydrogen in the first polymerisation step
• CPC Class Codes: C08G 18/302 Water
• CPC Class Codes: C08G 18/4202 Two or more polyesters of different physical or chemical nature C08G18/44 takes precedence
• CPC Class Codes: C08G 18/60 Polyamides or polyester-amides
• CPC Class Codes: C08G 18/603 Polyamides
• CPC Class Codes: C08G 2170/60 Compositions for foaming; Foamed or intumescent adhesives
• CPC Class Codes: C09J 175/06 from polyesters

Abstract

The present invention relates to foamable thermosetting polyurethane structural adhesive composites and compositions and processes for producing the same comprising dispersing a water-generating curing composition into a polyurethane base resin to form a nonactivated adhesive composite, and activating the same by heating to form an adhesive composition. Another aspect of the invention relates to dispersing a water-generating compound and an amine-terminated solid polyamide resin into the polyurethane base resin and heat-activating the same to form an adhesive composition.

Claims

1. A process for preparing a thermosetting polyurethane composite comprising dispersing a water-generating curing composition into a polyurethane base resin.

2. The process of claim 1 wherein said dispersing step is carried out at a temperature of from about 25°

C. to about 200°

C.

3. The process of claim 1 wherein said base resin is a liquid.

4. The process of claim 1 wherein the water-generating curing composition generates water by water formation or release at an elevated temperature.

5. The process of claim 4 wherein the polyurethane base resin has a melting point at least 5 degrees lower than the point of water formation or release from the water-generating curing composition.

6. The process of claim 5 wherein the polyurethane base resin has a melting point at least 40 degrees lower than the point of water formation or release from the water-generating curing composition.

7. The process of claim 1 wherein said polyurethane base resin is prepared by reacting excess 4,4'"'"'-diphenylmethane diisocyanate and at least one saturated copolyester diol compound.

8. The process of claim 1 wherein the water generating curing composition is at least one compound selected from the group consisting of CaSO₄.2H₂ O, CaSO₄.1/2H₂ O, NaHCO₃, (NH₄)₂ CO₃, (NH₄)₂ C₂ O₄ and ammonium stearate.

9. The process of claim 1 further comprising drying the water-generating curing composition prior to dispersing the curing composition into the polyurethane base resin.

10. The process of claim 1 further comprising treating the water-generating curing composition with at least one mono-isocyanate compound prior to dispersing the curing composition into the polyurethane base resin.

11. The process of claim 1 further comprising dispersing the water-generating curing composition into an inert encapsultant composition prior to dispersing the curing composition into the polyurethane base resin.

12. The process of claim 1 wherein the inert encapsultant composition is a thermoplastic resin.

13. The process of claim 12 wherein the water-generating curing composition generates water by water formation or release at an elevated temperature.

14. The process of claim 13 wherein the inert encapsultant composition has a melting point higher than the melting point of the polyurethane base resin and lower than the point of water formation or release from the water-generating curing composition.

15. The process of claim 1 wherein the polyurethane base resin is prepared by reacting an excess amount of a polyisocyanate compound with at least one copolyester selected from (a) a hydroxyl-terminated, linear, solid, amorphous saturated copolyester having a glass transition temperature greater than 0°

C. and having from about 80% to about 100% aromatic character;

(b) a hydroxyl-terminated, linear, saturated, liquid copolyester having a glass transition temperature between about -10°

C. and about -60°

C. and having from about 40% to about 100% aliphatic character; and

(c) a hydroxyl-terminated, linear, solid, partially crystalline, saturated copolyester having a glass transition temperature below 0°

C. and having from about 40% to about 100% aliphatic character, wherein said copolyesters each have a molecular weight between about 1000 g/mol and 6000 g/mol and wherein the amounts of said copolyesters are from about 0 to about 1 equivalent of the solid amorphous saturated copolyester, from about 0 to about 1 equivalent of the saturated liquid copolyester, and from about 0 to about 1 equivalent of the partially crystalline saturated copolyester, and wherein the sum of the equivalent amounts of said copolyesters is 1.

16. The process of claim 15 wherein the polyisocyanate compound is 4,4'"'"'-diphenylmethane diisocyanate.

17. The process of claim 1 further comprising dispersing a foam promoting agent into said polyurethane base resin.

18. The process of claim 17 wherein said foam promoting agent is selected from the group consisting of polyalkyleneoxide-methylsiloxane copolymers, tertiary amine catalysts, methylene chloride and monofluorotrichloromethane.

19. The process of claim 1 further comprising dispersing a foam reducing agent into said polyurethane base resin.

20. The process of claim 19 wherein said foam reducing agent is selected from the group consisting of calcium oxide, soda lime, activated carbon, molecular sieves and di-methylpolysiloxanes.

21. The process of claim 1 wherein the ratio of equivalents of isocyanate groups to active hydrogen groups in said composite is from about 0.5:

1.0 to about 2.0;

1.0.

22. The process of claim 21 wherein the ratio of equivalents of isocyanate groups to active hydrogen groups in said composite is from about 0.8:

1.0 to about 1.2;

1.0.

39. The thermosetting polyurethane composite of claim 14 wherein the composite further comprises a foam promoting agent.

40. The thermosetting polyurethane composite of claim 39 wherein said foam promoting agent is selected from the group consisting of polyalkyleneoxide-methylsiloxane copolymers, tertiary amine catalysts, methylene chloride and monofluorotrichloromethane.

23. A thermosetting polyurethane composite comprising a polyurethane base resin and a water-generating curing composition.

24. The thermosetting polyurethane composite of claim 23 wherein the polyurethane base resin is prepared by reacting excess 4,4'"'"'-diphenylmethane diisocyanate and at least one saturated copolyester diol compound.

25. The thermosetting polyurethane composite of claim 23 wherein the polyurethane base resin is prepared by reacting an excess amount of a polyisocyanate compound with at least one copolyester selected from (a) a hydroxyl-terminated, linear solid, amorphous saturated copolyester having a glass transition temperature greater than 0°

C. and having from about 80% to about 100% aromatic character;

(b) a hydroxyl-terminated, linear, saturated, liquid copolyester having a glass transition temperature between about -10°

C. and about -60°

C. and having from about 40% to about 100% aliphatic character; and

(c) a hydroxyl-terminated, linear, solid, partially crystalline, saturated copolyester having a glass transition temperature below 0°

C. and having from about 40% to about 100% aliphatic character, wherein said copolyesters each have a molecular weight between about 1000 g/mol and 6000 g/mol and wherein the amounts of said copolyesters are from about 0 to about 1 equivalent of the solid amorphous saturated copolyester, from about 0 toa bout 1 equivalent of the saturated liquid copolyester, and from about 0 to about 1 equivalent of the partially crystalline saturated copolyester, and wherein the sum of the equivalent amounts of said copolyesters is 1.

26. The thermosetting polyurethane composite of claim 25 wherein the polyisocyanate compound is 4,4'"'"'-diphenylmethane diisocyanate.

27. The thermosetting polyurethane composite of claim 23 wherein the water-generating curing composition generates water by water formation or release at an elevated temperature.

28. The thermosetting polyurethane composite of claim 27 wherein the polyurethane base resin has a melting point at least 5 degrees lower than the point of water formation or release from the water-generating curing composition.

29. The thermosetting polyurethane composite of claim 28 wherein the polyurethane base resin has a melting point at least 40 degrees lower than the point of water formation or release from the water-generating curing composition.

30. The thermosetting polyurethane composite of claim 23 wherein the polyurethane base resin is a liquid.

31. The thermosetting polyurethane composite of claim 23 wherein the water-generating curing composition is dispersed in the polyurethane base resin.

32. The thermosetting polyurethane composite of claim 31 wherein the dispersed water-generating curing composition is encapsulated with an inert encapsulant composition.

33. The thermosetting polyurethane composite of claim 32 wherein the encapsultant composition comprises a thermoplastic resin.

34. The thermosetting polyurethane composite of claim 33 wherein the encapsultant composition has a melting point higher than the melting point of the polyurethane base resin but lower than the point of water formation or release from the water-generating curing composition.

35. The thermosetting polyurethane composite of claim 34, wherein the encapsultant composition is present in an amount of from about 25 to about 75 percent by weight of the water-generating curing composition.

36. The thermosetting polyurethane composite of claim 23 wherein the water generating curing composition is at least one compound selected from the group consisting of CaSO₄.2H₂ O, CaSO₄.1/2H₂ O, NaHCO₃, (NH₄)₂ CO₃, (NH₄)₂ C₂ O₄ and ammonium stearate.

37. The thermosetting polyurethane composite of claim 23 wherein the composite further comprises an amine-terminated polyamide resin.

38. The thermosetting polyurethane composite of claim 23 wherein the composition is foamable.

41. The thermosetting polyurethane composite of claim 23 wherein the composite further comprises a foam reducing agent.

42. The thermosetting polyurethane composite of claim 41 wherein said foam reducing agent is selected from the group consisting of calcium oxide, soda lime, activated carbon, molecular sieves and dimethylpolysiloxanes.

43. The thermosetting polyurethane composite of claim 23 wherein the ratio of equivalents of isocyanate groups to active hydrogen groups in said composite is from about 0.5:

1.0 to about 2.0;

1.0.

44. The thermosetting polyurethane composite of claim 43 wherein the ratio of equivalents of isocyanate groups to active hydrogen groups in said composite is from about 0.8:

1.0 to about 1.2;

1.0.

45. The thermosetting polyurethane composite of claim 23 wherein the water-generating curing composition releases water or forms water upon heating to from about 50°

to about 250°

C. and the composite comprises an adhesive composition.

46. The thermosetting polyurethane composite of claim 45 wherein the water-generating curing composition releases water or forms water upon heating to from about 120°

to about 220°

C.

47. A process for preparing a hot melt adhesive which cures with moisture comprising adding a substance which releases water or forms water upon heating so as to cure a base resin via terminal isocyanate groups.

48. The hot melt adhesive made by the process of claim 47.