Film coated with glass barrier layer with metal dopant

• US 5,084,356 A
• Filed: 04/20/1990
• Issued: 01/28/1992
• Est. Priority Date: 04/20/1990
• Status: Expired due to Term

• Current Assignee: E. I. du Pont de Nemours and Company (Corteva, Inc.)
• Original Assignee: E. I. du Pont de Nemours and Company (Corteva, Inc.)
• Inventors: Jackson, Scott C., Deak, Gedeon I.
• Primary Examiner(s): Cashion, Jr., Merrell C.
• Assistant Examiner(s): Le, Hoa T.
• Application Number:
  US07/513,302
• Time in Patent Office: 648 Days
• Field of Search: 428/446, 428/458, 428/480, 428/412, 428/417, 428/474.4
• US Class Current: 428/458
• CPC Class Codes: B32B 37/12 characterised by using adhesives
• CPC Class Codes: B32B 38/00 Ancillary operations in connection with laminating processes
• CPC Class Codes: C23C 14/10 Glass or silica
• CPC Class Codes: Y10T 428/31507 Of polycarbonate
• CPC Class Codes: Y10T 428/31525 Next to glass or quartz
• CPC Class Codes: Y10T 428/31681 Next to polyester, polyamide or polyimide [e.g., alkyd, glue, or nylon, etc.]
• CPC Class Codes: Y10T 428/31725 Of polyamide
• CPC Class Codes: Y10T 428/31786 Of polyester [e.g., alkyd, etc.]

Abstract

A structure comprising a polymeric film substrate and a glassy coating of silicon dioxide heavily doped with at least one metal selected from the group consisting of antimony, aluminum, chromium, cobalt, copper, indium, iron, lead, manganese, tin, titanium, tungsten, zinc, and zirconium, provides improved barrier properties.

Claims

1. A structure having superior barrier properties, comprising:

(a) a polymeric substrate, and

(b) a glassy coating of silicon dioxide doped with at least one metal selected from the group consisting of antimony, aluminum, chromium, cobalt, copper, indium, iron, lead, manganese, tin, titanium, tungsten, zinc, and zirconium, said coating and metal dopant contained therein being present in an amount suitable to provide an oxygen transmission value through the coated structure of at most about 5 mL/day-m² -atm.

2. The structure of claim 1 wherein the amount of glassy coating and the amount of metal dopant contained therein are suitable to provide an oxygen transmission value through the coated structure of at most about 1.5 mL/day-m² -atm.

3. The structure of claim 1 wherein the amount of metal dopant is suitable to provide an oxygen permeation value for said glassy coating of at most about 3000×

10^-6 mL-mm/day-m² -atm.

4. The structure of claim 1 wherein the amount of metal dopant is suitable to provide an oxygen permeation value for said glassy ooating of at most about 600×

10^-6 mL-mm/day-m² -atm.

5. The structure of claim 1 wherein the amount of metal dopant is suitable to provide an oxygen permeation value for said glassy coating of at most about 400×

10^-6 mL-mm/day-m² -atm.

6. The structure of claim 1 wherein the thickness of the glassy coating is about 20 to about 500 nm.

7. The structure of claim 6 wherein the thickness of the glassy coating is about 50 to about 350 nm.

8. The structure of claim 1 wherein the glassy coating of silicon dioxide is doped with a metal selected from the group consisting of copper, chromium, manganese, tin, and zinc.

9. The structure of claim 8 wherein the metal is copper.

10. The structure of claim 8 wherein the metal is tin.

11. The structure of claim 1 wherein the amount of dopant metal is sufficiently low that the optical density of said glassy coating retains at least about 70% optical transmission at 550 nm.

12. The structure of claim 1 wherein the amount of dopant metal calculated as elemental metal is about 0.5 to about 30 weight percent of the glassy coating.

13. The structure of claim 9 wherein the amount of copper in the glassy coating is about 1 to about 15 weight percent.

14. The structure of claim 10 wherein the amount of tin in the glassy coating is about 3 to about 30 weight percent.

15. The structure of claim 1 wherein the polymeric substrate is a film.

16. A multiple layer structure comprising the structure of claim 15 as at least one layer.

17. The structure of claim 1 wherein the polymeric substrate has a surface smoothness such that the average height of roughness is less than about 50 nanometers.

18. The structure of claim 1 wherein the polymeric substrate has a surface smoothness such that the average height of roughness is less than about 10 nanometers.

19. The structure of claim 15 wherein the substrate film is polyester or polyamide.

20. The structure of claim 19 wherein the substrate film is oriented polyethylene terephthalate.

21. The structure of claim 1 further comprising a plastic resin protective layer.

22. A structure having superior barrier properties, comprising:

(a) a polymeric substrate, and

(b) a glassy coating of silicon dioxide doped with lithium borate in an amount suitable to provide an oxygen transmission value through the coated structure of at most about 5 mL/day-m² -atm.