Glass spinner manufacture

• US 5,085,679 A
• Filed: 11/23/1990
• Issued: 02/04/1992
• Est. Priority Date: 11/23/1990
• Status: Expired due to Fees

• Current Assignee: Inco Alloys International, Inc. (Berkshire Hathaway Incorporated), Owens- Corning Fiberglas Technology Incorporated (Owens Corning)
• Original Assignee: Owens-Corning Fiberglas Corporation
• Inventors: Blake, Mott J., Lawson, Richard D., Hinze, Jay W.
• Primary Examiner(s): LINDSAY JR, ROBERT
• Application Number:
  US07/617,240
• Time in Patent Office: 438 Days
• Field of Search: 65/1, 65/8, 65/15, 65/374.12, 72/208, 72/370, 419/28
• US Class Current: 65/515
• CPC Class Codes: B21D 51/18 vessels, e.g. tubs, vats, tanks, sinks, or the like
• CPC Class Codes: B21H 1/06 rings of restricted axial length extending closed shapes of metal bands by simultaneous rolling at two or more zones B21B5/00
• CPC Class Codes: C03B 37/0805 Manufacturing, repairing, or other treatment of bushings, nozzles or bushing nozzle plates
• CPC Class Codes: C22F 1/10 of nickel or cobalt or alloys based thereon

Abstract

Oxide dispersion strengthened metals are ring rolled into a profiled member which can be employed as a spinner in the manufacture of fibrous glass. Sufficient hot working and annealing are provided to develop the desired coarse grain structure.

Claims

1. A process for forming a glass fiber-forming spinner comprising ring rolling a hollow cylinder of an oxide dispersion strengthened alloy to decrease the wall thickness of said cylinder and increase both its inside and outside diameter;

converting said ring rolled cylinder into a ring member having an axially rectilinear central annular portion and upper and lower flange portions extending inwardly therefrom, said rolling and converting being done above the minimum warm working temperature and below the recrystallization temperature of said alloy;

heat treating said ring member;

said ring rolling and converting being such that the wall thickness of the central portion compared to the wall thickness of said hollow cylinder is decreased in an amount sufficient for recrystallization of said alloy into a coarse grain structure during said heat treating, the grain structure of said central portion being axially and circumferentially elongate, and forming a plurality of glass fiber-forming apertures in said central portion either before or after said heat treating.

13. The process of claim 1 wherein during ring rolling said oxide dispersion strengthened alloy is periodically reheated to maintain its temperature sufficiently high to stop cracking but not so high as to substantially decrease strength.

2. A process for producing a ring shaped member adaptable for use in glass fiber making comprising:

ring rolling a heavy walled hollow cylinder of an oxide dispersion strengthened alloy into a thinner walled ring, the wall of said thinner walled ring being rectangular in cross section;

pressing said thinner walled ring into a ring whose wall is C-shaped in cross section;

ring rolling said ring whose wall is C-shaped in cross section into a ring having a profiled cross section, said profiled cross section comprising an axially rectilinear annular central portion and upper and lower flanges respectively extending inwardly from said central portion;

annealing said ring having said profiled cross section at a temperature for a time sufficient to recrystallize the alloy to a coarse grain structure which is axially and circumferentially elongate in said central panel, the reduction in wall thickness from the heavy walled spinner to the ring having said profiled cross section being effective for said recrystallization to said coarse grains during annealing and, either before or after said annealing, forming a plurality of glass fiber-forming apertures in said central portion.

3. The process of claim 2 wherein the initial wall thickness of said heavy walled cylinder is t_i and wherein the final wall thickness of said axially rectilinear annular central portion is t_f and wherein [(t_i -t_f)/t_i ]×

100 is at least about 75%.

14. The process of claim 2 wherein during said ring rolling said oxide dispersion strengthened alloy is periodically reheated to maintain its temperature sufficiently high to stop cracking but not so high as to substantially decrease strength.

4. A hot working method of forming a generally inwardly concave annular member which is adaptable to producing fibrous glass comprising extruding oxide dispersion strengthened metal powder into a solid cylindrical billet;

forming said cylindrical billet into a precursor annular member;

ring-rolling said precursor annular member a sufficient number of times to form an annular single piece member of increased diameter and decreased thickness which can be recrystallized to a coarse grain structure, said member having an axially rectilinear annular central portion and upper and lower flanges extending inwardly from said central portion, and recrystallizing said member into a coarse grain structure in which said grains in said central portion are axially and circumferentially elongate and circumferentially forming a plurality of fiber forming orifices in said central portion either before or after said recrystallizing.

5. The method of claim 4 wherein said extruding is done at an extrusion ratio of at least 4:

1.

6. The method of claim 5 wherein the extrusion ram speed is between 4 inches/second and 9 inches/second.

7. The method of claim 4 wherein said precursor annular member formed from said cylinder has a thickness t_i and the thickness of said axially rectilinear central portion is t_f and wherein [(t_i -t_f)/t_i ]×

100 is at least about 75%.

8. In a method of making glass fibers comprising passing molten glass through the side wall of a rotating spinner, the improvement comprising forming the spinner in accordance with the process of claim 4.

15. The method of claim 4 wherein during said ring rolling said oxide dispersion strengthened metal is periodically reheated to maintain its temperature sufficiently high to stop cracking but not so high as to substantially decrease strength.

9. In a method comprising:

providing a glass fiber forming spinner at a fiber forming location and forming glass fibers with said spinner, the improvement wherein said providing step comprises;

fabricating an oxide dispersion strengthened metal powder into an annular cylindrically shaped billet;

ring-rolling said billet sufficiently to form a seamless annular member capable of being recrystallized to a coarse grain structure and having a central rectilinear portion and upper and lower flanges extending inwardly therefrom;

forming a plurality of glass forming apertures in said central portion, said forming being done either before or after a recrystallizing heat treatment, and heat treating said member to recrystallize said member into a coarse grain structure and wherein said central portion contains grains which are axially and circumferentially elongate.

10. The method of claim 9 wherein said ring-rolling provides a deformation factor of at least about 83%.

16. The method of claim 9 wherein during said ring rolling said oxide dispersion strengthened metal is periodically reheated to maintain its temperature sufficiently high to stop cracking but not so high as to substantially decrease strength.

11. A spinner for forming glass fibers said spinner having a plurality of fiber forming apertures and being formed from a ring-rolled oxide dispersion strengthened metal said spinner having a central rectilinear portion with recrystallized coarse grains which are axially and circumferentially elongate.

12. The spinner of claim 11 wherein said ring-rolling is sufficient to provide a deformation factor of at least about 75%.