Method of producing shaped articles of fiber/binder mixtures

• US 5,102,596 A
• Filed: 11/29/1990
• Issued: 04/07/1992
• Est. Priority Date: 12/01/1989
• Status: Expired due to Fees

• Current Assignee: G Siempelkamp GmbH &Company A Joint Stock Company With Limited Liability of Germany
• Original Assignee: G. Siempelkamp Gmbh & Co.
• Inventors: Lempfer, Karsten, Gupta, Satish
• Primary Examiner(s): THEISEN, MARY LYNN F
• Application Number:
  US07/620,402
• Time in Patent Office: 495 Days
• Field of Search: 264/109, 264/115, 264/122, 264/333, 106/731, 106/780, 156/39
• US Class Current: 264/115
• CPC Class Codes: B28B 1/525 containing organic fibres, e.g. wood fibres B28B1/526, B28B1/527 take precedence
• CPC Class Codes: B28B 17/02 Conditioning the material prior to shaping for mixtures containing clay or cement B28C
• CPC Class Codes: C04B 18/24 Vegetable refuse, e.g. rice husks, maize-ear refuse; Cellulosic materials, e.g. paper , cork
• CPC Class Codes: C04B 18/241 Paper, e.g. waste paper; Paper pulp
• CPC Class Codes: C04B 2111/00612 as one or more layers of a layered structure
• CPC Class Codes: C04B 28/04 Portland cements
• CPC Class Codes: C04B 28/14 containing calcium sulfate cements gypsum-paper plates E04C
• CPC Class Codes: C04B 40/0028 Aspects relating to the mixing step of the mortar preparation
• CPC Class Codes: C04B 40/0071 making use of a rise in pressure
• CPC Class Codes: D21J 3/00 Manufacture of articles by pressing wet fibre pulp, or papier-mâché, between moulds
• CPC Class Codes: Y02W 30/91 Use of waste materials as fillers for mortars or concrete

Abstract

Paper or cellulose pieces forming a fiber raw material are wetted with water prior to comminution so that the comminution into fibers is effected with the moistened raw material. The moisture content of the fibers makes up at least part of the water of hydration required to completely set the binder which is mixed with the fibers. The binder can be plaster (gypsum) or hydraulic cement. The mixture is pressed to the desired shape and heat may be applied.

Claims

1. A method of producing shaped articles, comprising the steps of:

(a) adding a quantity of water to a raw fiber product to form a mass of the raw fiber product moistened with said quantity of water;

(b) combining said mass of said raw fiber product moistened with said quantity of water with a binder hydratable with water of hydration to cause setting of said binder, thereby forming a mixture of said binder with said mass, said quantity of water in said mass providing at least part of the total water required to hydrate said binder;

(c) milling said mixture to comminute said mass into fibers and blend said fibers with said binder in said mixture;

(d) thereafter shaping said mixture under pressure to a shape of an article; and

(e) allowing said article to set by reaction of said binder at least in part with water from said mass.

2. The method defined in claim 1 wherein said raw fiber product is selected from the group which consists of paper scraps, pieces of cellulose products and mixtures thereof.

3. The method as defined in claim 1 wherein said binder hydratable with water is gypsum.

4. The method defined in claim 1 wherein said mass of raw fiber product contains all of the water necessary for hydration of said binder following step (a).

5. The method defined in claim 1 wherein said mass of fibers is moistened with a quantity of water in excess of the total amount of water required for hydration of said binder.

6. The method defined in claim 1 wherein the amount of water in said mixture for hydration of said binder is so adjusted that the fiber/binder mixture is agglomerate-free.

7. A method of producing shaped articles, comprising the steps of:

(a) moistening pieces of paper with a quantity of water;

(b) milling said pieces of paper moistened with said quantity of water and a gypsum binder requiring for setting a certain quantity of water of hydration in a rapidly rotating mill, said quantity of water moistening said pieces of paper making up at least part of said water of hydration to form a mixture of paper fibers, gypsum and water; and

(c) shaping said mixture under pressure into a shape of an article and causing said shape to set.

8. The method defined in claim 7 wherein said pieces of paper are pieces of scrap paper.

9. The method defined in claim 7 wherein said mixture is shaped under heat and pressure in step (c).

10. The method defined in claim 7, further comprising spraying additional water into said mill.

11. The method defined in claim 7 wherein said paper pieces upon introduction into said mill have a moisture content in excess of 60%.

12. The method defined in claim 11 wherein said moisture content is about 180%.

13. The method defined in claim 7 wherein said paper pieces in said mill make up 10 to 20 percent by weight of the dry solids introduced into said mill.