Intumescent sheet material

• US 5,110,413 A
• Filed: 08/06/1990
• Issued: 05/05/1992
• Est. Priority Date: 07/11/1989
• Status: Expired due to Fees

• Current Assignee: T&N Technology Limited
• Original Assignee: T&N Technology Limited
• Inventors: Steer, Adrian M.
• Primary Examiner(s): Chin, Peter
• Application Number:
  US07/562,844
• Time in Patent Office: 638 Days
• Field of Search: 162/145, 162/152, 162/181.6, 162/159, 162/181.8, 162/181.9, 162/169, 428/920, 428/921, 428/913
• US Class Current: 162/145
• CPC Class Codes: C04B 14/022 Carbon
• CPC Class Codes: C04B 14/104 Bentonite, e.g. montmorillonite
• CPC Class Codes: C04B 14/106 Kaolin
• CPC Class Codes: C04B 14/20 Mica; Vermiculite mechanical splitting B28D
• CPC Class Codes: C04B 14/42 Glass
• CPC Class Codes: C04B 18/24 Vegetable refuse, e.g. rice husks, maize-ear refuse; Cellulosic materials, e.g. paper , cork
• CPC Class Codes: C04B 26/02 Macromolecular compounds
• CPC Class Codes: Y02W 30/91 Use of waste materials as fillers for mortars or concrete

Abstract

Intumescent sheet material having a matrix whose predominant ingredient is an unfired kaolinitic clay comprising ball clay reinforced by inorganic vitreous fibre (for example, mineral wool) contains heat-expandable graphite as intumescent agent and up to 10 percent by weight of an organic binder. It is made by dewatering an aqueous suspension of the aforesaid ingredients in the form of a layer which includes cellulose fibre as web-forming agent.

Claims

1. A method of making intumescent sheet material having a matrix whose predominant ingredient is an unfired kaolinitic clay comprising ball clay reinforced by inorganic vitreous fibre, said material including up to 10 per cent by weight of an organic binder, by dewatering an aqueous suspension of the aforesaid ingredients in the form of a layer which includes cellulose fibre as web-forming agent, said suspension containing an amount of heat-expandable graphite sufficient to swell the sheet in a fire.

2. A method according to claim 1, in which the heat-expandable graphite forms at least 15 per cent by weight of the sheet.

3. A method according to claim 1, in which the inorganic vitreous fibre is mineral wool.

4. A method according to claim 1, in which the suspension contains mica in an amount up to 10 per cent by weight of the sheet.

5. A method according to claim 1, in which the suspension contains bentonite clay in an amount up to 5 per cent by weight of the sheet.

6. A method according to claim 1, in which the suspension contains china clay in an amount up to two-thirds by weight of the total kaolinitic clay.

7. A method according to claim 1, in which the organic binder comprises starch.

8. A method according to claim 1, in which the organic binder comprises an elastomer.

9. A method according to claim 1, in which the total content of organic material in the suspension is no greater than 15 per cent by weight of the sheet.