Aluminum alloy composition

• US 5,110,545 A
• Filed: 09/05/1990
• Issued: 05/05/1992
• Est. Priority Date: 02/24/1989
• Status: Expired due to Fees

• Current Assignee: Nichols Aluminum-Golden, Inc. (Crestwood Capital Management, Inc.)
• Original Assignee: Golden Aluminum, Inc.
• Inventors: McAuliffe, Donald C., Marsh, Ivan M.
• Primary Examiner(s): Dean, R.
• Assistant Examiner(s): Koehler, Robert R.
• Application Number:
  US07/578,019
• Time in Patent Office: 608 Days
• Field of Search: 420/542, 420/534
• US Class Current: 420/534
• CPC Class Codes: C22C 21/06 with magnesium as the next major constituent
• CPC Class Codes: C22F 1/04 of aluminium or alloys based thereon
• CPC Class Codes: C22F 1/047 of alloys with magnesium as the next major constituent

Abstract

An aluminum alloy that can be fabricated into aluminum sheet having novel properties is provided. The strip stock is suitable for the fabrication of both container ends and container bodies in thinner gauges than are typically presently employed, has low earing characteristics and may be derived from recycled aluminum scrap. The alloy preferably has a magnesium concentration of from about 2 to about 2.8 weight percent and a manganese concentration of from about 0.9 to about 1.6 weight percent. The process preferably includes continuous chill block casting the alloy melt into a strip, hot rolling the strip to a first thickness, annealing the hot rolled strip and then cold rolling the annealed strip to a final thickness. Cold rolling preferably includes two stages with an intermediate anneal step between the two stages. The process increases tensile and yield strength while decreasing earing percentage, even in very thin gauges, such as 0.010 inches.

Claims

1. An aluminum alloy composition, comprising:

a) from about 2 to about 2.8 weight percent magnesium;

b) from about 0.9 to about 1.6 weight percent manganese;

c) from about 0.13 to about 0.20 weight percent silicon;

d) from about 0.25 to about 0.35 weight percent iron; and

e) from about 0.20 to about 0.25 weight percent copper;

wherein the balance comprises aluminum.

3. An aluminum alloy composition as recited in claim 1, wherein the ratio of magnesium to manganese is less than about 1.5:

1.

6. An aluminum alloy composition as recited in claim 1, wherein said alloy comprises recycled container scrap.

8. An aluminum alloy composition as recited in claim 1, wherein said alloy is suitable for the manufacture of drawn and ironed container bodies.

9. An aluminum alloy composition as recited in claim 1, wherein said alloy composition is capable of being cast into aluminum sheet having a yield strength greater than about 38 ksi and a 45°

earing percentage of less than about 2 percent.

2. An aluminum alloy composition, comprising:

a) from about 2 to about 2.8 weight percent magnesium; and

b) from about 1.1 to about 1.6% weight percent manganese;

c) from about 0.13 to about 0.20 weight percent silicon;

d) from about 0.25 to about 0.35 weight percent iron; and

e) from about 0.20 to about 0.25 weight percent copper;

wherein the balance consists essentially of aluminum.

4. An aluminum alloy composition, comprising:

a) from about 2.6 to about 2.8 weight percent magnesium; and

b) from about 1.1 to about 1.5 weight percent manganese.

17. An aluminum alloy composition as recited in claim 4, further comprising:

a) from about 0.13 to about 0.20 weight percent silicon;

c) from about 0.25 to about 0.35 weight percent iron; and

e) from about 0.20 to about 0.25 weight percent copper;

wherein the balance consists essentially of aluminum.

5. An aluminum alloy composition, comprising:

a) from about 2.0 to about 2.1 weight percent magnesium;

b) from about 1.4 to about 1.6 weight percent manganese; and

c) from about 0.20 to about 0.25 weight percent copper.

7. An aluminum alloy composition, comprising:

a) from about 2 to about 2.8 weight percent magnesium; and

b) from about 1.1 to about 1.6 weight percent manganese;

wherein said alloy composition also comprises aluminum, silicon, iron and copper and less than about 0.05 weight percent of any impurity and less than about 0.2 weight percent total impurities.

10. An aluminum alloy composition, comprising:

a) from about 2.0 to about 2.8 weight percent magnesium;

b) from about 0.9 to about 1.1 weight percent manganese;

c) from about 0.13 to about 0.20 weight percent silicon;

d) from about 0.25 to about 0.35 weight percent iron; and

e) from about 0.20 to about 0.25 weight percent copper;

wherein said aluminum alloy composition is suitable for the manufacture of drawn and ironed container bodies.

11. An aluminum alloy composition, comprising:

a) from about 2.6 to about 2.8 weight percent magnesium;

b) from about 1.1 to about 1.5 weight percent manganese;

c) from about 0.13 to about 0.20 weight percent silicon;

d) from about 0.25 to about 0.35 weight percent iron; and

e) from about 0.20 to about 0.25 weight percent copper;

wherein said alloy composition comprises less than about 0.05 percent of any impurity and less than about 0.2 percent total impurities, the balance consisting essentially of aluminum.

12. An aluminum alloy composition, comprising:

a) from about 2.0 to about 2.1 weight percent magnesium;

b) from about 1.4 to about 1.6 weight percent manganese;

c) from about 0.13 to about 0.20 weight percent silicon;

d) from about 0.25 to about 0.35 weight percent iron; and

e) from about 0.20 to about 0.25 weight percent copper;

wherein said alloy composition comprises less than about 0.05 percent of any impurity and less than about 0.2 percent total impurities, the balance consisting essentially of aluminum.

13. An aluminum alloy composition, comprising:

a) from about 2 to about 2.8 weight percent magnesium; and

b) from about 1.1 to about 1.6 weight percent manganese;

wherein said alloy is suitable for the manufacture of drawn and ironed container bodies.

14. An aluminum alloy composition as recited in claim 13, wherein said alloy comprises recycled container scrap.

15. An aluminum alloy composition, comprising:

a) from about 2 to about 2.8 weight percent magnesium; and

b) from about 1.1 to about 1.6 weight percent manganese;

wherein said alloy composition is capable of being cast into aluminum sheet having a yield strength greater than about 42 kpsi and a 45°

earing percentage of less than about 2 percent.

16. An aluminum alloy composition as recited in claim 15, wherein said alloy comprises recycled container scrap.