Rapidly crystallizing polyurethane systems

• US 5,115,073 A
• Filed: 09/11/1990
• Issued: 05/19/1992
• Est. Priority Date: 09/23/1989
• Status: Expired due to Fees

• Current Assignee: Bayer AG
• Original Assignee: Bayer AG
• Inventors: Hansel, Eduard, Arend, Gu, Konig, Klaus, Meckel, Walter
• Primary Examiner(s): Kight, III, John
• Assistant Examiner(s): Truong, Duc
• Application Number:
  US07/580,717
• Time in Patent Office: 616 Days
• Field of Search: 528/83, 528/80, 521/126, 521/137, 521/138, 521/163, 521/172
• US Class Current: 528/83
• CPC Class Codes: C08G 18/0804 Manufacture of polymers containing ionic or ionogenic groups
• CPC Class Codes: C08G 18/12 using two or more compounds having active hydrogen in the first polymerisation step
• CPC Class Codes: C08G 18/302 Water
• CPC Class Codes: C08G 18/307 Atmospheric humidity
• CPC Class Codes: C08G 18/4202 Two or more polyesters of different physical or chemical nature C08G18/44 takes precedence
• CPC Class Codes: C08G 18/664 with compounds of group C08G18/3203
• CPC Class Codes: C08G 2170/20 Compositions for hot melt adhesives
• CPC Class Codes: C08G 2250/00 Compositions for preparing crystalline polymers
• CPC Class Codes: C09J 175/06 from polyesters

Abstract

The present invention is directed to a polyurethane system containing isocyanate groups prepared by reacting

A) 70 to 98 parts by weight of at least one polyester diol having a melting point of 30° C. to 60° C. and a molecular weight of 800 to 8,000,

B) 2 to 30 parts by weight of at least one polyester diol having a melting point of 65° C. to 150° C. and a molecular weight of 600 to 8,000, and

C) no more than 1 mole of a diol having a molecular weight of less than 600 per moles of A) plus B), with,

D) at least one organic polyisocyanate, the ratio of isocyanate groups to hydroxyl groups is between 3:1 and 1.2:1.

Claims

1. A polyurethane system containing isocyanate groups prepared by reacting:

A) 70 to 98 parts by weight of at least one polyester diol having a melting point of 30°

C. to 60°

C. and a molecular weight of a 800 to 8,000,

B) 2 to 30 parts by weight of at least one polyester diol having a melting point of 65°

C. to 150°

C. and a molecular weight of 600 to 8,000, and

C) no more than 1 mole of a diol having a molecular weight of less than 600 per moles of A) plus B), with,

D) at least one organic polyisocyanate, the ratio of isocyanate groups to hydroxyl groups is between 3;

1 and 1.2;

1.

2. The system of claim 1, wherein diol C) has a molecular weight below 400.

3. The system of claim 1 wherein the ratio of the isocyanate groups to isocyanate-reactive groups is from 2.2:

1 to 1.4;

1.

4. The system of claim 1 wherein 75 to 98% by weight of the mixture of A) and B) consists of hydroxylpolyesters of adipic acid and hexane-1,6-diol in a molecular weight range of 1,500 to 6,000.

5. The system of claim 1 wherein 2 to 15% by weight of the mixture of A) and B) consists of hydroxylpolyesters of terephthalic acid and hexane-1,6-diol in a molecular weight range of 800 to 2,500.

6. The system of claim 1 wherein 5 to 30% by weight of the mixture of A) and B) consists of hydroxylpolyesters of dodecanedioic acid and hexane-1,6-diol in a molecular weight range of 1,500 to 6,000.

7. The system of claim 1 wherein diphenyl methane diisocyanates are used as the polyisocyanate.

8. In a process for bonding substrates using a polyurethane system by applying said adhesive to at least one of the substrates to be bonded, bringing the substrates together, and allowing the adhesive to cure, the improvement wherein the adhesive is the system of claim 1.

9. The process of claim 8, wherein the polyurethane system is used in solvent-free form as a hotmelt adhesive.