Building plywood product and method

• US 5,147,486 A
• Filed: 11/30/1990
• Issued: 09/15/1992
• Est. Priority Date: 03/17/1989
• Status: Expired due to Term

• Current Assignee: Harry O. Hoffman, Kathleen A. Hoffman
• Original Assignee: Harry O. Hoffman, Kathleen A. Hoffman
• Inventors: Hoffman, Harry O.
• Primary Examiner(s): Ball, Michael W.
• Assistant Examiner(s): Stemmer, Daniel J.
• Application Number:
  US07/620,143
• Time in Patent Office: 655 Days
• Field of Search: 144/332, 144/330, 144/351, 144/346, 156/154, 156/94, 428/106, 428/535, 428/537.1, 428/114, 52/311, 52/312, 52/313
• US Class Current: 156/154
• CPC Class Codes: B27D 1/00 Joining wood veneer with any material; Forming articles thereby in conjunction with moulding of wood particles or fibres B27N3/06; Preparatory processing of surfaces to be joined, e.g. scoring
• CPC Class Codes: B32B 21/13 all layers being exclusively wood
• CPC Class Codes: Y10T 428/24066 Wood grain
• CPC Class Codes: Y10T 428/24132 including grain, strips, or filamentary elements in different layers or components parallel

Abstract

The disclosure relates to a medium density overlay plywood panel used as an exterior trim product for a residential building having a relatively high number of plies to total board thickness, and exposed edges with void free sanded surfaces having a predetermined pattern coarseness, and in which said overlay and edge surfaces are covered with an acrylic paint, whereby the trim product is characterized with the appearance of a solid wood product and the painted surfaces as highly weather resistant.

Claims

1. A method of manufacturing an exterior plywood building trim product comprising the steps of:

forming a base plywood board of an odd number of plies between 7 to 13 inclusive, said board having a ratio of 7 plies per five-eights inch of total board thickness and an approximately equal ratio for increased thicknesses of boards, by;

arranging each ply so that its grain is positioned perpendicularly to an adjacent ply to form alternately arranged plies having alternating degrees of edge coarseness,

forming the board to have appearance and construction side plies and interior plies,

providing said interior plies so that each ply thereof has substantially the same uniform thickness,

adhering adjacent said plies together,

forming the board to have a length substantially greater than its width, and to have two exposed ply edges opposite each other extending the length of the board, wherein said ply edges will have edge openings and edge core gaps;

sanding said appearance side ply to reduce show-through imperfections;

covering said appearance side ply with a fiber overlay;

filling said edge openings and edge core gaps with a filler compound to fill at least the outside portions of said openings and gaps and to cover the entire surfaces of said ply edges to an extent sufficient only to create substantially uniformly covered edges;

sanding said covered edges so that the sanded edges have a predetermined degree of overall coarseness created by said sanding, wherein the coarse sanding and said different degrees of edge coarseness of said alternately arranged plies form a strong bond between said ply edges and a covering of paint or stain; and

covering said sanded edges and said covered appearance side ply with paint or stain, wherein said appearance side ply and said ply edges are substantially resistant to conditions affecting appearance and longevity and have the appearance as to said covered edges and appearance side ply of a solid integral wood product.

2. In a method according to claim 1, the additional step of immediately prior to applying said void filling compound maintaining said compound at a temperature so as not to fall below approximately 60°

F.

3. In a method according to claim 1, the additional step of immediately prior to applying said void filling compound maintaining the compound at a temperature between approximately 60°

to 80°

F.

4. In a method according to claim 1, wherein said void filling compound comprises a wood putty having as an ingredient a substantial amount of solids and when dried has a high resistance to dimpling and mud cracks.

5. In a method according to claim 1, said sanding step further comprising creating a coarseness of the order of number 40 to 60 grit.

6. In a method according to claim 1, the additional step of forming said interior plies out of plies having a thickness of approximately 0.09 inch.

7. A method of manufacturing an exterior plywood building trim product comprising the steps of:

forming at least two base plywood boards of an odd number of plies between seven to thirteen inclusive, said boards having a ratio of seven plies per five eights inch of total board thickness and an approximately equal ratio for increased thicknesses of boards, wherein each board has the same number of plies, by;

arranging each ply so that its grain is positioned perpendicularly to an adjacent ply to form alternately arranged plies having alternating degrees of edge coarseness,

forming the board to have appearance and construction side plies and interior plies,

forming said interior plies so that each ply thereof has substantially the same uniform thickness, and

forming the plies out of Douglas fir,

adhering adjacent said plies together by a marine glue

joining together two or more end to end lengths of said boards by a transverse diagonal scarfed joint to form a length substantially greater than the width of the joined boards, wherein the joined boards will have two exposed ply edges opposite each other extending the length of the joined boards, and wherein said ply edges will have edge openings and edge core gaps;

limiting the thickness difference between the joined boards in the area of said joined ends to no more than approximately plus or minus one thirty second of an inch;

forming said appearance side ply and said construction side ply having the same grain directions;

sanding said appearance side ply to reduce show-through imperfections;

covering said appearance side ply with a medium density fiber overlay;

filling said edge openings and edge core gaps with a filler compound to fill at least the outside portions of said openings and gaps and to cover the entire surfaces of said ply edges to an extent sufficient only to create substantially uniformly covered edges;

sanding said covered edges to give the sanded edges a predetermined coarseness of the order of number 40 to 60 grit, wherein the coarse sanding and said different degrees of edge coarseness of said alternately arranged plies form a strong bonding surface for purposes of good coating adherence; and

covering said sanded edges and said covered appearance side ply with an acrylic latex paint coating, wherein said covered appearance side ply and said ply edges are substantially resistant against conditions affecting appearance and longevity, and have the appearance as to said painted surfaces of a solid integral wood trim product.

8. In a method according to claim 7, the additional step of immediately prior to applying said putty maintaining said putty at a temperature so as not to fall below approximately 60°

F.

9. In a method according to claim 7, wherein said putty comprises a wood putty having as an ingredient a substantial amount of solids and when dried has a high resistance to dimpling and mud cracks.

10. In a method according to claim 7, the additional step of forming said interior plies out of plies having a thickness of approximately 0.09 inch.

11. In a method according to claim 7, the additional steps of arranging, for several different thickness building trim products, seven said plies to form a five-eighths inch total thickness said board, nine said plies to form a three quarter inch total thickness said board, eleven said plies to form a one inch total thickness said board, and thirteen said plies to form a one and a quarter inch total thickness said board.